Dyeing and finishing processing method of single-guide wet-warm hollow cotton yarn-dyed fabric
A technology of one-way moisture guide and processing method, which is applied in the direction of fabric surface trimming, fiber type, textile and papermaking, etc., which can solve the problems of poor moisture conduction affecting wearing comfort, etc., and achieve excellent heat preservation effect and improve the effect of heat preservation effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] A dyeing and finishing method for a unidirectional moisture-conducting and warm-keeping hollow cotton yarn-dyed fabric includes the following steps: dyeing → warping → sizing → weaving → finishing. The dyeing process also includes: loose tube → rotten polyester → reverse loosening The finishing process includes: singeing→loose desizing→loose drying→setting tentering→front scraping water-repellent agent→baking→padding moisture absorption quick-drying finishing agent.
[0017] The rotten polyester process is to rotten the core polyester under high temperature, high pressure and strong alkaline conditions. The specific process conditions are temperature of 110°C, pressure of 2Mpa, time of 40min, and alkali concentration of 15g / L.
[0018] The mass of the bobbin in the anti-loosening process is 0.6kg.
[0019] In the dyeing process, salt and alkali are added at low temperature three times.
[0020] In the singeing process, natural gas is used as the heat source, a...
Example Embodiment
[0024] Example 2
[0025] The dyeing and finishing method of the unidirectional moisture-conducting and warm-keeping hollow cotton yarn-dyed fabric of this embodiment is the same as that of embodiment 1, and the difference lies in:
[0026] The decay process is to rot the core polyester under high temperature, high pressure and strong alkaline conditions. The specific process conditions are temperature of 120°C, pressure of 1.5Mpa, time of 60min, and alkali concentration of 35g / L.
[0027] The mass of the bobbin in the anti-loosening process is 0.8kg.
[0028] In the dyeing process, salt and alkali are added 5 times at low temperature.
[0029] In the singeing process, natural gas is used as the heat source, and the front and back sides of the cloth are burnt twice with the burner. The burner temperature is 1100°C and the cloth speed is 130m / min.
[0030] In the loose desizing process, first wash with amylase solution, the amount of amylase is 10g / L, the temperature is 60℃, the time is 4...
Example Embodiment
[0033] Example 3
[0034] The dyeing and finishing method of the unidirectional moisture-conducting and warm-keeping hollow cotton yarn-dyed fabric of this embodiment is the same as that of embodiment 1, and the difference lies in:
[0035] The decay process is to rot the core polyester under high temperature, high pressure and strong alkaline conditions. The specific process conditions are temperature of 115°C, pressure of 3Mpa, time of 50min, and alkali concentration of 25g / L.
[0036] The mass of the bobbin in the anti-loosening process is 0.7kg.
[0037] In the dyeing process, salt and alkali are added at low temperature four times.
[0038] In the singeing process, natural gas is used as the heat source, and the front and back sides of the cloth are burnt twice with the burner. The burner temperature is 1000°C and the cloth speed is 120m / min.
[0039] In the loose desizing process, first wash with amylase solution, the amylase dosage is 7.5g / L, the temperature is 55℃, the time is 30...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap