Thermoplastic oil-resistant polyolefin elastomer sheath material and preparation method thereof

A technology of polyolefin elastomer and sheath material, which is applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve problems such as cable failure, and achieve the effects of improving flow rate, easy operation, and wide application range

Inactive Publication Date: 2017-07-07
天津市普立泰高分子科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Failure to do so will cause the cable to fail

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic oil-resistant polyolefin elastomer sheath material and preparation method thereof
  • Thermoplastic oil-resistant polyolefin elastomer sheath material and preparation method thereof
  • Thermoplastic oil-resistant polyolefin elastomer sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1 and embodiment 2 are prepared according to the parts by weight of each component shown in table 1:

[0018] Table 1 is the parts by weight table of each component of the embodiment of the present invention

[0019]

[0020] Preferred embodiments of the present invention combine figure 1 The details are as follows:

[0021] The preparation of embodiment 1:

[0022] Prepare the raw materials in Table 1 according to their respective parts by weight, put them into a mixer and mix them evenly, and the mixing time is 5 to 10 minutes, and then send them into a twin-screw extruder with a diameter of 50 mm for blending, melting, extruding, and filtering For sliver, the extrusion temperature is 170°C to 220°C, the extrusion speed is 200 rpm, then cooled in a cooling water tank, dried by a blower, and then entered into a pelletizer to cut into particles, and finally cooled to below 50°C, Packing is carried out to obtain the finished product.

Embodiment 2

[0023] The preparation of embodiment 2:

[0024] Prepare the raw materials in Table 1 according to their respective parts by weight, put them into a mixer and mix them evenly, and the mixing time is 5 to 10 minutes, and then send them into a twin-screw extruder with a diameter of 50 mm for blending, melting, extruding, and filtering , Strand, the extrusion temperature is 170°C to 210°C, the extrusion speed is 300 rpm, and then cooled in a cooling water tank, dried by a blower, and then entered into a pelletizer to cut into particles, and finally cooled to below 50°C, Packing is carried out to obtain the finished product.

[0025] Examples of the present invention are prepared as shown in Table 2 below:

[0026] Table 2 is the main performance requirements for the preparation of thermoplastic oil-resistant polyolefin elastomer sheath material in the embodiment of the invention

[0027]

[0028]

[0029] The thermoplastic oil-resistant polyolefin elastomer sheathing mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Shore hardnessaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a thermoplastic oil-resistant polyolefin elastomer sheath material and a preparation method thereof. The material is mainly prepared from, by weight, 70-80 parts of polypropylene resin, 20-30 parts of dynamic vulcanized thermoplastic rubber, 0.5 part of antioxidant, 0.3 part of anti-copper agent and 0.1 part of rheological agent. The preparation method includes the steps that the raw materials are metered by weight and put into a mixer to be evenly mixed, then the mixture is conveyed into a dual-screw extruder for blending extrusion, filtering and drawing, the mixture is cooled through a water tank and dried and then enters a granulator to be cut into particles, the particles are packaged, and finished products are obtained. The sheath material is low in density, good in heat resistance and oil resistance, and capable of serving as a hydraulic packaged cable sheath material for well logging; the preparation method is reasonable in deign and easy to operate.

Description

technical field [0001] The invention relates to a hydraulic sealing cable sheath material for well logging and a production method thereof, in particular to a thermoplastic oil-resistant polyolefin elastomer sheath material and a preparation method thereof. Background technique [0002] Since the 1980s, with the rapid development of my country's national economy, the petroleum industry has become a pillar industry in my country, and the world economy is increasingly dependent on the petroleum industry. Oil and gas detection and oil extraction technologies continue to develop, oil field detection and electric submersible pump oil extraction technologies are widely used in the petroleum industry. As one of the essential technologies for oil and gas exploration and oil recovery, hydraulically encapsulated cables for oil field logging are widely used, and its technology has been monopolized by foreign companies. [0003] The technical difficulties of thermoplastic oil-resistant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L21/00C08L27/18C08K5/134C08K5/24H01B3/44
CPCC08L23/12C08L2201/08C08L2203/20C08L2205/03H01B3/441C08L21/00C08L27/18C08K5/1345C08K5/24
Inventor 汪全信董景茹汪全伟
Owner 天津市普立泰高分子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com