Science and technology decoration material

A decorative material and technological technology, applied in the field of wood, can solve the problems of rare, less research and application of glass fiber, and achieve the effect of bright color, more dynamic and dynamic patterns, and higher heat resistance temperature

Inactive Publication Date: 2017-11-07
龙门县品汐竹木制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are few studies and applications of glass fiber in wood-plastic composite materials, and there are few research reports on its performance, and the relevant research reports on the actual working conditions of materials are even rarer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Science and technology decoration material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] A technological decorative material, comprising a core board 1, the raw materials of the core board 1 and the parts by weight of each raw material are

[0071] 27 parts of balsa wood powder;

[0072] 20 parts of bamboo charcoal powder;

[0073] 15 parts of low floating fiber non-alkali long cut glass fiber;

[0074] 6 parts of polyolefin elastomer;

[0075] 12 parts of compound vegetable dyes;

[0076] Basalt fiber 20 parts;

[0077] 19 parts of cyanuric chloride;

[0078] 10 parts of cinchonidine sulfate;

[0079] Chitosan quaternary ammonium salt 19 parts;

[0080] 18 parts of octadecyldimethylamine;

[0081] 6 parts of ethylene carbonate;

[0082] Described balsa wood powder is the powder that the leftovers when balsa wood manufactures products are ground into, and particle size is 130 microns;

[0083] Described bamboo charcoal powder is the powder that bamboo obtains after calcining, grinding, pickling, calcining, and particle size is 320 microns;

[0084...

Embodiment 2

[0093] A technological decorative material, comprising a core board 1, the raw materials of the core board 1 and the parts by weight of each raw material are

[0094] 22 parts of balsa wood powder;

[0095] 29 parts of bamboo charcoal powder;

[0096] 11 parts of low floating fiber non-alkali long cut glass fiber;

[0097] 9 parts of polyolefin elastomer;

[0098] 9 parts of compound vegetable dyes;

[0099] Basalt fiber 16 parts;

[0100] 21 parts of cyanuric chloride;

[0101] 7 parts of cinchonidine sulfate;

[0102] Chitosan quaternary ammonium salt 11 parts;

[0103] 13 parts of octadecyldimethylamine;

[0104] 3 parts ethylene carbonate;

[0105] Described balsa wood powder is the powder that the leftovers when balsa wood manufactures products are ground into, and particle size is 150 microns;

[0106] Described bamboo charcoal powder is the powder that bamboo obtains after calcining, grinding, pickling, calcining, and particle size is 450 microns;

[0107] The...

Embodiment 3

[0116] A technological decorative material, comprising a core board 1, the raw materials of the core board 1 and the parts by weight of each raw material are

[0117] 34 parts of balsa wood powder;

[0118] 16 parts of bamboo charcoal powder;

[0119] 19 parts of low floating fiber non-alkali long cut glass fiber;

[0120] 4 parts polyolefin elastomer;

[0121] 16 parts of compound vegetable dyes;

[0122] Basalt fiber 16 parts;

[0123] 21 parts of cyanuric chloride;

[0124] 7 parts of cinchonidine sulfate;

[0125] Chitosan quaternary ammonium salt 26 parts;

[0126] 25 parts of octadecyldimethylamine;

[0127] 9 parts of ethylene carbonate;

[0128] Described balsa wood powder is the powder that the leftovers when balsa wood manufactures products are ground into, and particle size is 100 microns;

[0129] Described bamboo charcoal powder is the powder that bamboo obtains after calcining, grinding, pickling, calcining, and particle size is 250 microns;

[0130] Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Graininessaaaaaaaaaa
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a technological decorative material, comprising a core board, the raw materials of the core board and the parts by weight of each raw material are 22-34 parts of balsa wood powder; 16-29 parts of bamboo charcoal powder; 11-19 parts of glass fiber; 4-9 parts of polyolefin elastomer; 9-16 parts of composite vegetable dye; 16-23 parts of basalt fiber; 17-21 parts of cyanuric chloride; 7-15 parts of cinchonidine sulfate; 11-26 parts of chitosan quaternary ammonium salt; 13-25 parts of octadecyl dimethylamine; 3-9 parts of ethylene carbonate. The invention has the characteristics of high hardness and light specific gravity, and its properties of compression resistance, bending resistance and impact resistance are superior to those of natural wood. Environmental protection, flame retardant, moisture-proof, moth-proof, no deformation, high hardness, not afraid of water immersion, easy maintenance, high wear resistance, longer service life, etc. Simultaneously, the present invention also adds compound vegetable dyes, endows multiple colors, and simultaneously the color and luster is brighter, and the three-dimensional sense of texture is stronger.

Description

technical field [0001] The invention relates to the technical field of wood, in particular to a technological decorative material. Background technique [0002] The decoration materials are divided into two parts, one is outdoor materials and the other is indoor materials. Indoor materials are further divided into five types: solid materials, plates, sheets, profiles, and wires. The real material is the raw material, and the upper part refers to logs and logs. Commonly used logs include fir, Korean pine, elm, ash, camphor, and basswood, and the more expensive ones include rosewood, beech, and oak. The wooden squares used in the decoration are mainly made of fir, and other woods are mainly used for supporting furniture and carved accessories. Traditional decorative materials need to consume a lot of wood and metal materials, and there are problems such as fear of water and fire, radioactive pollution, excessive formaldehyde content, cumbersome installation and construction...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B30/02C04B111/20C04B111/27C04B111/28C04B111/40C04B111/82
CPCC04B30/02C04B2111/20C04B2111/27C04B2111/28C04B2111/40C04B2111/82C04B2201/20C04B2201/50
Inventor 王历文
Owner 龙门县品汐竹木制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com