Repairing agent for ceramic tiles and preparation method thereof

A repairing agent and a technology for ceramic tiles, applied in the field of ceramic tile surface treatment, can solve problems such as affecting the appearance of products, difficulty in penetration and filling of ultra-clean and bright nano-liquids, and reducing product quality, so as to improve product quality, facilitate industrial production and application, and achieve strong hydrophobicity. Oleophobic and self-cleaning effect

Active Publication Date: 2020-04-10
GUANGDONG NADE NEW MATERIALS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to technical problems in the sintering process of tiles, many small or large pores will be produced inside the glaze. After rough polishing, these small pores will be exposed, giving the subsequent ultra-clean and bright nano-liquid Osmotic filling brings difficulties
Especially for ceramic tiles with obvious color differences, if the pores are too large or too many, the surface of the tiles that have been super-clean and bright will appear white spots of varying sizes, which not only reduces the quality of the product but also affects the quality of the product. beautiful

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repairing agent for ceramic tiles and preparation method thereof
  • Repairing agent for ceramic tiles and preparation method thereof
  • Repairing agent for ceramic tiles and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0033] The repairing agent for ceramic tiles of Examples 1-3 has a specific formula as shown in Table 1 below.

[0034] The pottery brick of table 1 embodiment 1-3 is used repairing agent formula table

[0035]

[0036]

[0037] According to Table 1, the components of Examples 1-3 were respectively taken and mixed uniformly to obtain the corresponding restoration agent for ceramic tiles.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a repair agent for ceramic tiles. The repair agent is prepared from components in percentage by weight as follows: 0.1%-3% of oil-soluble pigment, 4%-40% of an aid and the balance of an organic solvent. The repair agent for the ceramic tiles can effectively remove white spots, produced in a pure brightening process, on surfaces of the ceramic tiles, the tile surfaces have good brightness increase, permeability increase and antifouling effects, and the repair agent has very long storage time and service life. The invention further discloses a preparation method of the repair agent for the ceramic tiles. The preparation method is simple, easy to operate and facilitates industrial production and application.

Description

technical field [0001] The invention relates to the technical field of tile surface treatment, in particular to a restoration agent for ceramic tiles and a preparation method thereof. Background technique [0002] As a building decoration material, ceramic tiles can not only be used to decorate buildings, making buildings beautiful and gorgeous; moreover, pasting a layer of ceramic tiles on the surface of buildings can isolate the erosion of the building surface by the external environment and make the buildings more durable. durable. "Super clean and bright technology" is a high-precision ceramic tile surface treatment method commonly used at present. It repeatedly presses, polishes and polishes the tiles through the polishing grinding head to better infiltrate the nano-silica particles in the nano-liquid. into the pores of polished tiles, block the pores and micro-cracks of the tiles, and form a special, continuous nano-film, so that the tiles have a bright surface, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/84
CPCC04B41/4961C04B41/84C04B41/4922C04B41/463C04B41/4535C04B41/478C04B41/483C04B41/4853
Inventor 张中明
Owner GUANGDONG NADE NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com