Synthesis process of an active antibacterial biological protective mask and its antibacterial material
A technology of biological protection and antibacterial agent, applied in the directions of biocides, animal repellents, and chemicals for biological control, etc., can solve the problems of secondary pollution and limited adsorption capacity, and avoid secondary pollution, particle Narrow diameter distribution and uniform particle effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] (1) Synthesis of antibacterial agent raw materials: calcium salt, phosphorus salt, and silver nitrate are synthesized in a solution system through "wet chemical reaction" to synthesize silver ion-doped calcium phosphate particles. The synthesized material is left to stand, aged, and prepared by Repeatedly wash with deionized water for 3 times, filter the sediment and dry it in low-temperature air, the diameter of the silver-doped calcium phosphate particle is 50-200nm, use it as the precursor powder for preparing the bioceramic body, the chemical reaction formula is as follows;
[0035] (10-x)Ca 2+ +xAg + +6PO 4 3- +2OH - → Ca 10-x Ag x (PO 4 ) 6 (OH) 2
[0036] (2) Preparation of antibacterial agent material: uniformly mix 1wt% polyvinyl alcohol into the silver ion-doped calcium phosphate precursor powder, mix 10wt% hydrogen peroxide, and the balance is deionized water to prepare a slurry, and pass through Prepare particles with a particle size of 1500um ~ 20...
Embodiment 2
[0047] The product preparation process and steps are the same as in Example 1, except that the thickness of each functional layer in step (7) is adjusted, and the structural system of the purchased mask is composed of the following percentages in the vertical direction of thickness: the outer (inner) cotton cloth spinning layer accounts for ratio of 20%; the sub-outer active carbon filter layer accounted for 40%, and the three-layer structure of the middle layer active antibacterial agent layer accounted for 40%. This example further expanded the thickness of the active antibacterial function layer, which showed obvious active antibacterial function According to the experimental test, its antibacterial rate against Staphylococcus aureus for 4 hours is ≥98%, and the antibacterial protection effect is good.
Embodiment 3
[0049] The product preparation process and steps are the same as in Example 1, except that the thickness of each functional layer in step (7) is adjusted, and the structural system of the purchased mask is composed of the following percentages in the vertical direction of thickness: the outer (inner) cotton cloth spinning layer accounts for ratio of 20%; the sub-outer activated carbon filter layer accounted for 60%, and the three-layer structure of the middle layer active antibacterial agent layer accounted for 20%. This example further expanded the thickness of the activated carbon filter layer, which showed better particle filtration. Function.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com