High-performance photovoltaic (PV) module back-side protective film containing silane coupling agent, and preparation method of protective film

A silane coupling agent, photovoltaic module technology, applied in photovoltaic power generation, electrical components, semiconductor devices, etc., can solve the problems of inability to protect photovoltaic modules, inconvenient use, damage to the protective film of photovoltaic modules, etc.

Active Publication Date: 2019-06-21
HUANGSHAN HUIZHOU TIANMA CHEM
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a high-performance protective film on the back of a photovoltaic module containing a silane coupling agent and a preparation method thereof, which solves the problem that the existing protective film on the back of a photovoltaic module has a short service life, is easy to wear, and cannot be used during use. Better protection of photovoltaic modules, due to long-term sunshine and high temperature, will damage the structure of the protective film on the back of the photovoltaic module, and the existing back protective film will produce air pockets when used, which is inconvenient to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance photovoltaic (PV) module back-side protective film containing silane coupling agent, and preparation method of protective film
  • High-performance photovoltaic (PV) module back-side protective film containing silane coupling agent, and preparation method of protective film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] S1. First confirm whether the workshop environment, raw materials, raw material pots, melt mixing machines and high and low pressure film blowing machines are clean and free of residues, and whether personal hygiene and protection facilities are all qualified;

[0032] S2, then accurately weigh the raw materials according to the weight of each formula to be selected, and affix a label to indicate the weight, name and code;

[0033] S3. Then the staff can put the natural rubber particles into the prepared raw material pot at normal temperature, start the mixer to stir at a speed of 40r / min, and keep the stirring speed constant, and then add polyolefin plastomer resin, ethylene- Vinyl acetate copolymer, polyethylene, appropriate amount of OPP, stir for 11 minutes;

[0034] S4. Afterwards, the material is discharged, and the material is put into a molten liquid stirring machine for anaerobic melting, the temperature is controlled at 400 ° C, and the stirring speed is 60 r / ...

Embodiment 2

[0039] S1. First confirm whether the workshop environment, raw materials, raw material pots, melt mixing machines and high and low pressure film blowing machines are clean and free of residues, and whether personal hygiene and protection facilities are all qualified;

[0040] S2, then accurately weigh the raw materials according to the weight of each formula to be selected, and affix a label to indicate the weight, name and code;

[0041] S3. Then the staff can put the natural rubber particles into the prepared raw material pot at normal temperature, start the mixer to stir at a speed of 40r / min, and keep the stirring speed constant, and then add polyolefin plastomer resin, ethylene- Vinyl acetate copolymer, polyethylene, appropriate amount of OPP, stir for 12 minutes;

[0042]S4. Afterwards, the material is discharged, and the material is put into a molten liquid stirring machine for anaerobic melting, the temperature is controlled at 450° C., and the stirring speed is 70 r / m...

Embodiment 3

[0047] S1. First confirm whether the workshop environment, raw materials, raw material pots, melt mixing machines and high and low pressure film blowing machines are clean and free of residues, and whether personal hygiene and protection facilities are all qualified;

[0048] S2, then accurately weigh the raw materials according to the weight of each formula to be selected, and affix a label to indicate the weight, name and code;

[0049] S3. Then the staff can put the natural rubber particles into the prepared raw material pot at normal temperature, start the mixer to stir at a speed of 40r / min, and keep the stirring speed constant, and then add polyolefin plastomer resin, ethylene- Vinyl acetate copolymer, polyethylene, appropriate amount of OPP, stir for 13 minutes;

[0050] S4. Afterwards, the material is discharged, and the material is put into a molten liquid stirring machine for anaerobic melting, the temperature is controlled at 500 ° C, and the stirring speed is 80 r / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of high-performance protective films, and discloses a high-performance photovoltaic (PV) module back-side protective film containing a silane coupling agent, and a preparation method of the protective film. The protective film comprises the following raw materials according to weight percentages: 85-95% of natural rubber, 3-5% of polyolefin plastomer resin, 5-8% of an ethylene and vinyl acetate copolymer, and 2-5% of polyethylene. The method comprises the following steps: S1, confirming whether a workshop environment, raw materials, a raw material crucible, a meltwater stirrer and a high-low voltage film blowing machine are clean or not, whether residuals are removed or not, and whether personal hygiene and protective facilities are qualified ornot; and the like. The high-performance PV module back-side protective film containing the silane coupling agent and the preparation method of the protective film have the advantages that the problems of the conventional PV module back-side protective film that the service life is short, effective protection for a PV module cannot be achieved during use because of high possibility of abrasion, PVmodule back-side protective film generation tissues are damaged under long-time sun exposure and high temperatures, and the use is inconvenient because air bubbles are generated during use can be solved.

Description

technical field [0001] The invention relates to the technical field of high-performance protective films, in particular to a high-performance protective film on the back of a photovoltaic module containing a silane coupling agent and a preparation method thereof. Background technique [0002] According to the application, the protective film can be divided into digital product protective film, car protective film, household protective film, food fresh-keeping protective film and so on. With the popularity of digital products such as mobile phones in China, protective film has gradually become a general term for screen protective films, and its functions in the field of screen protective films are also varied. The material has experienced more than 5 years of development from the earliest PP material to the current popular AR material, and has gradually been accepted by the majority of mobile phone groups. Functionally speaking, the protective film is to put a film on the ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L31/048H01L31/049C08L7/00C08L23/06C08L23/08C08J5/18B29C55/28B29L23/00
CPCY02E10/50
Inventor 汪惠琴马万升谢桂枝代荣程鹏飞
Owner HUANGSHAN HUIZHOU TIANMA CHEM