Method for producing gold powder frit on large scale

A production method and glass frit technology, applied in the field of production, can solve the problems of limited application scope of Venus glass, inability to mass-produce, high refractive index, etc., achieve good aesthetic and optical effects, facilitate mass production, and have a wide range of raw material sources. Effect

Inactive Publication Date: 2018-05-04
朱盛菁
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional Venus glass is produced by the crucible method, the output is low and the production cost is extremely high, the color is single, and the golden crystal particles are fine and completely opaque. This product does not conform to the modern aesthetic concept.
Modern Venus glass is made by adding metal oxide crystals on the surface of ordinary glass to achieve a high refractive index for light. The substrate is dark opaque glass, which is almost opaque and has no permeability as a whole. Glass can only be handcrafted and produced piece by piece, and cannot be mass-produced as a glass material, further limiting the range of applications of modern Venus glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of production method of large-scale production gold powder glass frit, concrete steps are as follows:

[0017] Step 1, put the glass raw material into a glass melting tank with a temperature of 1260 degrees Celsius, and the glass melting tank completely melts the glass raw material to obtain a glass melt;

[0018] Step 2, transporting molten glass to a clarification tank for clarification;

[0019] Step 3: The clarification tank is connected to the discharge port through the forehearth, and one or more feeding ports for feeding materials with metallic luster are arranged every 5 meters in the forehearth, and the clarified glass melt is artificially put into the metal The glossy powdery material is stirred with the stirring paddle. The order of putting in the metallic luster material and the stirring paddle is adjusted according to the needs of the user. When the user needs the material with metallic luster to be evenly distributed in the forming glass, the side i...

Embodiment 2

[0023] A kind of production method of large-scale production gold powder glass frit, concrete steps are as follows:

[0024] Step 1, put the glass raw material into a glass melting tank with a temperature of 1300 degrees Celsius, and the glass melting tank completely melts the glass raw material to obtain a glass melt;

[0025] Step 2, transporting molten glass to a clarification tank for clarification;

[0026] Step 3: The clarification tank is connected to the discharge port through the forehearth, and one or more feeding ports for putting in the material with metallic luster are set up every 3 meters in the forehearth, and the clarified glass liquid is put into the glass with metallic luster. Stir the material with the stirring paddle. The stirring speed of the stirring paddle is 400rpm. The order of putting in the material with metallic luster and stirring with the stirring paddle is adjusted according to the user's needs. On the side, first put the material with metallic...

Embodiment 3

[0030] A kind of production method of large-scale production gold powder glass frit, concrete steps are as follows:

[0031] Step 1, put the glass raw material into a glass melting tank with a temperature of 1420 degrees Celsius, and the glass melting tank completely melts the glass raw material to obtain a glass melt;

[0032] Step 2, transporting molten glass to a clarification tank for clarification;

[0033] Step 3: The clarification tank is connected to the discharge port through the forehearth, and one or more feeding ports for feeding materials with metallic luster are arranged every 8 meters in the forehearth, and the clarified glass melt is mechanically put into the The granular material with metallic luster is stirred with the stirring paddle. The stirring speed of the stirring paddle is 520rpm. The order of putting in the material with metallic luster and the stirring paddle is adjusted according to the user's needs. When the user needs to shape the glass with metal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing gold powder frit on a large scale. The method comprises the following specific steps: firstly, glass raw materials are put into a glass melting pool, anda glass melt is obtained; secondly, the glass melt is conveyed into a clarification tank for clarification; thirdly, the clarified glass melt is conveyed to a channel, a material with metallic lusteris added to the glass melt in the channel, and the mixture is stirred by a stirring paddle; fourthly, the glass melt flows into a molding position with a mold through a discharge port, and a finishedproduct can be obtained with a continuous casting method or press molding method. The gold powder frit prepared with the method has the advantages that the raw materials are widely sourced, the manufacturing process is simple, large-scale production is convenient, the produced frit is high in yield and low in production cost, particles provided with the metallic luster and used for production canbe sparse or dense and can be large or small, and have good light transmittance, refraction property and reflectivity, and good aesthetic and optical effects are realized. The production process canbe adjusted according to requirements of users, and different requirements of the users are met.

Description

technical field [0001] The invention relates to a production method, in particular to a production method for large-scale production of gold powder glass frit. Background technique [0002] Glass is formed by melting silicon dioxide and other chemical substances together, forming a continuous network structure during melting, and a silicate non-metallic material that gradually increases in viscosity and hardens during cooling to cause it to crystallize. With the development of science and technology, people have researched more types of glass, Venus glass is one of them. The traditional Venus glass is produced by the crucible method, the output is low and the production cost is extremely high, the color is single, and the golden crystal particles are fine and completely opaque. This product does not conform to the modern aesthetic concept. Modern Venus glass is made by adding metal oxide crystals on the surface of ordinary glass to achieve a high refractive index for light....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C1/04C03B1/00C03B1/02
CPCC03B1/00C03B1/02C03C1/04
Inventor 朱盛菁
Owner 朱盛菁