High-performance wear-resistant glaze and preparation method thereof

A high-performance, glazed technology, applied in the field of architectural ceramics, can solve the problems of glazed tiles that are easy to be scratched, the surface is dull, and the wear resistance is difficult to meet, so as to achieve less pores on the glazed surface, efficiently match the production system, and improve The effect of wear resistance

Active Publication Date: 2020-01-14
FOSHAN DONGPENG CERAMIC +2
View PDF9 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When using glazed tiles as floor decoration materials, there are high requirements for the wear resistance of glazes. Glazed tiles prepared from glazes with low wear resistance are easy to be scratched, and products with poor wear resistance can be used for a long time. After a long time, the gloss will decrease obviously, and the surface will be dull, which will seriously affect the appearance
At present, the surface hardness of polished glaze products on the market is below Mohs hardness 4, and the wear resistance level is generally at level 3 at 750 rpm. The wear resistance is difficult to meet the requirements of consumers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance wear-resistant glaze and preparation method thereof
  • High-performance wear-resistant glaze and preparation method thereof
  • High-performance wear-resistant glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-8

[0040] A kind of wear-resisting glazed tile, prepared according to the following steps:

[0041] (1) According to the weight percentage, the frit powder is prepared according to the mineral composition of the frit powder in Table 2. After the melting temperature is 1520° C. for 30 minutes, the discharge water is cooled to form a frit, and the prepared frit is powdered and sieved, Dry and get the 100 mesh sieve for subsequent use;

[0042] (2) According to the percentage by weight, according to the raw material composition of the high-performance wear-resistant glaze in Table 1, and the mineral composition of the raw glaze powder in Table 2, take by weighing for subsequent use;

[0043] (3) Add the above raw materials to water ball mill for 9 hours to obtain a glaze slurry, control the fineness of 325 mesh to 1.2% mass fraction, and then stale for 49 hours to obtain a high-performance wear-resistant glaze.

[0044] (4) Replace the surface glaze in the existing production proce...

Embodiment 9

[0069] (1) Preparation of frit powder: by weight percentage, get kaolin 48%, calcined talc 28%, quartz powder 11%, zinc oxide 2%, wollastonite 7%, albite feldspar 2% and corundum 2% to prepare The frit powder is kept at a melting temperature of 1520°C for 30 minutes, and then the material is cooled by water to form a frit, and the prepared frit is powdered, sieved, dried, and the 100-mesh sieve is taken for use;

[0070] (2) Preparation of raw glaze powder: by weight percentage, get albite 35%, burnt talc 15%, kaolin 6%, calcite 12%, zinc oxide 6%, wollastonite 10%, corundum 10% and carbonic acid Barium 6%, mix well and set aside;

[0071] (3) By weight percentage, take 65% of raw glaze powder and 35% of frit powder prepared in the above steps, add water and ball mill for 8 hours to obtain glaze slurry, control the fineness of 325 mesh sieve to be 1% by mass fraction, then stale for 49 hours, and prepare Obtain high-performance wear-resistant glaze;

[0072] (4) Replace the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Mohs hardnessaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of building ceramics, particularly to a high-performance wear-resistant glaze and a preparation method thereof, wherein the high-performance wear-resistantglaze comprises, by weight, 65-75% of raw glaze powder and 25-35% of frit powder, the raw glaze powder comprises, by weight, 30-40% of albite, 12-16% of calcined talc, 4-10% of kaolin, 10-15% of calcite, 2-8% of zinc oxide, 10-15% of wollastonite, 10-20% of corundum and 2-8% of barium carbonate. A purpose of the invention is to provide a high-performance wear-resistant glaze and a preparation method thereof, wherein the flatness of the glazed brick prepared from the glaze meets the production process requirements while the contradiction between the transparency and the wear resistance of theglaze layer is solved, and the prepared glazed brick is greatly improved in wear resistance, high in flatness and good in color development.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a high-performance wear-resistant glaze and a preparation method thereof. Background technique [0002] Ceramic glazed tiles combine the advantages of porcelain glazed tiles and polished tiles. They are not only rich in patterns and images, but also have a smooth and bright surface. In the early days of their appearance, they were popular among consumers for their rich designs and patterns and clear texture levels. However, with the passage of time, some disadvantages of glazed tiles have gradually become prominent, the most prominent of which is the low wear resistance of the product, which makes the surface easy to wear. The wear resistance of glazed glazed tiles is a big problem that plagues the industry. When using glazed tiles as floor decoration materials, there are high requirements for the wear resistance of glazes. Glazed tiles prepared from glazes with l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/04C03C8/02
CPCC03C8/20C03C8/04C03C8/02
Inventor 罗强钟保民李苏波周燕潘新东
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap