One-component varnish composition, preparation method and use thereof

A one-component, one-component technology that can be used in coatings, polyurea/polyurethane coatings, devices for coating liquids on surfaces, etc., and can solve problems such as negative effects on paint films, poor weathering stability, etc.

Active Publication Date: 2020-03-17
LANGFANG NIPPON PAINT +2
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of silanes to improve rub resistance has associated negative effects on the paint film
The Si-O-R group can also be hydrolyzed to react with the hydroxyl groups in the resin, which is beneficial to increase the crosslink density and improve the friction resistance, but the newly formed Si-O-C group is easy to hydrolyze, so it has relatively poor performance under hot and humid conditions. Weather stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component varnish composition, preparation method and use thereof
  • One-component varnish composition, preparation method and use thereof
  • One-component varnish composition, preparation method and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0158] Preparation of polymers with hyperbranched or dendritic structures

[0159] Add 354.8g of Boltorn H40 and 74g of hexahydrophthalic anhydride into a 1L reaction kettle equipped with a stirrer, a thermometer, a nitrogen conduit and a reflux condenser, and then raise the temperature of the reaction system to 130°C. After the reaction temperature is constant, continue to insulate at this temperature for 4 to 5 hours, during which the acid value is measured by sampling every 1 hour. When the acid value (63mgKOH / g) reaches the theoretical value (62.8mgKOH / g), add 115.2g ring Glycidyl tert-carbonate with an oxygen equivalent of 240 and 0.5 g of N,N-dimethylbenzylamine, and keep warm at this temperature for 4 to 5 hours. During the heat preservation process, continuously monitor the change of the acid value, and stop the reaction when the acid value is less than 2mgKOH / g. When the reaction temperature dropped to 110° C., butyl acetate was added to reduce the viscosity and adju...

Embodiment 2

[0161] Preparation of polymers with hyperbranched or dendritic structures

[0162] Add 354.8g of Boltorn H40 and 98.6g of hexahydrophthalic anhydride into a 1L reaction kettle equipped with a stirrer, a thermometer, a nitrogen conduit and a reflux condenser, and then raise the temperature of the reaction system to 130°C. After the reaction temperature is constant, continue to keep warm at this temperature for 4 to 5 hours, during which the acid value is measured by sampling every 1 hour. When the acid value measured value (79mgKOH / g) reaches the theoretical value (79.2mgKOH / g), add 153.6g ring Glycidyl tert-carbonate with an oxygen equivalent of 240 and 0.5 g of N,N-dimethylbenzylamine, and keep warm at this temperature for 4 to 5 hours. During the heat preservation process, continuously monitor the change of the acid value, and stop the reaction when the acid value is less than 2mgKOH / g. When the reaction temperature dropped to 110° C., butyl acetate was added to reduce the ...

Embodiment 3

[0164] Preparation of Epoxy Modified Hyperbranched Polyester Resin

[0165] Prepare with reference to the synthesis method described in Example 1 of patent CN104628995, the specific synthesis steps are as follows: add 354.8g Boltorn H40 and 74g hexahydrophthalic anhydride to a 1L reactor equipped with a stirrer, a thermometer, a nitrogen conduit and a reflux condenser, Then the temperature of the reaction system was raised to 130°C. After the reaction temperature is constant, continue to keep warm at this temperature for 4 to 5 hours, during which the acid value is measured by sampling every 1 hour. When the acid value measured value (63mgKOH / g) reaches the theoretical value (62.8mgKOH / g), add 134.4g ring 1,4-butanediol diglycidyl ether with an oxygen equivalent of 140 and 0.6 g of triphenylphosphine, and continue to keep warm at this temperature for 4 to 5 hours. During the heat preservation process, continuously monitor the change of acid value and epoxy equivalent, and sto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses a one-component varnish composition, comprising at least one polymer with hyperbranched or tree structure; at least one hydroxyacrylic resin or hydroxymethacrylic resin; at least one silicone-modified acrylic resin at least one crosslinking curing agent; at least one acid catalyst; at least one rheology control agent; at least one auxiliary agent, and at least one solvent; the one-component varnish composition is high scratch resistance and high Weather resistant one-component clearcoat composition. The one-component varnish composition with high scratch resistance and high weather resistance provided by the present invention can effectively improve the slipperiness of the coating film surface of the varnish composition, thereby increasing the friction resistance of the coating film; in addition, silicone-modified acrylic acid The introduction of the resin can further improve the weather resistance of the coating film of the varnish composition.

Description

technical field [0001] The invention belongs to the technical field of paint preparation, and relates to a varnish composition, a preparation method and its application, in particular to a one-component varnish composition with high scratch resistance and high weather resistance and a preparation method thereof, and the high scratch resistance and high weather resistance The high weather resistance one-component varnish composition is coated on a substrate according to different construction techniques to form a cured coating or an application method for preparing a multi-coat finishing system. Background technique [0002] At present, as the most common means of transportation in people's daily life, automobiles have gradually penetrated into thousands of households. With the continuous increase of people's demand for automobiles, the subsequent requirements for the appearance and performance of automobiles are also constantly improving. The car body can be given an excell...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/08C09D133/14C09D175/06B05D3/02B05D7/00C08F220/18C08F220/28C08F220/06C08F212/08C08F230/08
CPCB05D3/0254B05D7/58B05D7/582C08F220/18C08F220/1804C09D133/08C09D133/14C09D143/04C08L75/06C08L43/04C08L33/08C08L33/14C08F220/281C08F220/06C08F212/08C08F220/14C08F230/08
Inventor 张萌夏天渊果建军梅鹏张景斌
Owner LANGFANG NIPPON PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap