Method for preparing coating by 3D printing overlapping electron beam

Abstract

The invention relates to a method for preparing a coating by 3D printing overlapping an electron beam. Metal or ceramic powder and metal/ceramic powder are printed on the surface of a base material layer by layer through 3D printing, layer-by-layer printing is carried out by a three-dimensional model according to the set layer thickness, and then the metal or ceramic powder and metal/ceramic powder on the surface of the base material are preheated to form a fusion layer. A heating device used for the preheating includes a high-frequency vibrator and an induction heating coil which are placed on a workbench, the high-frequency vibrator acts on the bottoms of the fusion layer and the base material, the induction heating coil is arranged around the base material for preheating, after preheating is carried out, the fusion layer is melted with the electron beam to form a metal/ceramic. composite coating, and finally the metal/ceramic composite coating is subjected to post-heat treatment through the induction heating coil. The product development cycle is greatly shortened, production rate is improved, and the production cost is reduced.

Description

Technical field: [0001] The invention relates to a method for preparing a coating by 3D printing overlapping electron beams. Background technique: [0002] Laser 3D printing technology is a major breakthrough in manufacturing technology in the past two decades, and its influence on manufacturing can be compared with that of CNC machine tools in the middle of the 20th century. Laser 3D printing technology can directly and quickly manufacture complex functional parts. It has great competitive advantages in material selection, design freedom, and product development. It can also greatly shorten the processing cycle and greatly reduce the time for manufacturing preparation and data conversion. Compared with traditional material cutting and forming, the additive manufacturing method represented by this technology is a major innovation. 3D printing manufacturing technology is a near-net-shaping technology. The size of the printed parts is very close to the final product. Compared...

AI Technical Summary

Problems solved by technology

It solves the problems of low molding precision and low powder utilization rate in the prior art, and avoids the conventional problem of requiring more auxiliary powder and limited size

[0003] The relevant patents are as follows: publication number: CN 107225245 A; patent name: metal powder 3D laser forming powder coating device and forming method; and application number: CN 201811514812.2; patent name: a combination of pre-set layer and ultrasound to enhance the coating Bonding force method and application number: CN201210097330.8; patent name: method of presetting powder by extrusion method for laser cladding to obtain com

Images