Battery diaphragm and preparation method thereof

A battery separator and electrolyte technology, applied in battery pack parts, circuits, electrical components, etc., can solve the problems of reducing battery energy density, poor tensile mechanical properties, uneven current density distribution, etc., to improve energy density, The effect of high mechanical strength and small pore size

Inactive Publication Date: 2019-03-26
GUANGDONG UNIV OF TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of the former type of diaphragm is that there is a stretching pore-forming/pore-enlarging process in the process of preparing polyolefin microporous diaphragms by dry method or wet method, and the diaphragm will undergo serious heat loss at higher temperatures (>130°C). Shrinkage (especially in the direction of stretching), which will lead to a short circuit of the positive and negative areas of the battery, which will cause thermal runaway and safety accidents
And the choice of polymer substrates for this type of diaphragm is very narrow. At present, the substrates of commercial diaphragms are mainly polyethylene (PE) and polypropylene (PP).
The disadvantage of the latter type of separator is that whether it is made of paper or electrospinning, the porous membrane is made of random arrangement, interweaving and adhesion of micro/nano fibers. The thermal shrinkage of the film has disadvantages, but it also brings many new problems: On the o

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Battery diaphragm and preparation method thereof
  • Battery diaphragm and preparation method thereof
  • Battery diaphragm and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0065] Example 1

[0066] This embodiment provides the first battery separator, and the specific preparation method is as follows:

[0067] 1. Dry polyvinylidene fluoride (PVDF) at 80℃ for 10 hours in a vacuum environment, and then dissolve PVDF powder in N-methylpyrrolidone (NMP) solution to obtain a transparent, uniform and stable PVDF / NMP The battery separator spinning solution, wherein the solid content of the battery separator spinning solution is 21 wt%.

[0068] 2. The prepared PVDF / NMP battery diaphragm spinning solution is made into PVDF battery diaphragm fiber filaments by electrostatic spinning. The injection needle adopts 12# (the inner diameter of the needle is 1.2mm), the spinning voltage is 13.5KV, the advance speed of the metering pump is 0.065mm / min, the distance between the syringe needle and the take-up plate is 20cm, the spinning time is 0.5h, and the spinning temperature It is 25°C. The air humidity is 45%, the carbon paper is bent and spread on the receiving ...

Example Embodiment

[0070] Example 2

[0071] This embodiment provides a second battery separator, and the specific preparation method is as follows:

[0072] 1. Polyetherimide (PEI) is dried at 80°C for 6 hours in a vacuum environment, and then the PEI particles are dissolved in N-methylpyrrolidone (NMP) solution at 90°C to obtain a transparent, uniform and stable The PEI battery diaphragm spinning solution, wherein the solid content of the PEI battery diaphragm spinning solution is 25 wt%.

[0073] 2. The prepared transparent PEI battery diaphragm spinning solution is made into PEI battery diaphragm fiber filaments by the electrostatic spinning method. The injection needle adopts 12# (the inner diameter of the needle is 1.2mm), the spinning voltage is 14KV, the advancing speed of the metering pump is 0.05mm / min, the distance between the syringe needle and the take-up plate is 20cm, the spinning time is 0.5h, and the spinning temperature is 25°C. The air humidity is 45%, the carbon paper is bent and...

Example Embodiment

[0075] Example 3

[0076] This embodiment provides a third battery separator, and the specific preparation method is as follows:

[0077] 1. Polypropylene (PP) is dried at 80°C for 6 hours in a vacuum environment, and then PP particles are dissolved in N-methylpyrrolidone (NMP) solution at 90°C to obtain a transparent, uniform and stable PP battery The diaphragm spinning solution, wherein the solid content of the PEI battery diaphragm spinning solution is 25 wt%.

[0078] 2. The prepared transparent PP battery diaphragm spinning solution is made into PP battery diaphragm fiber yarn by electrostatic spinning method. The injection needle adopts 12# (the inner diameter of the needle is 1.2mm), the spinning voltage is 14KV, the advancing speed of the metering pump is 0.055mm / min, the distance between the syringe needle and the take-up plate is 20cm, the spinning time is 0.5h, and the spinning temperature is 25°C. The air humidity is 45%, the carbon paper is bent and spread on the rece...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of lithium ion batteries and particularly relates to a battery diaphragm and a preparation method thereof. The preparation method of the battery diaphragmcomprises the steps of putting battery diaphragm fiber filaments into a textile machine, and weaving by virtue of the textile machine, so as to obtain the battery diaphragm, wherein the battery diaphragm fiber filaments are electronically insulated battery diaphragm fiber filaments which do not react with electrolyte, and the diameters of the battery diaphragm fiber filaments are 5-40 microns. Theinvention aims at providing the battery diaphragm with uniform small pore diameter and high porosity, so that dendritic crystals are produced in the charging and discharging processes of the battery,and the cycle performance of the battery is improved.

Description

technical field [0001] The invention belongs to the technical field of batteries, and in particular relates to a battery diaphragm and a preparation method thereof. Background technique [0002] At present, there are two main types of methods for preparing lithium-ion battery separators: one is polyolefin microporous membranes prepared by melting heat stretching (dry method) or thermally induced phase separation (wet method); the other is using papermaking Or a non-woven separator prepared by an electrospinning process. The disadvantage of the former type of diaphragm is that there is a stretching pore-forming / pore-enlarging process in the process of preparing polyolefin microporous diaphragms by dry method or wet method, and the diaphragm will undergo serious heat loss at higher temperatures (>130°C). Shrinkage (especially in the direction of stretching), which will lead to a short circuit with a large area of ​​the positive and negative sides of the battery, causing th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M2/14H01M2/16H01M50/403H01M50/411H01M50/44H01M50/491
CPCH01M50/403H01M50/411H01M50/44Y02E60/10
Inventor 刘全兵李俊豪张圣洁党岱方岩雄
Owner GUANGDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap