A surface treatment composition containing fluorinated polyether siloxane

A fluorinated polyether siloxane and surface treatment technology, applied in the field of surface treatment and surface treatment composition, to achieve the effects of good smoothness, excellent wear resistance and excellent antifouling performance

Active Publication Date: 2021-06-04
QUZHOU FLUORIDE & SILICON RES INST
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing fluorinated siloxanes basically have to be cured at a high temperature above 120°C to meet the requirements of high wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A surface treatment composition containing fluorinated polyether siloxane
  • A surface treatment composition containing fluorinated polyether siloxane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Dissolve 90 parts by mass of fluorinated polyether siloxane A) and 10 parts by mass of aminosiloxane compound H into hydrofluoroether solvent 347, and prepare a test solution with a concentration of 1 wt‰.

[0058] The configuration methods of Examples 2-10 and Comparative Examples 1-6 are the same as that of Example 1, and the specific ratio of active ingredients is shown in Table 1.

[0059] Table 1: Active ingredient distribution ratio (all are mass parts in the table)

[0060] Example A B C D E F G H 1 90 10 2 70 30 3 99.9 0.01 4 85 15 5 85 15 6 85 15 7 68 17 15 8 68 17 15 9 55.25 29.75 15 10 68 17 15 5 comparative example 1 100 2 50 50 3 68 32 4 68 16 16 5 54.5 30.5 15 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a surface treatment composition containing fluorinated polyether siloxane. The composition comprises: (1) 70-99.99 parts by mass of fluorinated polyether siloxane, the fluorinated polyether siloxane can be Represented by general formulas (A) and (B): (R f ) α ‑M‑(S) β (A) (S) β ‑M‑(R f )‑M‑(S) β (B) where R f It is a monovalent or divalent polyfluoropolyether group, M is a covalent bond or at least a bivalent organic linking group, S is a silane group containing a hydroxyl group or a hydrolyzable group, and α and β are both 1 to 10. Integer, and α+β≤10; and fluorinated polyether siloxane represented by formula (B) in fluorinated polyether siloxane accounts for at most 35% of the total mass of fluorinated polyether siloxane; (2) 0.01~ 30 parts by mass of a silane compound containing both amino and hydroxyl groups or hydrolyzable groups. The antifouling coating prepared from the composition of the invention has excellent antifouling performance, excellent wear resistance, can be cured at room temperature, has good smoothness and has excellent hand feeling.

Description

technical field [0001] The invention relates to a surface treatment composition, in particular to a surface treatment composition containing fluorinated polyether siloxane, which belongs to the technical category of surface treatment. Background technique [0002] The transparent optical devices of touch-type electronic display devices (such as mobile phone glass screens, etc.) are often in contact with fingers, and are easily polluted by fingerprints, sweat, oil, etc., and once the dirt is formed, it is difficult to remove without using solvents. There is a danger of damaging the display device; on the other hand, dirt also affects the visual perception of the display device. In order to prevent contamination of display devices by dirt and possible damage to devices during the removal of dirt, it is of great significance to develop surface coatings with antifouling and easy decontamination functions. [0003] In order to achieve the above objectives, researchers have devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/12C09D5/16C09D7/63
CPCC08L2205/025C08L2205/03C09D5/1675C09D5/1687C09D183/12C08L83/12C08L71/02C08K5/544
Inventor 裴金东李建郦聪田小平郑欣
Owner QUZHOU FLUORIDE & SILICON RES INST