Packaging material and molded case

A technology of packaging materials and heat-resistant resins, which can be used in transportation and packaging, battery box/case materials, electronic equipment, etc., and can solve problems such as damage to uniform coloring and insufficient adhesion

Pending Publication Date: 2020-01-10
株式会社レゾナックパッケージング
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] That is, when the above-mentioned colored packaging material is molded into a container (casing) shape by deep drawing or bulge molding, there is a problem that the heat-resistant resin stretched film layer as the outer layer and the colored layer are closely spaced. Insufficient conformability, so the coloring layer peels off, the bottom layer (not black) is exposed and appears as an appearance, and the uniform coloring (black coloring, etc.) is impaired

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Packaging material and molded case
  • Packaging material and molded case
  • Packaging material and molded case

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0159] 50 parts by mass of carbon black with an average particle diameter of 0.8 μm, 5 parts by mass of ethylenediamine, and 45 parts by mass of polyester-based polyol (number average molecular weight: 2500) were blended to obtain a main ingredient. An ink composition was obtained by blending 3 parts by mass of toluene diisocyanate (TDI) as a curing agent with respect to 100 parts by mass of the above-mentioned main agent, and further blending 50 parts by mass of toluene.

[0160] The above-mentioned adhesive composition W was coated by a gravure roll coating method on a biaxially stretched nylon (6 nylon) film (resistant to Thermal resin stretch film layer, MD / TD=0.95) 2 side, after drying, place it in 40°C environment for 1 day, so as to carry out curing reaction, and form an easy-bonding layer 30, and its formation amount is 0.1g / m 2 .

[0161] Next, the above-mentioned ink composition was printed (coated) on the surface of the easily-adhesive layer 30 of the above-mention...

Embodiment 2

[0166] A biaxially stretched 6 nylon film (MD / TD=0.9) with a thickness of 15 μm and a shrinkage rate of 2.5% in hot water obtained by stretching by a simultaneous biaxial stretching method was used instead of a film with a thickness of 15 μm and a shrinkage rate of 4.0% in hot water. Biaxially stretched 6 nylon film (MD / TD = 0.95), except that, in the same manner as in Example 1, to obtain figure 1 Packing material 1 shown.

Embodiment 3

[0168] A biaxially stretched 6-nylon film (MD / TD=1.0) with a thickness of 15 μm and a hot water shrinkage rate of 3.5% obtained by stretching by a simultaneous biaxial stretching method was used instead of a film with a thickness of 15 μm and a hot water shrinkage rate of 4.0%. Biaxially stretched 6 nylon film (MD / TD = 0.95), except that, in the same manner as in Example 1, to obtain figure 1 Packing material 1 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a packaging material and a molded case. The packaging material (1) includes a heat resistant resin stretched film layer (2) as an outer layer, a thermoplastic resin layer (3)as an inner layer, a metal foil layer 4 arranged between these layers, and a colored ink layer (10) arranged between the metal foil layer 4 and the heat resistant resin stretched film layer (2). As the heat resistant resin stretched film, a heat resistant resin stretched film having a hot water shrinkage rate of 2% to 20% is used, and the heat resistant resin stretched film layer (2) and the colored ink layer 4 are integrally laminated via an easily adhesive layer (30). In this packaging material, at the time of forming and sealing, and even being used in a somewhat severe environment such ashigh-temperature and humid environment, the colored ink layer will not be detached from the heat resistant resin stretched film layer.

Description

[0001] This application is a divisional application of Chinese Invention Patent Application No. 201410281751.5 with the filing date of June 20, 2014, and the title of the invention is "Packaging Material and Formed Housing". technical field [0002] The present invention relates to a battery that can be suitably used as a casing for a notebook computer, a mobile phone, a vehicle, or a stationary secondary battery (lithium ion secondary battery), and is also suitable as a packaging material for food and pharmaceuticals. Packaging materials and molding shells used in packaging materials. Background technique [0003] Batteries such as lithium-ion secondary batteries are increasingly required to be colored in order to match the appearance and color of equipment such as electrical equipment to be loaded. In order to give a sense of massiness and luxury, the equipment is often made black, and in this case, the battery is also usually made black. In addition, coloring in other va...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/08H01M2/02H01M50/117H01M50/119H01M50/121H01M50/122H01M50/126H01M50/131
CPCB29C51/08B29C51/14B32B33/00B29L2031/3468B32B2457/10B32B37/12B32B2311/00B32B2307/402H01M50/117H01M50/131H01M50/122H01M50/119H01M50/126H01M50/121Y10T428/31678Y10T428/31522Y10T428/25Y10T428/269Y02E60/10H01M50/124H01M50/24
Inventor 南堀勇二王宏琳
Owner 株式会社レゾナックパッケージング