Growth factor loaded bacterial cellulose/biological ceramic composite membrane

A technology of bacterial cellulose membrane and bacterial cellulose is applied in the field of growth factor-loaded bacterial cellulose/bioceramic composite membrane and its preparation, which can solve the problem of poor mechanical strength of bone repair bioceramic membrane, easily inactivated growth factor loading and Release speed, difficult to control and other issues, to achieve the effect of improving adhesion stability, improving permeability, and improving existence stability

Active Publication Date: 2019-11-19
东营凤起生物科技发展有限公司 +1
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the deficiencies in the prior art, the purpose of the present invention is to provide a growth factor-loaded bacterial cellulose / bioceramic composite membrane, which has good biocompatibility and can effectively maintain the biological activity of bone repair growth factors, The repair material applied to bone defect tissue solves the problem of poor mechanical strength of bone repair bioceramic membranes; at the same time, the composite membrane can effectively control the release rate of growth factors, which solves the problem of easy growth factors in the current bone tissue repair materials loaded with growth factors. Deactivation and difficulty in controlling loading and release rates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Growth factor loaded bacterial cellulose/biological ceramic composite membrane
  • Growth factor loaded bacterial cellulose/biological ceramic composite membrane
  • Growth factor loaded bacterial cellulose/biological ceramic composite membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036]A bacterial cellulose membrane / bioceramic composite membrane loaded with growth factors is characterized in that the composite membrane is based on the bacterial cellulose membrane, and the surface is loaded with growth factors in the form of gel deposition coating, and then It is obtained by carrying a bioceramic film on its surface by electrospinning technology; its preparation method includes the following steps:

[0037] (1) Preparation of bacterial cellulose membrane loaded with growth factors

[0038] Inoculate the activated strain of Acetobacter xylinum into the egg liquid fermentation medium, take out the bacterial cellulose membrane on the upper layer of the fermentation broth after 4-5 days of fermentation, wash with warm water after washing until the washing liquid is neutral, and remove the bacterial cellulose membrane Cut to a size of 2cm×2cm, ready for use; Among them, the egg liquid medium is a fermentation medium obtained by adding 40g of sucrose, 15g of ...

Embodiment 2

[0046] A bacterial cellulose membrane / bioceramic composite membrane loaded with growth factors is characterized in that the composite membrane is based on the bacterial cellulose membrane, and the surface is loaded with growth factors in the form of gel deposition coating, and then It is obtained by carrying a bioceramic film on its surface by electrospinning technology; its preparation method includes the following steps:

[0047] (1) Preparation of bacterial cellulose membrane loaded with growth factors

[0048] Inoculate the activated strain of Acetobacter xylinum into the egg liquid fermentation medium, take out the bacterial cellulose membrane on the upper layer of the fermentation broth after 4-5 days of fermentation, wash with warm water after washing until the washing liquid is neutral, and remove the bacterial cellulose membrane Cut to a size of 4cm×4cm, ready for use; Among them, the egg liquid medium is a fermentation medium obtained by adding 40g of sucrose, 15g of...

Embodiment 3

[0056] A bacterial cellulose / bioceramic composite membrane loaded with growth factors is characterized in that the composite membrane is based on the bacterial cellulose membrane, and the surface is loaded with growth factors in the form of gel deposition coating, and then electrostatic Spinning technology is obtained by loading bioceramic membrane on its surface; its preparation method includes the following steps:

[0057] (1) Preparation of bacterial cellulose membrane loaded with growth factors

[0058] Inoculate the activated strain of Acetobacter xylinum into the egg liquid fermentation medium, take out the bacterial cellulose membrane on the upper layer of the fermentation broth after 4-5 days of fermentation, wash with warm water after washing until the washing liquid is neutral, and remove the bacterial cellulose membrane Cut to a size of 5cm×5cm, ready for use; Among them, the egg liquid medium is a fermentation medium obtained by adding 40g of sucrose, 15g of agar, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a growth factor loaded bacterial cellulose / biological ceramic composite membrane and a preparation method thereof. According to the composite membrane, a bacterial cellulose membrane is used as a basal body, growth factors are loaded on the surface of the bacterial cellulose membrane in a gel depositing and coating manner, and then a biological ceramic membrane is coated onto the surface through an electrostatic spinning technique so that the growth factor loaded bacterial cellulose / biological ceramic composite membrane is obtained. The bacterial cellulose membrane andthe biological ceramic membrane both have a nanometer fiber structure, so that the growth factor loaded bacterial cellulose / biological ceramic composite membrane can be used for materials for tissue repair, and has ample contact space with the cell environment of damaged tissue. Besides, the growth factor loaded bacterial cellulose / biological ceramic composite membrane has favorable effect of maintaining activity of the growth factors, the releasing speed of the growth factor can be controlled through controlling the degradation speed of the composite membrane, and the growth factor loaded bacterial cellulose / biological ceramic composite membrane has favorable application value in the tissue repair respect of promoting tissue division and cell regeneration and the like.

Description

technical field [0001] The invention relates to the technical field of biological materials, in particular to a bacterial cellulose / biological ceramic composite membrane loaded with growth factors and a preparation method thereof. Background technique [0002] Bone defect caused by trauma, tumor, etc. has become a common clinical disease at present. At present, the use of tissue engineering to repair bone defect has become a hot spot, and the tissue engineering scaffold materials used for bone tissue defect repair are mostly concentrated in the use of biopolymers. Composites of materials and ceramic particles, but simple composite materials have the problem of low biological activity. It is one of the research directions of tissue engineering to obtain higher activity of composite tissue engineering materials by loading growth factors; [0003] At present, tissue repair materials loaded with growth factors have been extensively studied. Growth factor loading can regulate the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/20A61L27/34A61L27/54A61L27/46A61L27/56A61L27/22A61L27/58
CPCA61L27/20A61L27/34A61L27/54A61L27/46A61L27/56A61L27/22A61L27/58A61L2300/252A61L2300/414A61L2300/604A61L2300/606C08L1/02C08L67/04
Inventor 张正男段书霞韩涵付迎坤林建香石沛龙崔彬彬王红磊韩修恒田崇于肇锦郝明严子跃佘开江
Owner 东营凤起生物科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products