Preparation method of anti-stripping rubber asphalt mixture

A technology for rubberized asphalt and mixture, which is applied in the field of preparation of anti-stripping rubberized asphalt mixture, can solve problems such as poor adhesion between acid aggregate and asphalt, and achieve the advantages of improving water damage resistance, reducing engineering cost and improving service life. Effect

Active Publication Date: 2021-12-21
HENAN PROVINCIAL COMM PLANNING & DESIGN INST CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a preparation method of anti-stripping rubber asphalt mixture, which solves the disadvantage of poor adhesion between acidic aggregates and asphalt at present, greatly increases the use ratio of acidic aggregates in asphalt pavement, and improves the asphalt Fatigue resistance and durability of pavement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of anti-stripping rubber asphalt mixture
  • Preparation method of anti-stripping rubber asphalt mixture
  • Preparation method of anti-stripping rubber asphalt mixture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1 Preparation of 1# anti-peeling rubber asphalt mixture

[0021] In the first step, put 100 parts of base asphalt, 4 parts of softener tall oil, and 0.8 parts of activator (a compound of alkylphenol disulfide and xylene disulfide at a mass ratio of 1:2) into the modified Heat in the asphalt reaction tank, when the temperature rises to 120°C, stir at constant temperature for 5 minutes, add 20 parts of rubber powder and start to raise the temperature step by step: when the temperature rises to 150°C, 4.5 parts, 0.9 parts of activator (alkylphenol disulfide and Xylene disulfide compounded with a mass ratio of 1:2) were put into the modified asphalt reaction tank and heated together. When the temperature rose to 120°C, the temperature was stirred for 5 minutes, and 20 parts of rubber powder was added to start the temperature rise step by step: when When the temperature rises to 150°C, stir at a constant temperature for 10 minutes; when the temperature continues to r...

Embodiment 2

[0030] Example 2 Preparation of 2# anti-peeling rubber asphalt mixture

[0031] In the first step, put 100 parts of base asphalt, 5 parts of softener tall oil, and 1.2 parts of activator (a compound of alkylphenol disulfide and xylene disulfide at a mass ratio of 1:2) into the modified Heat in the asphalt reaction tank, when the temperature rises to 120°C, stir at a constant temperature for 5 minutes, add 25 parts of rubber powder and start to raise the temperature step by step: when the temperature rises to 150°C, stir at a constant temperature for 10 minutes; when the temperature continues to rise to 180°C, stir at a constant temperature for 10 minutes ;When the temperature rises to 200°C, stir and react at this temperature for 30 minutes; then lower the temperature to 180°C, and store the prepared rubber asphalt for later use;

[0032] In the second step, add 5 parts of deionized water and 2.5 parts of absolute ethanol into the beaker to prepare an ethanol solution, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an anti-stripping rubber asphalt mixture. Firstly, base asphalt, a softener and an activator are put into a reaction tank together with gradient heating and stirring to obtain rubber asphalt; the mixture is prepared with deionized water and absolute ethanol into an ethanol solution, then add a coupling agent and a silicone waterproofing agent, and stir evenly at room temperature to make an organic surface modifier; mix cement and hydrated lime powder in a mixer in proportion to prepare an inorganic modifier; grading Under the continuous stirring of the aggregate in the forced mixer, the organic surface modifier is sprayed on the surface of the graded aggregate, and after drying, it is blended with the inorganic modifier to obtain a comprehensive modified aggregate; rubber asphalt and comprehensive The anti-stripping rubber asphalt mixture is obtained after the modified aggregate is prepared according to the basic ratio of the asphalt mixture. The invention adopts surface modification technical means to change the surface property of the mineral material in the asphalt mixture, improves the adhesion between the asphalt and the mineral material, and prolongs the service life of the road surface.

Description

technical field [0001] The invention relates to the field of road engineering materials, in particular to a preparation method of an anti-stripping rubber asphalt mixture. Background technique [0002] Asphalt roads have the characteristics of smooth surface, comfortable driving, and short construction period, and are widely used in road construction. However, many pavements often suffer serious damage during service, and early damage such as spalling, rutting, cracking, and potholes occurs. Especially among the various forms of early damage, water damage has a greater impact on pavement performance. Many studies have shown that the root cause of water damage to the pavement is that the adhesion of asphalt on the surface of the aggregate is weak. Potholes and other diseases. [0003] For asphalt pavement, the adhesion and anti-stripping performance of asphalt and aggregate is one of the most basic conditions to ensure the performance of the pavement. Therefore, when build...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B20/12C04B111/20
CPCC04B26/26C04B20/12C04B2111/20C04B2111/0075C04B14/048C04B14/28C04B24/34C04B24/08C04B24/16C04B20/1051C04B20/1077C04B20/1066
Inventor 王笑风杨博刘东旭刘建飞赵志刚徐琦万晨光
Owner HENAN PROVINCIAL COMM PLANNING & DESIGN INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com