A preparation method of high-strength tableware aluminum foil

A high-strength, aluminum foil technology, used in metal rolling and other directions, can solve the problems of long production cycle, many production processes, and high cost, and achieve the effects of increasing standing time, improving production efficiency and yield, and saving energy.

Active Publication Date: 2018-05-04
LUOYANG LONGDING ALUMINUM
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0023] The tensile strength of the aluminum foil prepared by this process can reach 220Mpa, but due to factors such as many production processes, long production cycle, and high cost, there are few reports on the use of 3004 alloy to produce aluminum foil for tableware.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of high-strength tableware aluminum foil
  • A preparation method of high-strength tableware aluminum foil
  • A preparation method of high-strength tableware aluminum foil

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The invention relates to a method for preparing high-strength tableware aluminum foil. In the invention, electrolytic aluminum liquid and aluminum ingots are smelted into an aluminum melt, and a 3-5mm thick aluminum coil is prepared by a continuous casting and rolling process. The reasonable setting of process technical parameters such as rolling and finished product annealing, so as to realize the direct preparation of high-strength tableware aluminum foil from aluminum melt, greatly shorten the process flow and reduce production costs.

[0047] The general preparation method of the present invention is: smelting electrolytic aluminum liquid and aluminum ingots into aluminum melt → preparing 3-5mm thick aluminum coils through continuous casting and rolling process → cold rolling → longitudinal shearing edge → foil rolling → finished product slitting → Finished product annealing → Check the packaging process to prepare high-strength aluminum foil for tableware, in which ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of high-strength tableware aluminum foil. The preparation method comprises the following steps that electrolytic aluminum liquid and an aluminum ingot are smelted into an aluminum melt, an aluminum foil coil with the thickness of 3-5 mm is prepared through a continuous casting process and a continuous rolling process, and then the aluminum foil coil is subjected to cold rolling, longitudinal shearing and side shearing, foil rolling, finished product slitting, finished product annealing and inspection and packaging to prepare the high-strength tableware aluminum foil, wherein the longitudinal shearing and edge shearing, the finished product slitting and the inspection and packaging are carried out according to conventional processes, an aluminum foil roll with the thickness of 0.05-0.095 mm after the finished product annealing is made into the tableware aluminum foil, and after detecting, the tensile strength of the tableware aluminum foil is larger than or equal to 220 Mpa, the elongation rate is larger than or equal to 6%, and the cupping value is larger than or equal to 4 mm. According to the preparation method, the casting process and the secondary remelting process of the aluminum ingot are omitted, and measurement shows that 0.4-0.5% of aluminum loss can be reduced during the process that the aluminum liquid is cast into the aluminum ingot, 2-4% of the aluminum burning loss can be reduced during the secondary remelting process of the aluminum ingot, the energy is saved, and the production efficiency and the finished product ratio are improved.

Description

technical field [0001] The invention belongs to the technical field of aluminum foil processing, in particular to a preparation method of high-strength tableware aluminum foil. Background technique [0002] Tableware aluminum foil is also commonly known as container foil. It is an aluminum foil widely used in aviation food, fast food packaging and other fields. It is beautiful, generous, clean and hygienic. At present, the common alloys used in the production of container foils in the market are 8011, 3003 and so on. However, although this type of alloy has good plastic deformation ability, its strength is generally between 120 and 150Mpa. The lower strength causes the aluminum foil to be easily deformed and damaged after being stamped into a lunch box. However, if you want to maintain the good anti-deformation ability of the lunch box, you must increase the thickness of the aluminum foil, resulting in material waste. [0003] 3004 alloy has become the first choice for the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C21/08C22F1/047C22F1/04B21B1/40
CPCB21B1/40C22C21/00C22C21/08C22F1/04C22F1/047
Inventor 张安乐韩成艺刘雪梅
Owner LUOYANG LONGDING ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products