Coating adhesive for polyester clean clothes fabric and preparation method thereof

A technology of clean clothes and coating glue, which is applied in fiber treatment, textile and papermaking, biochemical fiber treatment, etc., to achieve excellent washing resistance, enhanced film-forming performance, and improved dust filterability

Active Publication Date: 2019-05-17
DANDONG UNIK TEXTILE
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After modification, the fabric has good antistatic properties, except for this, the fabric has no other properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Add the polybutadiene glycol 50 of the Polyethylene Glycol 10 of MDI 50, the Polyethylene Glycol 10 of average molecular weight 1450, the Polyethylene Glycol 15 of average molecular weight 1000, the average molecular weight 2000 of diphenylmethane diisocyanate (MDI) 50, the average molecular weight, and heat up to 75°C, react for 2.5 hours, then cool down to 50°C, add styrene 10, neoprene 10, methacryloyloxyethyltrimethylammonium chloride 5, deionized water 150, heat up to 75°C, drop A mixed solution containing initiator 2,2'-azobisisobutylamidine dihydrochloride 1 and deionized water 10 was added dropwise in 2 hours, then kept at 80°C for 1 hour, cooled to 45°C and discharged to obtain Acrylic modified polyurethane emulsion;

[0028] The acrylic modified polyurethane emulsion 100 prepared above was added to the polyurethane leveling rheological agent 2 and the blocked isocyanate crosslinking agent 2, stirred evenly, and filtered to obtain the product, the product visco...

Embodiment 2

[0030] Add the polybutadiene glycol 55 of the Polyethylene Glycol 12 of 60, the Polyethylene Glycol 12 of average molecular weight 1450, the Polyethylene Glycol 16 of average molecular weight 1000, the average molecular weight 2000 of diphenylmethane diisocyanate (MDI) 60, average molecular weight, heat up to 70°C, react for 2.6 hours, then cool down to 55°C, add styrene 12, neoprene 15, methacryloyloxyethyltrimethylammonium chloride 6, deionized water 180, heat up to 70°C, drop A mixed solution containing initiator 2,2'-azobisisobutylamidine dihydrochloride 1.5 and deionized water 15 was added dropwise in 2.2 hours, then kept at 81°C for 1 hour, cooled to 45°C and discharged to obtain Acrylic modified polyurethane emulsion;

[0031] The acrylic modified polyurethane emulsion 100 prepared above was added to the polyurethane leveling rheology agent 3 and the blocked isocyanate crosslinking agent 2.5, stirred evenly, and filtered to obtain the product, the product viscosity was ...

Embodiment 3

[0033] Add the polybutadiene glycol 58 of the Polyethylene Glycol 14 of 65, the Polyethylene Glycol 14 of average molecular weight 1450, the Polyethylene Glycol 18 of average molecular weight 1000, the average molecular weight 2000 of diphenylmethane diisocyanate (MDI) 65, average molecular weight into reaction kettle, be heated up to 78°C, react for 2.8 hours, then cool down to 56°C, add styrene 16, neoprene 17, methacryloyloxyethyltrimethylammonium chloride 8, deionized water 190, heat up to 78°C, drop A mixed solution containing initiator 2,2'-azobisisobutylamidine dihydrochloride 1.8 and deionized water 18 was added dropwise in 2.3 hours, then kept at 83°C for 1 hour, cooled to 45°C and discharged to obtain Acrylic modified polyurethane emulsion;

[0034] The acrylic-modified polyurethane emulsion 100 prepared above was added to the polyurethane leveling rheological agent 4 and the blocked isocyanate crosslinking agent 3, stirred evenly, and filtered to obtain the product ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a terylene cleanroom clothes fabric coating adhesive and a preparation method thereof. The terylene cleanroom clothes fabric coating adhesive is prepared by compounding 100 parts of acrylic acid modified polyurethane emulsion, 2 to 5 parts of a polyurethane flatting and rheological agent and 2 to 5 parts of an end-capped isocyanate cross-linking agent, wherein the acrylic acid modified polyurethane emulsion is prepared from the following raw materials in parts by weight: 50 to 70 parts of diphenylmethane diisocyanate, 10 to 15 parts of polyethylene glycol of which the average molecular weight is 1450, 15 to 20 parts of polyethylene glycol of which the average molecular weight is 1000, 50 to 60 parts of polybutadiene diol of which the average molecular weight is 2000, 10 to 20 parts of styrene, 10 to 20 parts of chloroprene rubber, 5 to 10 parts of methyl acrylyl ethyl trimethyl ammonium chloride, 150 to 200 parts of deionized water, and 1 to 2 parts of 2,2'-azobis(isobutylamidine dihydrochloride). Terylene conductive cloth finished by the coating adhesive has excellent antibacterial, anti-static, moisture permeable, air permeable and dust filtration performances, and excellent washing resistance.

Description

technical field [0001] The invention relates to fabric coating glue for textile fabrics, in particular to a polyester clean clothing fabric coating glue with durable antibacterial, moisture-permeable, antistatic, dust-filtering and air-permeable functions and a preparation method thereof. Background technique [0002] At present, the processing methods of clean clothing fabrics are mainly obtained by increasing the weaving density of fabrics, weaving conductive fibers and laminating PTFE on fabrics to minimize fabric voids, but the products produced by the above methods have high cost and antistatic properties. Low performance, poor air and moisture permeability, and decreased mechanical properties. [0003] "Preparation of Polyester Clean Clothing Fabrics by Wet Coating" published in the 22nd issue of "Printing and Dyeing" in 2009, which uses vinylidene chloride, polyethylene glycol, dimethylacetamide, dimethyl sulfoxide, lithium chloride, chlorine The coating solution mad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/356D06M15/564D06M13/395C08F283/00C08F212/08C08F220/34C08G18/76C08G18/69C08G18/48D06M101/32
CPCC08F283/006C08G18/4808C08G18/698C08G18/7671D06M13/395D06M15/356D06M15/564D06M16/00D06M2101/32C08F212/08
Inventor 张悦陈丽颖李喆孟雅贤
Owner DANDONG UNIK TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap