Steel for cold pressing stamping

A stamping and cold-pressing technology, applied in the field of cold-pressed steel, can solve the problems of poor polishing performance, easy wrinkling of ordinary steel, poor formability, etc., to improve the formability of finished products, ensure elongation performance, and improve toughness. and the effect of elongation

Inactive Publication Date: 2018-06-29
KUNSHAN YIBANGTAI AUTO PART MFG CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ordinary steel materials processed by cold stamping often have relatively poor formability; at the same time, due to the columnar grains produced during continuous casting, the microstructure clusters in the subsequent processing process cause ordinary steel to have the defect of being easy to wrinkle during cold rolling. The polishing performance after processing is also relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1, a steel for cold stamping, the weight components are as follows: 0.05wt%C, 0.4wt%Mn, 10wt%Cr, 0.5wt%Mo, 0.3wt%V, 0.5wt%Si, 0.6 wt%Ni, 0.01wt%S, 0.05wt%N, the balance is Fe and impurities.

Embodiment 2

[0028] Example 2, a steel for cold stamping, the weight components are as follows: 0.06wt%C, 0.45wt%Mn, 12wt%Cr, 1.0wt%Mo, 0.35wt%V, 0.8wt%Si, 0.7 wt%Ni, 0.02wt%S, 0.06wt%N, the balance is Fe and impurities.

Embodiment 3

[0029] Example 3, a steel for cold stamping, the weight components are as follows: 0.08wt%C, 0.5wt%Mn, 15wt%Cr, 1.5wt%Mo, 0.4wt%V, 1wt%Si, 0.9wt% %Ni, 0.03wt%S, 0.09wt%N, and the balance is Fe and impurities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses the steel for cold pressing stamping. The steel for cold pressing stamping is characterized by comprising the following ingredients, by weight, 0.05% to 0.08% of C, 0.4% to 0.5% of Mn, 10% to 15% of Cr, 0.5% to 1.5% of Mo, 0.3% to 0.4% of V, 0.5% to 1% of Si, 0.6% to 0.9% of Ni, 0.01% of 0.03% of S, 0.05% to 0.09% of N, the balance Fe and impurities. The steel for cold pressing stamping has the advantages that compared with the prior art, according to the formula of the steel for cold pressing stamping, the content of C, the content of N, the content of Mn, the contentof S, the content of Si and the content of Ni are respectively controlled within a certain range, the stretch property of the material is guaranteed, and the forming property of finished products is improved; and furthermore, the phenomenon that because of the overhigh content of C and N, the content of impurities is overhigh, intercrystalline carbide precipitates, and the forming property and thecorrosion resistance of cold stamping are poor is avoided, and the toughness and the ductility can be improved because that the Cr, Mo and Vi are added.

Description

technical field [0001] The invention relates to a kind of steel used for cold stamping processing, which belongs to the technical field of iron and steel materials. Background technique [0002] Ordinary steel materials processed by cold stamping often have relatively poor formability; at the same time, due to the columnar grains produced during continuous casting, the microstructure clusters in the subsequent processing process cause ordinary steel to have the defect of being easy to wrinkle during cold rolling. The polishing performance after processing is also relatively poor. However, cold stamping has high requirements on the formability and polishability of stainless steel materials. It is difficult for ordinary stainless steel to meet the high requirements of cold stamping. Therefore, in order to make ordinary stainless steel meet the high requirements of cold stamping , It is extremely important to further improve its wrinkle resistance and elongation. Contents of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/44C22C38/46C22C38/02
CPCC22C38/04C22C38/001C22C38/02C22C38/44C22C38/46
Inventor 郑坚雄
Owner KUNSHAN YIBANGTAI AUTO PART MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products