Sintering method suitable for thin-walled output window ceramics

A sintering method and output window technology, applied in the field of ceramics, can solve problems such as non-compliance with product requirements

Inactive Publication Date: 2019-04-19
CHANGSHU CITY YINYANG CERAMIC CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For ceramics whose height is twice the diameter and whose wall thickness is only 1mm, using the traditional sintering process, the out-of-roundness of the product is greater than 0.3mm, and the upper and lower tapers are greater than 0.5mm, which does not meet the requirements of the product. Therefore, it is necessary to improve the sintering process , to improve the roundness and taper of the ceramics, so as to meet the product requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sintering method suitable for thin-walled output window ceramics
  • Sintering method suitable for thin-walled output window ceramics
  • Sintering method suitable for thin-walled output window ceramics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The technical solutions in the embodiments of the present invention will be described clearly and completely below. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0020] See Figure 1-3 , The embodiment of the present invention includes:

[0021] A sintering method suitable for output window ceramics of thin-walled parts includes the following steps:

[0022] a. Place gasket 2 on the setter plate 1;

[0023] b. Place ceramic product 3 on gasket 2;

[0024] c. Place gasket 2 on top of ceramic product 3;

[0025] d. Push the setter plate 1, and push the ceramic product 3 with gaskets 2 on the top and bottom into the high-temperature sintering furnace, and dry it into a mechanical hydraulic pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Circularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sintering method suitable for thin-walled output window ceramics. The method includes the following steps: a, placing one pad on a load bearing board; b, placing a ceramic product on the pad; c, placing one pad on the top of the ceramic product; and d, pushing the load bearing board, pushing the ceramic product with the pads on both the top and bottom into a high temperature sintering furnace, and performing dry pressing through a mechanical oil press. Through the above modes, the roundness of the product sintered through the method is less than or equal to 0.1 mm, the upper and lower tapers are less than or equal to 0.1 mm, and therefore, the method can accord with product requirements.

Description

Technical field [0001] The invention relates to the field of ceramics, in particular to a sintering method suitable for output window ceramics of thin-walled parts. Background technique [0002] For ceramics whose height is twice the diameter and the wall thickness is only 1mm, the traditional sintering process is adopted, and the roundness of the product is greater than 0.3mm, and the upper and lower taper is greater than 0.5mm, which does not meet the requirements of the product. Therefore, the sintering process needs to be improved. , In order to improve the roundness and taper of the ceramics, so as to meet the product requirements. Summary of the invention [0003] The main technical problem solved by the present invention is to provide a sintering method suitable for the output window ceramics of thin-walled parts. The roundness of the sintered product is less than or equal to 0.1mm, and the upper and lower taper is less than or equal to 0.1mm, which meets the product requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/64
CPCC04B35/64
Inventor 王和化高沛君
Owner CHANGSHU CITY YINYANG CERAMIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap