Construction technology for pasting carbon fiber cloth in repairing process of bridge crack

A crack repair and carbon fiber cloth technology, applied in the field of technology, can solve the problems of easy falling off, exposed cracks, hidden dangers of bridge safety, etc., and achieve the effects of simple operation steps, tight sticking, and guaranteeing service life and safety.

Inactive Publication Date: 2018-03-06
彭建明
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the above-mentioned existing poor sticking effect on carbon fiber cloth, resulting in poor coverage of cracks, easy to fall off after a period of use, causing cracks to be exposed, cracks will continue to expand, and cause hidden dangers to the safety of the bridge. A construction process for pasting carbon fiber cloth in the repair of bridge cracks is designed. The operation steps of this process are simple and can ensure that the carbon fiber cloth is tightly pasted and will not fall off in the natural environment. The cracks are repaired to ensure The service life and safety of the bridge solve the problem that the existing poor sticking effect of carbon fiber cloth leads to poor coverage of cracks, and it is easy to fall off after a period of use, causing cracks to be exposed, and the cracks will continue to expand, causing hidden dangers to the safety of the bridge question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0012] The construction process of sticking carbon fiber cloth in bridge crack repair includes the following steps:

[0013] (1) Cut the carbon fiber cloth according to the size required by the design. Before construction, the surface moisture content of the concrete at the paste site and the ambient temperature should be measured. If the concrete surface moisture content is >4% or the ambient temperature is <5°C, measures should be taken. Construct after meeting the requirements;

[0014] (2) Remove the loose parts on the surface of the reinforced member until the concrete structure layer is exposed. If there are cracks, they should be repaired first, and then repaired with repair materials, and the thickness of the concrete protective layer should not be less than 15mm. If it is solid, impurities such as laitance layer and oil stain should also be removed, and it should be polished until the new aggregate surface is exposed, and the flatness should reach 5mm / m; the corner of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a construction process for pasting carbon fiber cloth in repairing bridge cracks. The carbon fiber cloth is cut according to the size required by the design. Before construction, the surface moisture content of the concrete at the pasting part and the ambient temperature are measured, and the reinforced components are removed. On the loose part of the surface, until the concrete structure layer is exposed, the prepared adhesive is evenly applied to the concrete surface of the part that needs to be pasted, and the cut carbon fiber cloth is applied on the base layer coated with the adhesive. The primer should be roller brush or special The brush is evenly applied on the concrete surface that has been wiped clean with acetone, and the special roller is used to roll the surface of the carbon fiber cloth several times along the fiber direction. It will not fall under the environment, and the cracks have been repaired to ensure the service life and safety of the bridge.

Description

technical field [0001] The invention relates to a technology, in particular to a construction technology for pasting carbon fiber cloth in repairing bridge cracks. Background technique [0002] A bridge refers to a building erected on rivers, lakes and seas to enable the smooth passage of vehicles and pedestrians. It is called a bridge. A bridge is generally composed of a superstructure, a substructure, a support and ancillary structures. The superstructure is also called a bridge span structure, which is the main structure for crossing obstacles; the substructure includes abutments, piers and foundations; Or the force transmission device installed at the supporting place of the bridge abutment; the auxiliary structures refer to the bridge head board, conical slope protection, bank protection, diversion works, etc. Bridges are actually divided into three categories: girder bridges, arch bridges and suspension bridges, and cable-stayed bridges. Girder bridges are generally ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01D22/00
CPCE01D22/00
Inventor 彭建明
Owner 彭建明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products