Firing method for Southern Song Ge-kiln opacified ink pattern glaze

A Ge kiln and biscuit firing technology, which is applied in the field of opaque ink-patterned glaze preparation of Ge kiln in the Southern Song Dynasty, can solve the problems of dull color, complicated process, poor texture, etc., and achieve the effect of good visual sense and good color

Inactive Publication Date: 2019-01-04
吴俊
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the traditional Southern Song Ge Kiln opacity ink pattern glaze preparation method has been lost, and the Southern Song Ge Kiln opacity ink pattern glaze produced by modern technology is dull in color, poor in texture, and more complicated in technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0028] As a preferred embodiment of the present invention, the manufacturing process steps are as follows:

[0029] a. Put 62.7 parts by mass of quartz, 12.2 parts by mass of alumina, 5.3 parts by mass of potassium feldspar, 1.2 parts by mass of albite, 0.2 parts by mass of talc, 0.8 parts by mass of iron and 10.2 parts by mass of limestone into the crusher respectively Carry out crushing treatment, screen the crushed particles through a sieve with a mesh number of 180-200, and crush and screen the large particles that have not been screened;

[0030] b. Mix the above-mentioned screened particles according to the preliminary raw material ratio, and at the same time stir slowly during the mixing process, so that the raw materials are evenly mixed;

[0031] c. Bisque firing the uniformly mixed raw materials;

[0032] d. putting the raw materials after bisque firing into a ball mill for grinding, and screening the raw materials after ball milling through a sieve with a mesh numb...

Embodiment 2

[0037] As a preferred embodiment of the present invention, the manufacturing process steps are as follows:

[0038] S1. Get the original semi-finished vessel after bisque firing and the glaze water obtained in step e, and use the dipping method to glaze the semi-finished vessel;

[0039] S2. Carry out glaze repair operation to the semi-finished vessel in step f by the glaze spraying method, so that the glaze water on the surface of the semi-finished vessel is evenly distributed;

[0040] S3. Place the glazed semi-finished vessel in a ventilated place for air drying, and the air drying time is 24 hours;

[0041] S4. Put the air-dried semi-finished product into the kiln and start firing. Use an oxidizing flame to fire. First, quickly increase the temperature to 900 degrees Celsius, keep the temperature for 2 hours, and then raise the temperature to 1180 degrees Celsius. It is controlled to increase by about 1 degree Celsius per minute, and after the temperature is raised to 118...

Embodiment 3

[0044] As a preferred embodiment of the present invention, the raw materials in d that have not passed through the mesh sieve are selected, and are repeatedly ground through a ball mill, and the selected ball mill is specifically an ultra-fine lamination mill.

[0045] In this embodiment, the raw materials that have not passed the mesh sieve are polished many times to avoid waste, and at the same time, the mixing ratio of raw materials will not be affected. Secondly, the more fully the grinding is, the more thorough the subsequent mixing will be, and the glaze water produced will be purer and more colorful. Also more gorgeous.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a firing method for Southern Song Ge-kiln opacified ink pattern glaze. The Southern Song Ge-kiln opacified ink pattern glaze is prepared from, by mass, 62.7 parts of quartz, 12.2 parts of aluminum oxide, 5.3 parts of potash feldspar, 1.2 parts of albite, 0.2 part of soapstone, 0.8 part of iron and 10.2 parts of limestone. Raw materials in the method are smashed, subjected tobiscuit firing and ground again, so that the raw materials are finer after being mixed; the texture of the glaze obtained after the raw materials are mixed is opacified, rich but matt, and the glazehas butter texture, the crackled glaze has the patterns stacked in a plum blossom cloud pattern shape, the visual effect is good, and moreover, through cooperation of a modern glazing technology, after a vessel is glazed, the color is very good.

Description

technical field [0001] The invention relates to the technical field of preparation of opaque ink pattern glaze of Ge kiln in Southern Song Dynasty, in particular to a firing method for opacified ink pattern glaze of Ge kiln in Southern Song Dynasty. Background technique [0002] "Ge Kiln" was listed among the five famous kilns in the Song Dynasty and played a pivotal role in the history of ceramics. Ge kiln tires are mostly purple black, iron black, and also yellowish brown. The glaze is a devitrified opaque glaze, with a layer of crisp light on the glaze surface. The glaze color is mostly fried beige and grayish green, and the glaze surface is combined with large and small patterns. [0003] The enamel of Ge kiln is pure and thick, not very clear, and there are many air bubbles in the glaze, which appear like beads, so it is commonly called "polyfoam and pearls". It is called eel pattern, black blue pattern, light yellow pattern, roe pattern, and it is called outline patt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C03C2204/04C03C2205/02C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 吴俊
Owner 吴俊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com