Highly adhesive eye makeup composition
A cosmetic composition, high adhesion technology, applied in the direction of cosmetics, cosmetics, cosmetic preparations, etc., can solve the problems of impossibility of pushing, rough surface of application, etc., and achieve the effect of improving the surface, excellent smoothness, and excellent adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1-3 and comparative example 1-3
[0045] The composition and content of the eye cosmetic composition are shown in Table 1 below. Mascara formulations were prepared according to the following preparation methods. In Table 1 below, the film-forming agent used is the styrene / ammonium / methacrylate of Interpolymer's Syntran series (5009, 5760).
[0046] 【Table 1】
[0047]
[0048]
[0049] 1) Components 1-6 were heated at 80°C to dissolve them.
[0050] 2) Components 7-12 were heated at 80°C and stirred.
[0051] 3) Slowly add the 2) into the 1) and emulsify.
[0052] 4) Add ingredients 13-15 and stir, and cool to 35°C.
[0053] 5) Fill it into a mascara container.
experiment Embodiment 1
[0054] smoothness, adhesion test (sensory evaluation)
[0055] Aiming at 35 women aged 20 to 35 who use mascara daily or frequently as objects, let them actually use the mascara products of Comparative Examples 1 to 3 prepared by conventional methods and the mascara products of Examples 1 to 3 prepared by the method of the present invention. 3 mascara products to compare the effect of the products. After scoring the smoothness and adhesion of each product as a comparison item, a score of 0-10 was evaluated. Repeat the test five times to ensure the accuracy of the data. After the average score is obtained, the results are shown in Table 2 below. In Table 2, an average score of 4.0 or less is represented as "×", 5-6 is represented as "△", 7-8 is represented as "○", and 9 or above is represented as "◎".
[0056] 【Table 2】
[0057] Test items
[0058] According to the above experimental results, it can be determined that with the increase of talcum powder as a flake ...
experiment Embodiment 2
[0059] Density test (sensory evaluation)
[0060] For the same sample subjects as in Experimental Example 1, evaluate the density item when applying for the first time and when applying for 5 times, and score 0-10, and the results are shown in Table 3 below. In Table 3, those with an average score of 4.0 or less are represented as "×", 5-6 as "△", 7-8 as "○", and 9 or above as "◎".
[0061] 【table 3】
[0062]
[0063]
[0064] From the above test results, it can be seen that the density of the first application is determined by the flake powder, and the density of the second application is determined by the total content of the powder.
[0065] exist figure 1 The graphs of Example 1 and Comparative 3, which are excellent in the density, are smeared in . It can be seen from this that, as shown in Comparative Example 3, when only the adhesion is excellent, there will be agglomeration between the liquids during application. On the contrary, as shown in Example 1, when b...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Average particle size | aaaaa | aaaaa |
| The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to view more - R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap