Corrosion-resistant spring steel with tensile strength of more than or equal to 2100 MPa and production method thereof
A technology with a tensile strength of 2100mpa, applied in the direction of low internal friction springs, springs/shock absorbers, mechanical equipment, etc., can solve the problems of no corrosion resistance and no significant increase in the tensile strength of spring steel, and achieve good The effect of corrosion resistance
Inactive Publication Date: 2019-06-21
MAANSHAN IRON AND STEEL COMPANY
View PDF6 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, the tensile strength of this spring steel has not been significantly improved compared with the strength of national standard 55SiCrV and other brands, and it does not have obvious corrosion resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0035] The present invention will be further described below in conjunction with embodiment. The described examples and their results are only for illustrating the invention, but should not and will not limit the invention as detailed in the claims.
[0036]Each embodiment of the present invention is all produced by the following process:
[0037] (1) Conventional electric furnace or converter smelting: Oxygen is fixed before tapping, and slag is strictly controlled during tapping;
[0038] (2) Conventional refining furnace refining: C, Si, Cr, Mn, V, Ni, Cu, Re and other elements are adjusted to the target value;
[0039] (3) Vacuum degassing: the pure degassing time is ≥15 minutes, and the [H] content after vacuum treatment is guaranteed to be ≤1.5ppm;
[0040] (4) Continuous casting: control the target temperature of molten steel in the tundish to be 10-40°C above the liquidus temperature, and continuously cast 150mm×150mm-250mm×250mm billets;
[0041] (5) Wire rod rolli...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| Strength | aaaaa | aaaaa |
| Fatigue strength | aaaaa | aaaaa |
Login to View More
Abstract
The invention belongs to the field of spring steel and production methods thereof, and particularly relates to a corrosion-resistant spring steel with tensile strength of more than or equal to 2100 MPa and a production method thereof. The corrosion-resistant spring steel comprises the following chemical components of, in percentage by weight, 0.57%-0.63% of C, 1.50%-2.00% of Si, 0.40%-0.60% of Mn,0.80%-1.00% of Cr, 0.20%-0.30% of V, 0.05%-0.15% of Ni, 0.05%-0.15% of Cu, 0.01%-0.03% of Re, about 0.015% of P trace, about 0.015% of S trace, less than or equal to 0.0015% of O, less than or equalto 0.006% of N, less than or equal to 0.00015% of [H], and the balance Fe and other inevitable impurities. The production method comprises the following steps of smelting, refining, vacuum degassing,continuous casting and wire rod rolling; after heat treatment, the tensile strength is larger than or equal to 2100 MPa, the grain size of the steel is larger than or equal to 10 grade, the percentageelongation after fracture is larger than or equal to 13%, the fracture surface shrinkage rate is larger than or equal to 45%, and the fatigue strength is larger than or equal to 850 MPa; and good corrosion resistance is achieved, and the requirement of spring manufacturing in a humid environment is met.
Description
technical field [0001] The invention belongs to the field of spring steel and a production method thereof, in particular to a corrosion-resistant spring steel with a tensile strength ≥ 2100 MPa and a production method thereof. Background technique [0002] Spring steel is widely used in the manufacture of railways, automobiles, construction machinery and other machinery. With the increasing requirements for light weight and high performance of motor vehicles, the suspension springs supporting the vehicle body are also strengthened. Furthermore, domestic trains are speeding up and trucks are developing towards high speed and heavy loads, so there is an urgent need for bogie springs with high strength, light weight and long life. In addition, in some humid environments with high concentration of chloride ions, such as coastal environments, spring parts are required to have good corrosion resistance. [0003] However, while the coil springs used in automobile suspensions have ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C22C38/46C22C38/42C22C38/02C22C38/04C21D8/06F16F1/02
Inventor 汪开忠姜婷于同仁张晓瑞孙凯龚梦强尹德福郭湛吴科成
Owner MAANSHAN IRON AND STEEL COMPANY