A kind of production method of silk composite fabric

A composite fabric and silk technology, applied in the direction of enzyme/microorganism biochemical treatment, biochemical fiber treatment, improved hand-feeling fiber, etc., can solve the problems of uneven soaking of fabrics and insufficient other properties of fabrics, and achieve the improvement of applicable value and excellence. The effect of wrinkle resistance and high elongation

Active Publication Date: 2021-12-10
吴江市金帆纺织有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing silk fabrics still have room for improvement in terms of moisture absorption, breathability, coolness and comfort, and the other properties of the fabrics are not comprehensive enough.
Generally, during the soaking process, fabrics are prone to sticking, resulting in uneven soaking of fabrics. Therefore, it is necessary to develop a soaking device that is easy to use and has a good implementation effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production method of silk composite fabric
  • A kind of production method of silk composite fabric
  • A kind of production method of silk composite fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of silk composite fabric, its production method comprises the steps:

[0038] (1) Spinning: blending bamboo fiber and ramie fiber to make bamboo fiber-ramie fiber blended yarn, softening with acid cellulase, the acid cellulase consumption is 3% of the quality of bamboo fiber-ramie fiber blended yarn , the pH value is 4.8, the temperature is 55°C, and the treatment time is 60min;

[0039] (2) Silk production: take spandex filament as the core thread, wrap the silk on the outside of the spandex filament in a spiral shape through the wrapping process, and make silk-spandex coated filament;

[0040] (3) weaving: take the bamboo fiber-ramie fiber blended yarn processed in the step (1) as the weft, and the silk-spandex covered silk made in the step (2) as the warp, weave to obtain the composite gray silk;

[0041] (4) Refining: immerse the composite gray silk obtained in step (3) into a soaking device equipped with a mixed solution of soap and sodium carbonate, heat, ...

Embodiment 2

[0051] A kind of silk composite fabric, its production method comprises the steps:

[0052] (1) Spinning: blending bamboo fiber and ramie fiber to make bamboo fiber-ramie fiber blended yarn, carry out softening treatment with acid cellulase, and the acid cellulase consumption is 2.5% of the quality of bamboo fiber-ramie fiber blended yarn , the pH value is 4.8, the temperature is 53°C, and the treatment time is 55min;

[0053] (2) Silk production: take spandex filament as the core thread, wrap the silk on the outside of the spandex filament in a spiral shape through the wrapping process, and make silk-spandex coated filament;

[0054] (3) weaving: take the bamboo fiber-ramie fiber blended yarn processed in the step (1) as the weft, and the silk-spandex covered silk made in the step (2) as the warp, weave to obtain the composite gray silk;

[0055] (4) Refining: immerse the composite gray silk obtained in step (3) into a soaking device equipped with a mixed solution of soap an...

Embodiment 3

[0063] A kind of silk composite fabric, its production method comprises the steps:

[0064] (1) Spinning: blending bamboo fiber and ramie fiber to make bamboo fiber-ramie fiber blended yarn, softening treatment with acid cellulase, the acid cellulase consumption is 2% of the quality of bamboo fiber-ramie fiber blended yarn , the pH value is 4.8, the temperature is 50°C, and the treatment time is 50min;

[0065] (2) Silk production: take spandex filament as the core thread, wrap the silk on the outside of the spandex filament in a spiral shape through the wrapping process, and make silk-spandex coated filament;

[0066] (3) weaving: take the bamboo fiber-ramie fiber blended yarn processed in the step (1) as the weft, and the silk-spandex covered silk made in the step (2) as the warp, weave to obtain the composite gray silk;

[0067] (4) Refining: immerse the composite gray silk obtained in step (3) into a soaking device equipped with a mixed solution of soap and sodium carbona...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a silk composite fabric, which belongs to the technical field of fabric production technology, and comprises the following steps: firstly blending bamboo fiber and ramie fiber to make a mixed yarn, and performing softening treatment; wrapping silk and spandex filament to produce Silk-spandex covered silk; then the mixed yarn is used as the weft, and the silk-spandex covered silk is used as the warp to weave composite gray silk; then the composite gray silk is removed by refining process; soaked after washing, menthol molecules are introduced; Finally, through reprocessing such as dyeing, the silk composite fabric is obtained. The silk composite fabric prepared by the invention has excellent characteristics in terms of moisture absorption, breathability, coolness and comfort, and is especially suitable for use as a summer fabric; at the same time, the fabric has good mold resistance, elasticity, elastic recovery and wrinkle resistance , making the fabric performance more comprehensive. In addition, the soaking device adopted in the method has a simple and flexible structure, is easy to apply, and has a good implementation effect.

Description

technical field [0001] The invention relates to the technical field of production technology of fabrics, in particular to a production method of silk composite fabrics. Background technique [0002] In recent years, with the development of science and technology and the improvement of people's living standards, people have higher requirements for the functionality, comfort, health, environmental protection and health care of clothing fabrics. When the weather is hot, the breathable and cool properties of clothing fabrics have become the first choice for people to buy clothing. Silk fabric has a strong sense of comfort and good moisture absorption and release properties. The main raw material for silk weaving is silk, which is a natural animal protein fiber with a soft and smooth texture and a delicate touch, often giving people a soft, delicate and elegant feeling. Wearing silk clothing in summer can dissipate sweat and heat quickly, and has strong air permeability, making...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M16/00D06M15/643D06M11/76D06M13/144D02G3/04D03D15/217D03D15/283D03D15/47D03D15/56D03D15/50D06M101/06D06M101/10D06M101/38D03D15/233D03D15/58
CPCD02G3/042D06M11/76D06M13/144D06M15/643D06M16/003D10B2331/10D10B2201/08D10B2201/10D10B2211/04D06M2101/38D06M2200/50D06M2101/06D06M2101/10D03D15/47D03D15/56
Inventor 杨正荣钱飞王国和
Owner 吴江市金帆纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com