High-Cr-content cast heading machine cutter steel and manufacturing technique thereof

A manufacturing process and tool steel technology, which is applied in the field of new high-Cr casting roadheader tool steel and its manufacturing process, can solve the problems of difficult to obtain imported tools, save processing hours, improve thermal fatigue crack level, and improve oxidation and corrosion resistance effect of ability

Active Publication Date: 2018-04-06
JILIN UNIV
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, domestic roadheader cutting tool production companies have also started one after another (the components are shown in Table 2), such as China Shield Engineering Tool Co., Ltd., Luoyang Jiujiu Technology Co., Ltd., China Railway Tunnel Equipment Manufacturing Co., Ltd., etc., but most Some are still in the imitation stage, and it is difficult to meet the standards of imported knives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-Cr-content cast heading machine cutter steel and manufacturing technique thereof
  • High-Cr-content cast heading machine cutter steel and manufacturing technique thereof
  • High-Cr-content cast heading machine cutter steel and manufacturing technique thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) The chemical composition of the new high-Cr cast roadheader tool steel is by weight percentage:

[0045] C: 0.307; Cr: 8.151; Mo: 1.272; Ni: 0.564; V: 0.665; Mn: 0.131; Si: 0.648;

[0046] (2) The heat treatment process scheme and mechanical properties of this embodiment are shown in Table 4.

[0047] The high-Cr cast roadheader tool steel is mainly composed of lath martensite and retained austenite after heat treatment in schemes 2 to 4, and its mechanical properties have reached or exceeded that of forged high-carbon H13 roadheader tool steel. Among them, after process plan 3 heat treatment, the impact toughness increased by 19.4%, the tensile strength increased by 6.8%, the yield strength increased by 12.7%, and the elongation increased by 18.0%; the oxidation weight was increased by oxidation at 550°C for 60 hours in the air environment. 42.4% of H13 steel; after 10,000 thermal cycles at 550°C → 25°C, the length and number of thermal fatigue cracks were signifi...

Embodiment 2

[0055] (1) The chemical composition of high-Cr cast roadheader tool steel is by weight percentage:

[0056] C: 0.415; Cr: 10.163; Mo: 2.171; Ni: 1.233; V: 0.804; Mn: 0.235; Si: 0.706;

[0057] (2) The heat treatment process characteristics of the new high-Cr cast roadheader tool steel are shown in Table 6.

[0058] The new high-Cr cast roadheader tool steel is mainly composed of lath martensite and retained austenite after heat treatment in schemes 2 to 4, and its mechanical properties have met or exceeded that of forged high-carbon H13 roadheader tool steel. Among them, after the heat treatment process scheme 3, the hardness increased by 1.5HRC, the impact toughness increased by 17.8%, the tensile strength increased by 13.5%, the yield strength increased by 19.5%, and the elongation increased by 13.8%. Oxidation at 550°C in the air environment 60-hour oxidation weight gain is 40.5% of that of forged H13 steel; after 10,000 thermal cycles at 550°C → 25°C, the oxidation corros...

Embodiment 3

[0065] (1) The chemical composition of the new high-Cr cast roadheader tool steel is by weight percentage:

[0066] C: 0.547; Cr: 11.89; Mo: 2.880; Ni: 1.692; V: 0.947; Mn: 0.384; Si: 0.771;

[0067] (2) The heat treatment process characteristics of the new high-Cr cast roadheader tool steel are shown in Table 8.

[0068] After the heat treatment of the new high-Cr cast roadheader tool steel through heat treatment schemes 1 to 3, the structure is mainly lath martensite, and at the same time, high-carbon acicular martensite appears in different degrees, and the plasticity and toughness decrease. Compared with forged high-carbon H13 roadheader tool steel, the hardness is increased by 2-3HRC, the tensile strength is increased by 8.3%-11.5%, and the yield strength is increased by 13.2%-19.5%. When the quenching temperature is higher than 1100 °C, quenching cracks on the surface of the sample are more obvious. Oxidation at 550°C for 60 hours in the air environment, oxidation weig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to high-Cr-content cast heading machine cutter steel. The cutter steel comprises the chemical components of, by weight, 0.30%-0.55% of C, 8.0%-12.0% of Cr, 1.2%-3.0% of Mo, 0.5%-1.8% of Ni, 0.6%-1.0% of V, 0.1%-0.4% of Mn, 0.6%-0.8% of Si, 0.04%-0.30% of N, no more than 0.005% of S, no more than 0.03% of P and the balance Fe. The cutter steel manufacturing technique comprisesthe following steps that a near-net shape blank of a cutter is obtained through precise casting, then heat treatment is conducted, and a finished product is obtained directly after fine machining. Yield strength and tensile strength are improved while the hardness, impact toughness and elongation of the cutter steel all can reach the level of domestic forged heading machine cutter steel; the oxidation corrosion resistant capability, thermal fatigue resistant performance and abrasive grain abrasion resistance are improved; and the production period is shortened, and the production cost is reduced.

Description

technical field [0001] The invention belongs to the technical field of cutting tool steel manufacturing, and relates to a novel high-Cr cast roadheader cutting tool steel and a manufacturing process thereof. Background technique [0002] The cutter is the key component of the rock-breaking excavation of the roadheader, and it is also a consumable item. In the case of hard rock, more than 200 cutting tools of the roadheader are changed every month; the single-track tunnel of Guangzhou Metro Line 7 from Hanxi Changlong to Hezhuang is 1739 meters long, and the rock in most sections is hard rock. A total of 1097 single knives and 92 double knives have been replaced in the project. The cost of simple knives accounts for a large part of the construction cost, and it also seriously affects the construction progress (it takes about 1 hour to replace a knife), so the quality of the knives is directly related to the quality of the knives. Affect the rock-breaking ability and tunnelin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/46C22C38/04C22C38/02C22C33/06C21D1/18C21D1/74C21D9/22
Inventor 王金国房钦平姜启川闫瑞芳王慧远
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap