A kind of conductive silver paste and its preparation method and application

A technology of conductive silver paste and silver paste, which is applied in the field of solar cells, can solve the problems of difficult control, reduce the corrosion of the sintering process, and the adverse effects of bonding tension, and achieve high photoelectric conversion efficiency, good welding tension and aging performance, good adhesion effect

Active Publication Date: 2020-09-15
SUZHOU ISILVER MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, by formulating a new system of glass powder, reducing the amount of glass powder used, reducing the corrosion during the sintering process, thereby reducing the damage to the passivation layer on the surface of the solar cell, it is difficult to control, and the reduction in the use of glass powder will reduce the It will have an adverse effect on the bonding tension of the silver paste after sintering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of conductive silver paste and its preparation method and application
  • A kind of conductive silver paste and its preparation method and application
  • A kind of conductive silver paste and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0066] This embodiment provides a conductive silver paste, which is prepared through the following steps.

[0067] Preparation of glass powder composition: raw materials are mixed (45 parts of bismuth oxide, 18 parts of silicon oxide, 20 parts of aluminum oxide, 15 parts of boron oxide, 2 parts of sodium oxide, potassium oxide, magnesium oxide, barium oxide, zinc oxide), and then Perform melting, quenching, grinding, and water washing processes to obtain a glass powder composition;

[0068] Prepare organic vehicle: mix solvent (75 parts of butyl carbitol acetate), cellulose resin (10 parts of ethyl cellulose), additives (4 parts of oleic acid, 3 parts of polypropylene glycol, 8 parts of polyamide wax), get an organic carrier;

[0069] Prepare conductive silver paste, mix silver powder, glass powder, organic vehicle and organosilicon compound,

[0070] Or, after mixing with the raw materials of the organic carrier when preparing the organic carrier, then mix with other raw ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
tensile loadaaaaaaaaaa
Login to View More

Abstract

The invention provides a conductive silver paste and a preparation method and an application thereof. The raw materials of the conductive silver paste include a conductive silver paste base material and an organic silicon compound. There are 0.1-5 parts of the organic silicon compound by weight, and the total mass of the conductive silver paste is 100 parts. The organic silicon compound is used toform a silicon oxide protective layer. The conductive silver paste of the invention can be used to prepare a back electrode and a main gate electrode. The conductive silver paste can improve the bonding strength of a silicon substrate without destroying the passive film of a battery pole piece.

Description

technical field [0001] The invention relates to a conductive silver paste, in particular to a conductive silver paste used for back electrodes and main grid electrodes, and belongs to the technical field of solar cells. Background technique [0002] The biggest difference between Passivated Emitter and Rear Surface Passivated Cells (PERC) and ordinary silicon solar cells is that the back surface is protected by thin layers such as aluminum oxide and silicon nitride, and the back silver electrode and the back aluminum back field are no longer directly connected with the solar cell. The contact of the silicon solar cell reduces the surface recombination rate, increases the open circuit voltage of the silicon solar cell, and finally improves the efficiency of the silicon solar cell. [0003] Due to the addition of a passivation layer on the back of the cell, the direct contact area between the silver electrode on the back and the silicon cell is greatly reduced, which will lead...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B1/22H01L31/0224H01B13/00
CPCH01B1/22H01B13/00H01L31/022425
Inventor 陈东锋包娜孙达汪山周欣山
Owner SUZHOU ISILVER MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com