Machining method for bearing outer rings

A technology of bearing outer ring and processing method, applied in the field of bearing processing, can solve problems such as poor wear resistance, and achieve the effects of prolonging maintenance period, good surface wear resistance and saving use cost

Inactive Publication Date: 2018-05-01
方晓超
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a processing method for the outer ring of a bearing to solve the problem of poor wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Machining method for bearing outer rings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The principles and features of the present invention are described below in conjunction with the accompanying drawings, and the examples given are only used to explain the present invention, and are not intended to limit the scope of the present invention.

[0016] In the description of the present invention, it should be understood that the orientation or positional relationship indicated by the terms "upper", "lower", "center", "inner", "outer", "top", "bottom" etc. are based on the attached The orientation or positional relationship shown in the figure is only for the convenience of describing the present invention and simplifying the description, and does not indicate or imply that the referred device or element must have a specific orientation, be constructed and operated in a specific orientation, and therefore cannot be construed as a reference to this invention. Invention Limitations.

[0017] In the description of the present invention, it should be noted that ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
radiusaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of bearing machining, in particular to a machining method for bearing outer rings. The machining method for bearing outer rings comprises the following steps that anannular blank plate is fetched, an annular rolling groove with a U-shaped axial section is formed in the outer circumferential surface of a core roller of a cold rolling machine, and two inclined surfaces of the annular rolling groove have the same angle; and the blank plate is placed in the cold rolling machine and subjected to cold rolling machining, and a semi-finished product comprising two conical bearing outer rings is obtained. Strength and abrasion resistance are high, cold deformation molding is good, surface abrasion resistance is good, the overall quality of bearing products is improved, and the service life of bearing products is prolonged, so that the continuous operating time of equipment is effectively prolonged, the maintenance period of the equipment is prolonged, and theusing cost of the equipment is saved.

Description

technical field [0001] The invention relates to the field of bearing processing, in particular to a processing method for a bearing outer ring. Background technique [0002] At present, alloy steel has a history of more than one hundred years. The industrial use of alloy steel was about the second half of the 19th century. At that time, due to the increasing production and use of steel, the machinery manufacturing industry needed to solve the problem of steel In 1868, R.F. Mushet, an Englishman, invented self-hardening steel with a composition of 2.5% Mn-7% W, which increased the cutting speed to 5 m / min. With the development of commerce and transportation, a bridge with a span of 158.5 meters was built on the Mississippi River in the United States in 1870 with chrome steel (1.5-2.0% Cr); due to difficulties in processing components, later, some industrial countries switched to nickel Steel (3.5% Ni) for building long-span bridges. At the same time, some countries also use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21H1/12C22C38/14C22C38/02C22C38/12C22C38/04C22C38/08C22C38/16C22C38/28C22C38/22C22C38/20C22C38/50C22C38/44C22C38/42
CPCB21H1/12C22C38/002C22C38/02C22C38/04C22C38/08C22C38/12C22C38/14C22C38/16C22C38/20C22C38/22C22C38/28C22C38/42C22C38/44C22C38/50
Inventor 方晓超
Owner 方晓超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap