Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Cotton cellosilk and bamboo cellosilk mixed spinning process

A technology of bamboo fiber silk and cotton fiber silk, which is used in textiles, textiles, papermaking, looms, etc., can solve the problems of multi-blocks and unsatisfactory effects, and achieves the effect of not easy to break and reducing the number of blocks.

Inactive Publication Date: 2017-10-24
RUGAO XIAYUAN SCI & TECH ESTABLISH A BUSINESS SERVICES CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of the above-mentioned traction and pretreatment process is still unsatisfactory, and there will still be more baffles in the final woven product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Present embodiment cotton fiber silk and bamboo fiber silk mixed textile process, this mixed textile process comprises the steps:

[0026] (1) Measure the stretchable maximum of bamboo fiber silk, that is, the maximum pressure value that can be applied to it;

[0027] (2) Put the cotton fiber silk in a water steamer, steam for 70 minutes at a water temperature of 85°C;

[0028] (3) Place the cotton fiber thread treated in step (2) in a natural state for pre-setting for 16 hours;

[0029] (4) Use the water-jet loom to carry out mixed spinning with the maximum pressure value in step (1) and the ratio of cotton fiber silk and bamboo fiber silk is 2:1; wherein, when the water-jet loom draws the cotton fiber silk, the specification is 75-40 nozzle, the nozzle with specification 45-20 is used when pulling the bamboo fiber filaments.

Embodiment 2

[0031] Present embodiment cotton fiber silk and bamboo fiber silk mixed textile process, this mixed textile process comprises the steps:

[0032] (1) Measure the stretchable maximum of bamboo fiber silk, that is, the maximum pressure value that can be applied to it;

[0033] (2) Put the cotton fiber in a water steamer at a water temperature of 75°C and steam for 80 minutes;

[0034] (3) Place the cotton fiber thread treated in step (2) in a natural state for pre-setting for 12 hours;

[0035] (4) Use the water-jet loom to carry out mixed spinning with the maximum pressure value in step (1) and the ratio of cotton fiber silk and bamboo fiber silk is 2:1; wherein, when the water-jet loom draws the cotton fiber silk, the specification is 75-40 nozzle, the nozzle with specification 45-20 is used when pulling the bamboo fiber filaments.

Embodiment 3

[0037] Present embodiment cotton fiber silk and bamboo fiber silk mixed textile process, this mixed textile process comprises the steps:

[0038] (1) Measure the stretchable maximum of bamboo fiber silk, that is, the maximum pressure value that can be applied to it;

[0039] (2) Put the cotton fiber in a water steamer at a water temperature of 80°C and steam for 75 minutes;

[0040] (3) Place the cotton fiber thread treated in step (2) in a natural state for pre-setting for 14 hours;

[0041] (4) Use the water-jet loom to carry out mixed spinning with the maximum pressure value in step (1) and the ratio of cotton fiber silk and bamboo fiber silk is 2:1; wherein, when the water-jet loom draws the cotton fiber silk, the specification is 75-40 nozzle, the nozzle with specification 45-20 is used when pulling the bamboo fiber filaments.

[0042] In summary, as described in Examples 1-3, compared with the existing mixed textile process of the enterprise, the improved process of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cotton cellosilk and bamboo cellosilk mixed spinning process. The cotton cellosilk and bamboo cellosilk mixed spinning process comprises the following steps: (1) measuring a maximum extension extent of bamboo cellosilk, namely measuring the value of maximum pressure which can be applied to the bamboo cellosilk; (2) placing cotton cellosilk in a water steaming box, and steaming for 70-80 minutes at the water temperature of 75-85 DEG C; (3) pre-shaping the cotton cellosilk which is treated in the step (2) in a natural state for 12-16 hours; and (4) carrying out mixed spinning on the cotton cellosilk and the bamboo cellosilk through a hydraulic loom by the maximum pressure value obtained in the step (1). When the hydraulic loom pulls the cotton cellosilk, a nozzle with the specification of 75-40 is used; and when the hydraulic loom pulls the bamboo cellosilk, a nozzle with the specification of 45-20 is used. The cotton cellosilk and bamboo cellosilk mixed spinning process has the advantages that the shortcoming of poor quality of woven products due to different characteristics of the cotton cellosilk and the bamboo cellosilk during mixed spinning by the cotton cellosilk and the bamboo cellosilk can be overcome.

Description

technical field [0001] The invention relates to a weaving process, in particular to a weaving process using different raw material silks for mixed weaving. Background technique [0002] When using different raw material yarns for mixed spinning, the tension of various raw material yarns and suitable processing temperature are important parameters that affect the quality of the final product. Therefore, it is necessary to take into account the characteristics of different raw material yarns when designing the textile process. For example, when we use cotton fiber silk and bamboo fiber silk to weave into fabrics, because the characteristics of cotton fiber silk and bamboo fiber silk are quite different, we need to use a specific process for weaving. Specifically, bamboo fiber silk is soft and comfortable, has good hygroscopicity, but weak elastic recovery ability; while cotton fiber silk has good hot water resistance and good elastic recovery ability. In order to take care of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/04D03D47/32
CPCD02G3/042D03D47/32D10B2201/02D10B2201/10D03D15/47
Inventor 曹建民
Owner RUGAO XIAYUAN SCI & TECH ESTABLISH A BUSINESS SERVICES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com