Titanium alloy barrel class part hot circling forming method
A titanium alloy and cylinder technology, which is applied in the field of forming a cylinder or a conical cylinder by bending a titanium alloy billet, can solve the problems of low forming quality, poor cold forming performance, long working time, etc., and achieves fewer processing steps. , improve efficiency, small impact effect
Active Publication Date: 2017-12-12
BEIJING HANGXING MACHINERY MFG CO LTD
View PDF9 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] As a commonly used metal material in the aerospace industry, titanium alloy has poor cold forming performance and has always been an important problem in production tests, especially when forming common cylinder and cone parts, titanium alloy after conventional cold forming The resulting springback causes the actual plastic deformation to be very small, and the process has to be repeated multiple times, the working time is long, the efficiency is low, and the final forming quality is not high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0038] The material of the titanium alloy conical cylinder part is TA15 titanium alloy. The diameters of the two ends of the conical cylinder are 280mm and 320mm respectively, the height of the part is 800mm, and the wall thickness is 2mm. , the distance between the two ends of the billet in the final free state is not more than 20mm;
[0039] The specific real-time method is carried out according to the following process steps:
[0040] (1) Prepare the blank;
[0041] The blank includes a processing body and a fixed part located at the top and bottom of the processing body. The shape and size of the processing body are consistent with the expanded shape and size of the titanium alloy cylinder parts to be formed. The fixed part refers to the The height direction of the top and bottom of the processing main body is not less than 20mm; the number of design positioning gaps is 9 pairs, such as figure 1 As shown; according to the calculated blank size, the blank is laser cut;
...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| height | aaaaa | aaaaa |
| diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a titanium alloy barrel class part hot circling forming method, in particular to a method applied to titanium alloy barrel and conic barrel hot circling forming, namely a method applied to titanium alloy barrel and conic barrel circling forming under the hot state. The method is suitable for bending and circling on a titanium alloy blank into a barrel or a conical part under the heat state, and the method belongs to the technical field of titanium alloy forming. When the method is used for preparing titanium alloy barrel class parts, springback generated by titanium alloy performance during cold forming can be effectively avoided, the barrel class part circling forming efficiency is improved, the part circling quality is improved, the follow-up machining processes of the formed part are fewer, influences of the forming process on the quality of the part surface are small, and the parts are free of folding after circling.
Description
technical field [0001] The invention relates to a method for forming a hot circle of a titanium alloy cylinder part, in particular to a method for forming a hot circle of a titanium alloy cylinder and a cone, that is, a method for forming a circle of a titanium alloy cylinder and cone. The invention discloses a circle forming method in a hot state, which is suitable for bending a titanium alloy billet into a cylinder or a conical cylinder part in a heat state, and belongs to the technical field of titanium alloy forming. Background technique [0002] As a commonly used metal material in the aerospace industry, titanium alloy has poor cold forming performance and has always been an important problem in production tests, especially when forming common cylinder and cone parts, titanium alloy after conventional cold forming The resulting springback causes the actual plastic deformation to be very small, and the process has to be repeated multiple times, resulting in long working...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/08B21D5/10
CPCB21C37/08B21D5/10
Inventor 李保永徐凯姚为闫寒吴凯秦中环刘伟刘奇李信
Owner BEIJING HANGXING MACHINERY MFG CO LTD