Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Manufacturing method of RuYi advanced porcelain painting with pictures located under glaze layers

A technology of Ruyi jade porcelain and its production method, applied in coating, decorative arts, manufacturing tools, etc., can solve problems such as affecting product quality and enterprise production efficiency, unable to form the artistic texture of Ru porcelain surface, and weak three-dimensional image of the picture. , to achieve the effect of easy control of firing time, easy control of firing temperature, and beautiful pattern.

Pending Publication Date: 2019-12-31
张柳松
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problems existing in the production process of the existing glass-ceramic plate paintings: 1. Generally, single-sided porcelain plate paintings, the picture is directly printed on the front or back of the glass plate, and it is easy to scratch the picture during the production and transportation process; 2. , most of the ordinary single-sided porcelain plate paintings are two-dimensional printing, and the three-dimensional effect of the picture is not strong; third, the surface of ordinary single-sided porcelain plate paintings is generally coated with plain white glaze, and the jade texture on the surface is not strong after firing, which cannot form the surface of Ru porcelain. Artistic texture affects technical issues such as product quality and enterprise production efficiency. The present invention provides a method for making Ruyi jade porcelain paintings with pictures located at the lower part of the glaze layer. The method is reasonable and feasible, the design is ingenious, and the pictures will not be scratched inside and outside , the picture has a strong three-dimensional effect, bright colors, strong jade texture on the surface, strong and durable, and can be preserved for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for making Ruyi jade porcelain painting whose picture is located at the lower part of the glaze layer, comprising the following steps:

[0024] Step 1, select the glass plate for cleaning treatment first, and then perform jade treatment on the front of the glass plate;

[0025] Step 2, print and draw on the back of the glass plate, and use a nano-ceramic printer to print high-definition patterns on the back of the glass plate;

[0026] Step 3: Put the high-definition printed glass plate horizontally into the glass tempering furnace for rolling firing, the firing temperature is 650°C, the firing time is 20 minutes, and naturally cool down to room temperature for 5 minutes after firing;

[0027] Step 4: Prepare the glaze layer of Ruyi Tianqing glaze, and glaze the reverse side of the glass plate to protect the picture. The mass ratio of each component of the glaze layer is: 8 parts of black bluestone, 8 parts of kaolin, 30 parts of feldspar powder, 5 parts of qu...

Embodiment 2

[0033] A method for making Ruyi jade porcelain painting whose picture is located at the lower part of the glaze layer, comprising the following steps:

[0034] Step 1, select the glass plate for cleaning treatment first, and then perform jade treatment on the front of the glass plate;

[0035] Step 2, print and draw on the back of the glass plate, and use a nano-ceramic printer to print high-definition patterns on the back of the glass plate;

[0036] Step 3: Place the high-definition printed glass plate horizontally into a glass tempering furnace for rolling firing at a firing temperature of 700°C for a firing time of 12 minutes. After firing, naturally cool for 15 minutes to cool down to room temperature;

[0037] Step 4: prepare the glaze layer of Ruyi Tianqing glaze, and glaze the reverse side of the glass plate to protect the picture. The mass ratio of each component of the glaze layer is: 12 parts of black bluestone, 12 parts of kaolin, 35 parts of feldspar powder, 8 pa...

Embodiment 3

[0043] A method for making Ruyi jade porcelain painting whose picture is located at the lower part of the glaze layer, comprising the following steps:

[0044] Step 1, select the glass plate for cleaning treatment first, and then perform jade treatment on the front of the glass plate;

[0045] Step 2, print and draw on the back of the glass plate, and use a nano-ceramic printer to print high-definition patterns on the back of the glass plate;

[0046] Step 3: Place the high-definition printed glass plate horizontally into a glass tempering furnace for rolling firing at a firing temperature of 780°C for a firing time of 5 minutes. After firing, cool naturally for 20 minutes to room temperature;

[0047] Step 4: prepare the glaze layer of Ruyi Tianqing glaze, and glaze the reverse side of the glass plate to protect the picture. The mass ratio of each component of the glaze layer is: 15 parts of black bluestone, 15 parts of kaolin, 40 parts of feldspar powder, 10 parts of quartz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of RuYi advanced porcelain painting with pictures located under glaze layers. The manufacturing method comprises the steps of glass plate cleaning treatment, jade-like treatment, high-definition printing, direct firing, celeste blue glaze layer preparation, glaze layer spraying, continuous firing, cooling and the like. The manufacturing method is reasonable and feasible; design is skillful; picture scratching is avoided, picture stereoscopic impression is strong, color is brilliance, surface jade-like texture feel is strong, obtained products arefirm and durable; long term storage can be realized. The technical problems that in the existing glass porcelain plate painting manufacturing process, picture scratching is easily caused, picture stereoscopic impression is not strong, surface jade-like texture feel is not strong after firing, the artistic texture feel of Ru porcelain surface cannot be formed, and product quality and enterprise production benefits are affected are solved. Compared with the prior art, the advantages of the manufacturing method are that the market prospect is promising, and development space is large.

Description

technical field [0001] The invention relates to the technical field of jade porcelain paintings on glass plates, in particular to a method for making Ruyi jade porcelain paintings whose pictures are located at the lower part of the glaze layer. Background technique [0002] Porcelain plate painting is an innovative new type of decorative painting. It is loved by people because of its vivid image, not afraid of wind and sun, and excellent quality. [0003] Ru kiln is famous for firing celadon, which has glaze colors such as sky blue, sky blue, bean green and moon white. The sky blue glazed porcelain of Ru kiln contains agate in the glaze. The color is green and lustrous. It is said that the color is elegant and natural, and it has the reputation of "after the rain, the blue clouds break the place". [0004] Most of the existing porcelain plate paintings are glass porcelain plate paintings and metal porcelain plate paintings. During the process, it is easy to scratch the pi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/34C03C8/00C03B27/04B44C5/04B24C1/06
CPCB24C1/06B44C5/0407B44C5/0446C03B27/04C03C8/00C03C17/002C03C17/3411C03C2217/72C03C2218/112C03C2218/119C03C2218/32
Inventor 张柳松
Owner 张柳松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com