Novel high-temperature-resistant cold mounting material

A new type of cold inlay technology, applied in the field of cold inlay of metallographic samples, can solve the problems of low deformation temperature and achieve the effect of high hardness and high strength

Inactive Publication Date: 2019-05-10
HARBIN UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And it has the characteristics of excellent chemical stability and dimensional stability, but the disadvantage is that the deformation temperature is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0018] It comprises the following components in terms of parts by mass: 8 parts of tray powder, 15 parts of aluminate cement, and 7 parts of tray water.

Embodiment approach 2

[0020] It comprises the following components in terms of parts by mass: 8 parts of tray powder, 14 parts of aluminate cement, and 7 parts of tray water.

Embodiment approach 3

[0022] The following components are included in parts by mass: 7 parts of tray powder, 13 parts of aluminate cement, and 7 parts of tray water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an ingredient designing and preparing method of a novel cold mounting material, in particular to a novel cold mounting material for metallographic specimen mounting. The coldmounting material is composed of, by mass, 5-8 parts of dental base acrylic resin liquid, 7-9 parts of dental base acrylic resin powder and 6-15 parts of aluminate cement. The preparation method includes: sufficiently mixing the dental base acrylic resin powder and the aluminate cement, and adding the dental base acrylic resin liquid. The cold mounting material prepared by the method is quick in curing, good in forming effect, high in hardness, wear resistance and deformation temperature and free of deformation after being formed below 200 DEG C.

Description

technical field [0001] The invention relates to the field of cold mounting materials for metallographic samples, and has the characteristics of high deformation resistance at high temperature and convenient operation. Background technique [0002] The invention aims to solve the problems that the deformation temperature of the current cold mounting material is low, and the samples well mounted by the cold mounting material cannot be heated at high temperature and high temperature mechanical property experiments cannot be performed. [0003] Inlaid metallographic sample preparation has the functions of sample fixation, sample support, and standardized samples. The inlaid samples need to continue to be subjected to high-temperature aging or mechanical performance experiments at high temperatures. Therefore, there are certain high temperature resistance requirements for the mosaic material. [0004] Cold mounting material is a mounting material for embedding samples at room te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06
Inventor 孙凤莲韩帮耀庞树帅刘洋
Owner HARBIN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com