Method for preparing soluble potassium and calcium silicate soil conditioner through alkaline activation of potassium feldspar

A kind of technology of activating potassium feldspar and soil conditioner

Active Publication Date: 2018-07-03
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of method that alkali activates potassium feldspar to prepare soluble potassium and calcium silicate soil conditioner, this method solves the large energy consumption of utilizing potassium feldspar to extract soluble potassium process in the prior art, high cost, pollution Serious, low potassium extraction rate and other problems, at the same time, the reaction product is used to prepare a soil conditioner that has beneficial effects on plant growth and soil improvement, and realizes the comprehensive utilization of potassium feldspar with high added value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing soluble potassium and calcium silicate soil conditioner through alkaline activation of potassium feldspar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Add the prepared potassium hydroxide solution with a mass concentration of 1g / L into the reaction kettle with a cooling device, and add the oxidized Potassium content is 13.94%, silicon dioxide content is the potassium feldspar powder of 66.41% (passes through 100 mesh sieves after being pulverized), and calcium hydroxide is added to adjust the Ca / Si molar ratio in the mixture to be 0.9, and after mixing evenly, react at 190° C. for 6 hours, Stir well, and after the reaction is completed, cool down to below 100°C, and the filtrate obtained after suction filtration of the reaction product is a soluble potassium solution; wash the filter residue slurry twice, and dry the filter residue at 100°C after suction filtration. After testing, K in the filter residue 2 The content of O is 1.6%, and K is calculated 2 The dissolution rate of O was 92.78%; the content of citrate-soluble silica in the filter residue was 26.88%, the content of calcium oxide was 32.01%, and the water c...

Embodiment 2

[0029] The configured potassium hydroxide solution with a mass concentration of 50g / L is added to the reaction kettle with a cooling device, and the oxidation Potassium content is 12.04%, silicon dioxide content is 65.01% potassium feldspar powder (passes through 50 mesh sieves after crushing), and calcium oxide is added to adjust the Ca / Si molar ratio in the mixture to be 0.3, after mixing evenly, react at 210°C for 1h, fully Stir and cool down to below 100°C after finishing the reaction. The filtrate obtained after liquid-solid separation of the reaction product is a soluble potassium solution; wash the filter residue slurry 3 times, and dry the filter residue at 30°C after suction filtration. After testing, K in the filter residue 2 The content of O is 1.75%, calculated K 2 The dissolution rate of O was 91.17%; the content of citrate-soluble silica in the filter residue was 23.06%, the content of calcium oxide was 8.80%, and the moisture content of the filter residue was 3...

Embodiment 3

[0031] The configured potassium hydroxide solution with a mass concentration of 30g / L is added to the reaction kettle with a cooling device, and the oxidation Potassium feldspar powder with a potassium content of 10.21% and a silicon dioxide content of 68.02% (passed through a 80-mesh sieve after crushing), adding calcium hydroxide to adjust the Ca / Si molar ratio in the mixture to 1.5, and reacting at 160°C for 4.5 hours after mixing evenly , fully stirred, after the reaction was completed, the temperature was lowered to below 100°C, and the filtrate after suction filtration of the reaction product was a soluble potassium solution; the filter residue slurry was washed 4 times, and the filter residue was dried at 120°C after suction filtration. After testing, K in the filter residue 2 The content of O is 1.13%, it is calculated that K 2 The dissolution rate of O is 90.00%, the content of citrate-soluble silicon dioxide in the filter residue is 24.06%, the content of calcium ox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of comprehensive utilization of resources such as chemical engineering metallurgy and environmental protection and particularly relates to a method for preparing a soluble potassium and calcium silicate soil conditioner through alkaline activation of potassium feldspar. The method comprises the following steps; (1) mixing raw materials, namely mixing an alkalineactivating agent, potassium feldspar and a calcium preparation; (2) carrying out pressurization reaction, namely putting the mixture into a pressurization reaction kettle for reaction; (3) carrying out liquid-solid separation, namely cooling a reactant in the step (2), and carrying out liquid-solid separation, so as to obtain filtrate to prepare a soluble potassium solution; and (4) drying, namelywashing filter residues filtered in the step (3), washing, and drying, so as to obtain a calcium silicate soil conditioner. According to the method, the reaction rate is high, and the reaction residue has the characteristics of lightness and high water absorption rate, is rich in high-activity silicon and calcium, contains a small amount of potassium and is suitable for being used as the soil conditioner. The process has the advantages of simplicity in operation, low reaction temperature, environmental pollution and equipment requirements and the like and further has relatively good industrial prospects.

Description

technical field [0001] The invention belongs to the field of comprehensive utilization of resources such as chemical industry, metallurgy and environmental protection, and relates to a method for extracting soluble potassium, in particular to a method for preparing soluble potassium and calcium silicate soil conditioner by alkali-activating potassium feldspar. Background technique [0002] my country is rich in potassium ore resources, but the reserves of soluble potassium resources are small and the demand is large. At present, it mainly depends on imports. Potassium feldspar ore is an important insoluble potassium resource in my country. The ore reserves are large and widely distributed, but it is difficult to use it as a soluble potassium resource such as potash fertilizer. Therefore, it is of great significance to develop and utilize insoluble potassium feldspar ore to extract soluble potassium. [0003] At present, there are many kinds of techniques for extracting solu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/04C05D3/02C01D1/02C05G3/80
CPCC01D1/02C05D3/02C05G3/80
Inventor 王晓辉马淑花穆小占赵振清郑诗礼
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com