Process control method for glass plate tempering process

A technology of process and control method, which is applied in glass tempering, glass manufacturing equipment, temperature control by electric means, etc., can solve problems such as heating furnace temperature error, and achieve easy monitoring, which is beneficial to production process and product quality, The effect of reducing labor costs

Active Publication Date: 2020-04-14
洛阳兰迪智能科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a method for controlling the tempering process of glass plates in order to solve the problems in the prior art that the heating furnace is determined by estimating and directly monitoring the internal temperature of the heating furnace to cause errors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process control method for glass plate tempering process
  • Process control method for glass plate tempering process
  • Process control method for glass plate tempering process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Such as figure 1 As shown, the executive mechanism is a driving mechanism for controlling the movement of the glass plate into the furnace, and the control process of the heating control method of the present invention is as follows:

[0031] First determine the heating furnace to be used, adjust the working temperature of the heating furnace according to the type of glass plate to be heated (such as low-emissivity coated glass, clear glass) and thickness information, and run the heating furnace at room temperature without load to reach the working temperature. Monitor the percentage of the number of temperature measuring units that have not reached the set temperature of the heating element in this state to the total number of temperature measurement units, and measure the percentage of the number of temperature measurement units that have not reached the set temperature at five different times The percentage of the number of units, average the five values, and the ave...

Embodiment 2

[0034] Such as figure 2 As shown, the executive mechanism is a driving mechanism for controlling the movement of the glass plate out of the furnace. The control process of the heating control method of the present invention is as follows:

[0035] First determine the heating furnace to be used, adjust the working temperature of the heating furnace according to the type of glass plate to be heated (such as low-emissivity coated glass, clear glass) and thickness information, and run the heating furnace at room temperature without load to reach the working temperature. Monitor the percentage of the number of temperature measuring units that have not reached the set temperature of the heating element in this state to the total number of temperature measurement units, and measure the percentage of the number of temperature measurement units that have not reached the set temperature at five different times Percentage of the number of units, average five values, the average is the s...

Embodiment 3

[0038] Such as image 3 As shown, the executive mechanism is a control mechanism that controls the opening of the cooling fan or changes from an idle state to a working state. The control process of the control method of the present invention is as follows:

[0039] First determine the heating furnace to be used, adjust the working temperature of the heating furnace according to the type of glass plate to be heated (such as low-emissivity coated glass, clear glass) and thickness information, and run the heating furnace at room temperature without load to reach the working temperature. Monitor the percentage of the number of temperature measuring units that have not reached the set temperature of the heating element in this state to the total number of temperature measurement units, and measure the percentage of the number of temperature measurement units that have not reached the set temperature at five different times. The percentage of the number of temperature units, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a control method for a tempering technological process of a glass plate. The control method comprises the following steps: in a working process of a heating furnace, monitoring temperature information in the heating furnace in real time through temperature measuring units; counting up the quantity of the temperature measuring units, which do not reach pre-set temperature, through a control unit; calculating the percentage of the quantity of the temperature measuring units which do not reach the pre-set temperature in the quantity of all temperature measuring units; carrying out filtering processing on a calculation result; then comparing the calculation result of the filtering processing with a pre-set threshold value; when the percentage of the quantity of the temperature measuring units which do not reach the pre-set temperature in the quantity of all the temperature measuring units reaches maximum and minimum values, sending out an instruction to an executing mechanism by the control unit when the percentage is less than or equal to the pre-set threshold value in a decreasing process. According to the control method provided by the invention, a traditional control method taking time as evidences is changed and a novel control method for the tempering technological process of the glass plate is provided.

Description

technical field [0001] The invention relates to a glass production process, in particular to a glass plate tempering process control method. Background technique [0002] In the tempering process of the glass plate, the glass plate is first heated to the softening temperature (for example, 600°C to 700°C), and then the tempering process is completed by rapid cooling, among which, the heating of the glass plate is an important process . [0003] According to the process requirements, before the glass plate is transported into the heating furnace, the heating furnace in the cold state or heat preservation state must be heated to the set temperature. In the prior art, the conventional method is: firstly, preset the temperature value achieved by heating according to the type, thickness and past operating experience of the glass plate; then, when the measurement result of the temperature sensor in the furnace reaches the set temperature value, In order to eliminate the influenc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B27/012G05D23/19
CPCC03B27/012G05D23/19C03B27/0417
Inventor 赵雁窦高峰江春伟
Owner 洛阳兰迪智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com