High-wear-resistance long-life ductile iron and method of producing lower cylinder with ductile iron

A technology of high wear resistance, ductile iron, applied in casting molding equipment, mold, mold composition, etc., can solve the problems of high tensile strength, low tensile strength, low plasticity, etc., and achieve high-quality comprehensive mechanical properties, Long service life and ensure the effect of wear resistance

Active Publication Date: 2017-06-13
GUANGDONG ZHONGTIAN CHUANGZHAN DUCTILE IRON CO LTD
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Moreover, in the prior art, ductile iron has the problem that the tensile strength and plasticity cannot be unified, either the tensile strength is high but the plasticity is low, or the tensile strength is small but the plasticity is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-wear-resistance long-life ductile iron and method of producing lower cylinder with ductile iron
  • High-wear-resistance long-life ductile iron and method of producing lower cylinder with ductile iron
  • High-wear-resistance long-life ductile iron and method of producing lower cylinder with ductile iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Preparation method of lower cylinder of ductile iron with high wear resistance and long service life

[0042] 1.1 Raw material preparation:

[0043] The overall raw material requirements for the lower cylinder are C: 3.80%, Si: 2.20%, Mn: 0.65%, P: 0.017%, S: 0.005%, Cu: 0.55%, Mo: 0.30%, La: 0.0041%, Mg: 0.038 %, the balance of iron and non-removable impurities. In the present embodiment, in order to achieve the above-mentioned raw material requirements, the specific raw material ratio of the present invention is:

[0044] 50 parts by weight of automobile scraps, 50 parts by weight of metal stamping parts, 4.10 parts by weight of carburizers, 1 part by weight of lanthanide nodulizers, 0.6 parts by weight of high-calcium barium inoculants, 0.56 parts by weight of copper, and 0.2 parts by weight of sulfur oxide Inoculants, 1.92 parts by weight of ferrosilicon, 0.75 parts by weight of ferromanganese, and 0.54 parts by weight of ferromolybdenum.

[0045] The present inv...

Embodiment 2

[0066] Preparation method of lower cylinder of ductile iron with high wear resistance and long service life

[0067] 1.1 Raw material preparation:

[0068] The overall raw material requirements for the lower cylinder are C: 3.88%, Si: 2.30%, Mn: 0.55%, P: 0.015%, S: 0.008%, Cu: 0.45%, Mo: 0.40%, La: 0.0059%, Mg: 0.045 %, the balance of iron and non-removable impurities. In the present embodiment, in order to achieve the above-mentioned raw material requirements, the specific raw material ratio of the present invention is:

[0069] 50 parts by weight of automotive scraps, 50 parts by weight of metal stamping parts, 4.30 parts by weight of carburizers, 1 part by weight of lanthanide nodulizers, 0.6 parts by weight of high-calcium barium inoculants, 0.46 parts by weight of copper, 0.15 parts by weight of sulfur oxide Inoculants, 2.22 parts by weight of ferrosilicon, 0.50 parts by weight of ferromanganese, and 0.73 parts by weight of ferromolybdenum.

[0070] The present invent...

Embodiment 3

[0087] Preparation method of lower cylinder of ductile iron with high wear resistance and long service life

[0088] 1.1 Raw material preparation:

[0089] The overall raw material requirements for the lower cylinder are C: 3.85%, Si: 2.25%, Mn: 0.60%, P: 0.018%, S: 0.010%, Cu: 0.50%, Mo: 0.35%, La: 0.0050%, Mg: 0.0040 %, the balance of iron and non-removable impurities.

[0090] In the present embodiment, in order to achieve the above-mentioned raw material requirements, the specific raw material ratio of the present invention is:

[0091] 50 parts by weight of automobile scraps, 50 parts by weight of metal stamping parts, 4.19 parts by weight of carburizers, 1 part by weight of lanthanide nodulizers, 0.6 parts by weight of high-calcium barium inoculants, 0.51 parts by weight of copper, and 0.2 parts by weight of sulfur oxide Inoculants, 2.12 parts by weight of ferrosilicon, 0.60 parts by weight of ferromanganese, and 0.64 parts by weight of ferromolybdenum.

[0092] The p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-wear-resistance long-life ductile iron, comprising, by weight, 3.80-3.88% of C, 2.20-2.30% of Si, 0.55-0.65% of Mn, < / =0.020% of P, < / =0.010% of S, 0.45-0.55% of Cu, 0.30-0.40% of Mo, 0.0040-0.0060% of La, 0.035-0.045% of Mg, and the balance of iron and unavoidable impurity. The invention is intended to provide the high-wear-resistance long-life ductile iron that has high rigidity and fatigue strength and has improved tensile strength and plasticity, and a method of producing a lower cylinder with the ductile iron.

Description

technical field [0001] The invention relates to the field of ductile cast iron processing, and more specifically relates to a ductile cast iron with high wear resistance and long service life and a method for preparing a lower cylinder using the cast iron. Background technique [0002] The barrel diesel pile driver is a high-performance pile foundation construction equipment, which is suitable for foundation construction of concrete piles, prefabricated piles, steel pipe piles, steel sheet piles, wooden piles and other pile types. The lower cylinder is an important part of the barrel diesel pile driver. It is not only used as the hammer seat of the whole machine, but also the piston made of QT600-3 (with a hardness of 220-260HB) moves up and down in the cylinder, and a huge pile is generated longitudinally during the movement. At the same time, it must bear the effect of high temperature and high pressure during diesel combustion; therefore, the lower cylinder is required to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C21C1/10C22C33/08B22C9/24B22D15/02B22D1/00C21D1/18C21D1/58C21D9/00C22B9/16C21D5/00E02D7/12
CPCB22C9/24B22D1/00B22D15/02C21C1/10C21D1/18C21D1/58C21D5/00C21D9/0068C21D2211/009C22B9/16C22C33/08C22C37/04C22C37/10E02D7/125E02D2300/0031Y02P10/20
Inventor 柯志敏陈永成何良荣陈捷文
Owner GUANGDONG ZHONGTIAN CHUANGZHAN DUCTILE IRON CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com