Self-lubricating hydrophilic aluminum foil and preparation method thereof
A hydrophilic aluminum foil, self-lubricating technology, applied in the direction of pretreatment surface, coating, device for coating liquid on the surface, etc., can solve the problem of inability to adapt to different types of molds, shorten the service life of abrasive tools, poor versatility and adaptability and other problems, to achieve good economic and social benefits, reduce friction, and improve service life.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0068] Example 1 A self-lubricating hydrophilic aluminum foil
[0069] 1. Production method
[0070] 1) Aluminum foil: use 0.083*627 mm aluminum foil.
[0071] 2) Degreasing: Use the comprehensive cleaning method of immersion degreasing + spraying type to prepare degreasing liquid with Huigu liquid degreasing agent; the total alkali concentration in the degreasing liquid is maintained at 0.042mol / L; the temperature of the degreasing liquid is 58°C.
[0072] 3) Hot water cleaning: first immersion cleaning, add pure water with EC=1~10us / cm to the tank solution, and then use pure water spray cleaning with EC=1~10us / cm, the temperature of the hot water tank is 56℃, the tank solution pH value 8.
[0073] 4) Cold water cleaning: Pure water spray cleaning with EC=1~10us / cm, pH value of bath 6.8.
[0074] 5) Pure water cleaning: pure water spray cleaning with EC=3.5us / cm.
[0075] 6) Drying: time 2.4 seconds; temperature 320℃.
[0076] 7) Undercoat coating: use 304 stainless steel roller as coati...
Example Embodiment
[0085] Example 2 A self-lubricating hydrophilic aluminum foil
[0086] 1. Production method
[0087] 1) Aluminum foil: use 0.083*627mm aluminum foil.
[0088] 2) Degreasing: Use the comprehensive cleaning method of immersion degreasing + spraying type, using Huigu liquid degreasing agent; the total alkali concentration in the degreasing solution is maintained at 0.040mol / L; the temperature of the degreasing solution is 58°C.
[0089] 3) Hot water cleaning: first immersion cleaning, adding pure water with EC=1~10us / cm to the bath, and then spray cleaning with pure water with EC=1~10us / cm, bath temperature 55℃; The pH value is 7.8.
[0090] 4) Cold water cleaning: pure water spray cleaning with EC=1~10us / cm, pH value of bath is 7.0.
[0091] 5) Pure water cleaning: pure water spray cleaning with EC=4.1us / cm.
[0092] 6) Drying: time 2.5 seconds; temperature 321℃.
[0093] 7) Undercoat coating: use 304 stainless steel roller as coating roller, use PU60 polyurethane rubber roller as tape roll...
Example Embodiment
[0102] Example 3 A self-lubricating hydrophilic aluminum foil
[0103] 1. Production method
[0104] 1) Aluminum foil: use 0.083*746mm aluminum foil.
[0105] 2) Degreasing: Use the comprehensive cleaning method of immersion degreasing + spraying type, and use Huigu liquid degreasing agent to prepare degreasing liquid; the total alkali concentration in the degreasing liquid is maintained at 0.052mol / L; the temperature of the degreasing liquid is 60℃.
[0106] 3) Hot water cleaning: first immersion cleaning, add pure water with EC=1~10us / cm to the bath, and then spray cleaning with pure water with EC=1~10us / cm, bath temperature is 54℃; The pH value is 8.0.
[0107] 4) Cold water cleaning: Pure water spray cleaning with EC=1~10us / cm, pH value of bath 6.8.
[0108] 5) Pure water cleaning: pure water spray cleaning with EC=3.6us / cm.
[0109] 6) Drying: time 2.18 seconds; temperature 320℃.
[0110] 7) Undercoat coating: use 304 stainless steel roller as coating roller, use PU60 polyurethane ru...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap