A kind of silicone material edge banding and production method thereof

A technology of edge banding and silicone, which is applied in the field of furniture edge banding, can solve the problems of small selection and few types of edge banding, and achieve the effects of easy operation, widening material types, and good heat resistance

Active Publication Date: 2021-03-16
ZHEJIANG WELLSCOM PLASTIC CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the fact that there are relatively few types of edge banding for existing furniture and less room for choice, the purpose of the present invention is to provide an edge banding made of organic silicon, which makes full use of the stability, electrical insulation performance, and weather resistance of the selected organic silicon. Silicone edge banding strips are prepared with properties such as water resistance and water resistance to meet the market's demand for edge banding strips

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of silicone material edge banding and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An edge banding strip made of silicone material, made of the following components: 30g of hydroxy-terminated dimethyl polysiloxane, 80g of ABS resin, 10g of EVA emulsion, 1g of polycaprolactone, 2g of cross-linking compounding agent, nano 15g of zirconia, 1g of silane coupling agent KH550, 0.5g of antioxidant DNP and 0.2g of nano-titanium dioxide, wherein the crosslinking compound consists of component A, component B and component C in a mass ratio of 10:1:5 Composition, component A is alkoxysilane, component B is dibutyltin dilaurate, component C is acrylic acid, and the cross-linking compounding agent can make hydroxyl-terminated dimethyl polysiloxane and EVA solution cross-linked respectively solidified.

[0029] The production method of the above-mentioned edge banding made of silicone material comprises the following steps:

[0030] (1) Premix the EVA emulsion with the cross-linking compounding agent and let it stand at room temperature for 2 hours, then mix it wi...

Embodiment 2

[0033] An edge banding strip made of silicone material, made of the following components: 35g of hydroxy-terminated diethyl polysiloxane, 85g of ABS resin, 12.5g of EVA emulsion, 2g of polycaprolactone, and 2.25g of cross-linking compounding agent , 17.5g of nano-zirconia, 1.25g of silane coupling agent KH550, 0.5g of antioxidant TNP and 0.25g of chopped carbon fiber, wherein the crosslinking compound is composed of component A, component B and component C in mass ratio It is composed of 10:1:5, component A is acetoxysilane, component B is dibutyltin dilaurate, component C is acrylic acid, and the cross-linking compounding agent can make hydroxyl-terminated diethyl polysiloxane and EVA solution were cross-linked and cured.

[0034] The production method of the above-mentioned edge banding made of silicone material comprises the following steps:

[0035] (1) After premixing the EVA emulsion with the cross-linking compounding agent, let it stand at room temperature for 2 hours,...

Embodiment 3

[0038] An edge banding strip made of silicone material, made of the following components: 40g of hydroxyl-terminated vinyl dimethyl polysiloxane, 90g of ABS resin, 15g of EVA emulsion, 3g of polycaprolactone, and 2.5g of cross-linking compounding agent g, nano-magnesium oxide 17.5g, silane coupling agent KH560 1.5g, antioxidant TPP 0.65g and sorbitol 0.3g, wherein the cross-linking compound consists of component A, component B and component C in mass ratio It is composed of 11:1:6.5, wherein component A is tetraethyl orthosilicate, component B is stannous octoate, and component C is crotonic acid. Joint curing.

[0039] The production method of the above-mentioned edge banding made of silicone material comprises the following steps:

[0040] (1) Premix the EVA emulsion with the cross-linking compounding agent, let it stand at room temperature for 3 hours, and then mix it with hydroxyl-terminated vinyl dimethyl polysiloxane, ABS resin, polycaprolactone, nano-magnesium oxide, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of furniture edge banding and particularly relates to an edge banding strip prepared from an organosilicone material and a production method thereof. The edge banding strip is prepared from hydroxyl group-containing organosilicone, a reinforcing resin, an EVA emulsion, polycaprolactone, a crosslinking compounding agent, a filler aid, a coupling agent, an antioxidant agent and an antistatic agent according to a specific amount ratio. The production method comprises: mixing the EVA emulsion and the crosslinking compounding agent, standing the mixture,mixing the mixture and other components, carrying out granulation, and carrying out extrusion molding through a twin-screw extruder. The edge banding strip fully utilizes the stability, electrical insulation properties, weather resistance and waterproof properties of the selected organosilicone, has strong tensile strength, toughness and other mechanical properties, has good heat resistance, aging resistance, UV resistance, electrical insulation, waterproof performances, moisture resistance and antistatic properties and broadens the material type range of edge banding strips.

Description

technical field [0001] The invention relates to the technical field of furniture edge banding, in particular to an edge banding made of organic silicon and a production method thereof. Background technique [0002] The edge banding is used to seal the section of the furniture panel, so as to protect the furniture section from the environment and unfavorable factors such as moisture in the use process, and prevent the volatilization of formaldehyde inside the panel. At the same time, it can achieve beautiful decoration It can make the furniture show the overall effect of clear wood grain and colorful colors. Now the commonly used edge banding mainly includes: log edge banding, PVC edge banding, ABS edge banding and melamine edge banding, among which the log edge banding is made of the log bark of the tree, which has the characteristics of natural and non-chemical pollution. However, the demand for tree resources is large and the cost is high; PVC edge banding is made of poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L51/04C08L83/04C08L83/07C08L23/08C08L67/04C08K13/04C08K3/22C08K7/26C08K3/34C08K5/134C08K7/06C08K5/053
CPCC08K2003/222C08K2003/2241C08K2003/2244C08K2201/011C08L51/04C08L55/02C08L2201/04C08L2201/08C08L2205/035C08L83/04C08L23/0853C08L67/04C08K13/04C08K3/22C08K7/26C08K3/34C08K5/1345C08K7/06C08K5/053
Inventor 赵亚琼
Owner ZHEJIANG WELLSCOM PLASTIC CO LTD