Injectable hydrogel and preparation method and application thereof

A technology for injecting water and hydrogel, which is applied in the fields of non-active ingredients medical preparations, pharmaceutical science, aerosol delivery, etc., to achieve the effects of easy adjustment, overcoming potential safety hazards, and controllable release effect

Active Publication Date: 2017-10-10
THE SECOND PEOPLES HOSPITAL OF SHENZHEN
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has been reported in the literature that gels and microgels composed of phenylboronic acid and poly(N-isopropylacrylamide) (PNIPAM) can swell and release insulin in the presence of glucose, but these materials can only be used above the pKa of phenylboronic acid. It has glucose responsiveness only at pH 9 and higher glucose concentration (20g / L), which limits its application under physiological conditions (pH 7.4, glucose concentration 1-3g / L) (Synthesis and Volume Phase Transitions of Glucose-Sensitive Microgels, Biomacromolecules 2006, 7, 3196-3201, Phenylboronic acid-based glucose-responsive polymeric nanoparticles: synthesis and applications in drug delivery, Polym.Chem., 2014, 5, 1503-1518)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Injectable hydrogel and preparation method and application thereof
  • Injectable hydrogel and preparation method and application thereof
  • Injectable hydrogel and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]Add 0.5 g of butyraldehyde-polyethylene glycol-butyraldehyde (m=100) and 1 g of four-arm terminal amino-modified polyethylene glycol (n=1000, Laysan) to 28.5 g of sterile deionized water, and shake rapidly at 37°C Mix well, and after 35 seconds, 30 g of injectable hydrogel in a transparent and uniform state are obtained.

[0036] The scanning electron microscope image of the injectable hydrogel is shown in figure 1 , showing that the hydrogel has a porous and dense structure with a pore size of 0.1mm-0.4mm.

Embodiment 2

[0038] Add 5g of butyraldehyde-polyethylene glycol-butyraldehyde (m=16000) and 1g of four-arm terminal amino-modified polyethylene glycol (n=5000, Laysan) to add 34g of disodium hydrogen phosphate-citric acid buffer (pH= 6.5), at 37°C, oscillate quickly and mix evenly, and after 30 seconds, 40 g of injectable hydrogel in a transparent and uniform state is obtained.

[0039] The scanning electron microscope image of the obtained injectable hydrogel shows that the hydrogel has a porous and dense structure with a pore diameter of 0.1mm-0.3mm.

Embodiment 3

[0041] 14g butyraldehyde-polyethylene glycol-butyraldehyde (m=10000) and polyethylene glycol (n=5700, Laysan) of 1g four-arm terminal amino-modification are added 85g disodium hydrogen phosphate-sodium dihydrogen phosphate buffer solution ( pH=7.4), 37° C., oscillating rapidly and mixing evenly, and after 25 seconds, 100 g of injectable hydrogel in a transparent and uniform state was obtained.

[0042] The scanning electron microscope image of the obtained injectable hydrogel shows that the hydrogel has a porous and dense structure with a pore diameter of 0.1mm-0.3mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses injectable hydrogel and a preparation method and application thereof. The injectable hydrogel is composed of a raw material A, a raw material B and gelling liquid, a mass sum of the raw material A and the raw material B accounts for 5-50% of mass of the hydrogel, the raw material A is butyraldehyde-polyethylene glycol-butyraldehyde, and the raw material B is four-arm-terminated amino modified polyethylene glycol. The injectable hydrogel is obtained by mainly utilizing imide dynamic bonds formed by amino of four-arm-terminated amino modified polyethylene glycol and aldehyde of butyraldehyde-polyethylene glycol-butyraldehyde. The injectable hydrogel can be applied as a drug carrier, an embolization material or a tissue engineering material. The preparation method includes steps: adding the gelling liquid into the raw material A and the raw material B, and well mixing to obtain the injectable hydrogel. The injectable hydrogel has the advantages of simple, convenient and quick preparation process and easiness in large-scale production.

Description

technical field [0001] The invention belongs to the technical field of biomolecular medicine, and in particular relates to an injectable hydrogel and its preparation and application. Background technique [0002] Hydrogel is a three-dimensional network structure cross-linked by polymers, and has a wide range of applications in biomedical fields such as drug release, tissue engineering, and biosensing. Injectable in situ gel systems have received extensive attention in minimally invasive medicine and injectable tissue engineering. The gel matrix mixes biomolecules or cells in the solution before injection, and the scaffold material loaded with biomolecules or cells can be implanted into the desired site after injection. After gelation, it becomes the drug release base or The cell growth basis of tissue regeneration avoids the pain and cumbersomeness of surgical implantation, and in situ cell fixation is also conducive to filling an irregular tissue defect. [0003] At prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/52A61L27/26A61L31/14A61L31/04A61K9/06A61K47/10
CPCA61K9/0002A61K9/0019A61K9/06A61K47/10A61L27/26A61L27/52A61L31/041A61L31/145A61L2400/06A61L2430/36C08L71/02
Inventor 谭回李维平黄贤键黄国栋刘文兰
Owner THE SECOND PEOPLES HOSPITAL OF SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com