Multifunctional environmentally-friendly water-based paint and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A water-based coating and multi-functional technology, applied in antifouling/underwater coatings, fireproof coatings, coatings, etc., can solve problems such as poor persistence of formaldehyde adsorption, secondary pollution of formaldehyde, indoor air pollution, etc., to achieve the elimination of harmful substances, Attenuate low-frequency noise and reduce noise
Inactive Publication Date: 2017-06-23
程艳青
View PDF4 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, the formaldehyde removal coatings on the market mainly add activated carbon components, which have poor formaldehyde adsorption persistence and are easy to reach adsorption saturation, and the escape of formaldehyde after adsorption saturation will cause secondary pollution; existing antibacterial coatings are added with organic amines. Azines and isothiazolinones are used as antibacterial agents, and their short-term antibacterial effect is obvious, but their durability is poor, their temperature resistance is poor, and harmful substances will be produced after decomposition under ultraviolet light
In addition, the volatilization process of volatile organic compounds added in liquid paint will also pollute the indoor air.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0034] The present invention includes the following raw material components in terms of weight percentage: 5% diatom mud, 10% Maya blue, 8% tourmaline, 2% nano-titanium dioxide, 7% ultrafine aluminum silicate, 10% sepiolite, silicon carbide 5%, zinc fluorosilicate 6%, acrylate emulsion 10%, silver ionic liquid 0.2%, fluorosilicon emulsion 5%, wetting and dispersing agent 0.4%, preservative 0.4%, polyvinyl alcohol 7%, thickener 5%, hydroxypropyl methylcellulose 10%, buffering agent 1%, defoamer 3‰, anti-cracking agent 3‰, inorganic pigment 0.2%, and the balance is deionized water.
Embodiment 2
[0036] The present invention includes the following raw material components in terms of weight percentage: 10% of diatom mud, 8% of Maya blue, 5% of tourmaline, 1% of nano-titanium dioxide, 5% of ultrafine aluminum silicate, 6% of sepiolite, silicon carbide 10%, zinc fluorosilicate 5%, acrylate emulsion 15%, silver ion liquid 0.3%, fluorosilicon emulsion 8%, wetting and dispersing agent 0.3%, preservative 0.2%, polyvinyl alcohol 10%, thickener 3%, hydroxypropyl methylcellulose 7%, buffering agent 1.5%, defoamer 3‰, anti-cracking agent 3‰, inorganic pigment 0.4%, and the balance is deionized water.
Embodiment 3
[0038]The present invention includes the following raw material components in weight percentage: 7% diatom mud, 6% Mayan blue, 8% tourmaline, 0.5% nano-titanium dioxide, 5% superfine aluminum silicate, 8% sepiolite, silicon carbide 6%, zinc fluorosilicate 7%, acrylate emulsion 15%, silver ionic liquid 0.3%, fluorosilicon emulsion 7%, wetting and dispersing agent 0.5%, preservative 0.3%, polyvinyl alcohol 5%, thickener 2%, hydroxypropyl methylcellulose 10%, buffering agent 1%, defoamer 3‰, anti-cracking agent 3‰, inorganic pigment 0.3%, and the balance is deionized water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
size
aaaaa
aaaaa
porosity
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses multifunctional environmentally-friendly water-based paint. The multifunctional environmentally-friendly water-based paint comprises main materials, additives and deionized water, wherein the main materials include diatom ooze, maya blue, tourmaline, nanometer titania, ultra-fine aluminum silicate, sepiolite, silicon carbide and zinc fluosilicate; the additives include acrylate polymer emulsion, silver ion solution, fluoro-silicone emulsion, wetting dispersant, preservative, polyvinyl alcohol, a thickener, hydroxypropyl methyl cellulose, a buffering agent, a defoaming agent, an anticracking agent and inorganic pigment. The invention also discloses a preparation method of the multifunctional environmentally-friendly water-based paint. According to the multifunctional environmentally-friendly water-based paint, the raw materials are environmentally-friendly, nontoxic and pollution-free materials; maya blue, nanometer titania and diatom ooze are used in match to enable efficient function of resisting formaldehyde, ammonia and benzene; the silver ion solution and nanometer titania are used in match to enable effective antibacterial effect and long-lasting antibacterial effect; tourmaline and silicon carbide are added, so that the functions of health care, smell removing and fireproofing are realized.
Description
technical field [0001] The invention relates to the field of building materials, in particular to a multifunctional environment-friendly water-based paint and a preparation method thereof. Background technique [0002] In recent years, people have paid more and more attention to the safety of interior decoration, especially the use of environmentally friendly functional coatings has been sought after by people. At present, the formaldehyde-removing coatings on the market mainly add activated carbon components, which have poor formaldehyde adsorption persistence and are easy to reach adsorption saturation, and the escape of formaldehyde after adsorption saturation will cause secondary pollution; Azines and isothiazolinones are used as antibacterial agents, and their short-term antibacterial effect is obvious, but their durability is poor, their temperature resistance is poor, and harmful substances will be produced after decomposition under ultraviolet rays. In addition, the...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more