Weak solvent system PU resin and preparation method thereof

A technology of PU resin and weak solvent, applied in the field of weak solvent system PU resin and its preparation, can solve the problems of slow drying speed and unenvironmental protection of PU ink, and achieve the effects of low price, fast volatilization speed and improved efficiency.

Active Publication Date: 2017-09-22
肇庆市华莱特复合新型材料有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is that the current PU ink has the problems of slow drying speed and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The present invention includes the following raw materials in parts by weight: 71.74 parts of mixed solvent, 21.31 parts of polyester polyol, 5.68 parts of MDI, 1.07 parts of small molecule chain extender, 0.10 part of organic catalyst and 0.10 part of antioxidant .

Embodiment 2

[0032] The present invention includes the following raw materials in parts by weight: 68 parts of mixed solvent, 24 parts of polyester polyol, 7 parts of MDI, 0.9 part of small molecule chain extender, 0.05 part of organic catalyst and 0.05 part of antioxidant .

Embodiment 3

[0034] The present invention includes the following raw materials in parts by weight: 73 parts of mixed solvent, 19 parts of polyester polyol, 7 parts of MDI, 1.2 parts of small molecule chain extender, 0.15 parts of organic catalyst and 0.10 parts of antioxidant .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a weak solvent system PU resin and a preparation method thereof, wherein the weak solvent system PU resin comprises the following raw materials by weight: 68-73 parts of a mixed solvent, 19-24 parts of polyester polyol, 3-7 parts of MDI, 0.8-1.2 parts of a small molecule chain extender, 0.05-0.15 part of an organic catalyst, and 0.05-0.15 part of an antioxidant. According to the present invention, the weak solvent system PU resin is used in the shoe production industry, is particularly suitable for the surface coating decoration of PU materials, can be used for coat spraying and printing of the surface of shoe materials and the like, has advantages of fast evaporation and low cost, can greatly improve the efficiency of the sole modification process, and further has advantages of corresponding benefit increasing, energy saving, and high efficiency.

Description

technical field [0001] The invention relates to PU resin, in particular to a weak solvent system PU resin and a preparation method thereof. Background technique [0002] Now the PU inks on the market need to be diluted with strong soluble solvents such as cyclohexanone and DMF (Chinese name dimethyl fumarate), and the dilution ratio of the diluent is 1.5 to 2 times. The cyclohexanone in the diluent , DMF accounts for more than 45%, and PU ink needs to be added to improve adhesion by adding DMF. [0003] The use of strong solvents has the following disadvantages: [0004] (1) The volatilization speed is slow, the drying speed is slow, and the price is more expensive; [0005] (2) DMF is mainly used for sterilization and anti-mildew in the production, storage and transportation of leather, footwear and textiles. Standards (such as EU standards) clearly point out that DMF is a prohibited chemical; cyclohexanone has carcinogenic effects, and high concentrations of cyclohexano...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/42C08G18/66C08G18/76C08G18/08C08K5/524C09D175/06
Inventor 陈应华徐进勇
Owner 肇庆市华莱特复合新型材料有限公司