Ray-proof composite wallboard for electric power dispatching machine room
A composite wallboard and power dispatching technology, applied in building components, building materials, buildings, etc., can solve the problems of destroying bioelectric current and biomagnetic field, cumbersome wallboard preparation method, poor radiation protection effect, etc., to reduce the cost of raw materials, Improve compatibility and foaming ratio, good effect of flame retardant and thermal insulation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1
[0023] The radiation-proof composite wallboard for the power dispatching computer room is prepared from the following parts by weight of raw materials: 1 part of radiation protection agent, 1 part of flame retardant, 2 parts of foaming agent, 3 parts of graphite powder, 30 parts of polypropylene resin, and 50 parts of styrene particles;
[0024] The anti-radiation agent is prepared according to the following process: add lead sulfate, barium sulfate and iron powder in a mass ratio of 1:1:2 into a ball mill tank containing absolute ethanol, mix them well, and give a ball-to-material ratio of 5 Add alumina ceramic balls at a weight ratio of 1: 1, the ball milling temperature is room temperature, the ball mill speed is 500 rpm, the material is ball milled to more than 500 mesh, and the absolute ethanol is evaporated to get it.
[0025] The flame retardant is formed by mixing magnesium oxide and aluminum oxide in a mass ratio of 2:1.
[0026] The foaming agent is prepa...
Example Embodiment
[0029] Example 2
[0030] The radiation-proof composite wallboard for the power dispatching computer room is prepared from the following parts by weight of raw materials: 2 parts by weight of anti-radiation agent, 2 parts of flame retardant, 3 parts of foaming agent, 5 parts of graphite powder, 50 parts of polypropylene resin, and 70 parts of styrene particles;
[0031] The anti-radiation agent is prepared according to the following process: add lead sulfate, barium sulfate and iron powder in a mass ratio of 1:1:2 into a ball mill tank containing absolute ethanol, mix them well, and give a ball-to-material ratio of 5 Add alumina ceramic balls at a weight ratio of 1: 1, the ball milling temperature is room temperature, the ball mill speed is 500 rpm, the material is ball milled to more than 500 mesh, and the absolute ethanol is evaporated to get it.
[0032] The flame retardant is formed by mixing magnesium oxide and aluminum oxide in a mass ratio of 2:1.
[0033] The foaming agent is...
Example Embodiment
[0036] Example 3
[0037] Test detection of performance parameters of wallboard composite material prepared by the invention:
[0038] Comparative test: PVC panels commonly used in the market; wall panels prepared in Example 1 of the present invention; all with a thickness of 10 mm as an example. The water absorption rate is determined as follows: accurately weigh the weight of the completely dry test block with a balance m, then put the test block in water at about 30 degrees Celsius, take it out of the water after 1 hour, wipe off the surface moisture with a dry towel, and weigh the test block again The weight n is obtained by multiplying (nm) / m by 100% to obtain the water absorption; the compressive strength refers to the B / T17669.3-199 standard; the sound insulation detection refers to the "classification and detection method of air sound insulation performance of building doors and windows" GB / T 8485-2008, see Table 1 for specific results.
[0039] Table 1
[0040] Group
[...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap