Low-cost and high-strength titanium alloy plate prepared by 100% of returned burdens and preparation method thereof

A titanium alloy, low-cost technology, which is applied to the preparation of low-cost high-strength titanium alloy plates with 100% returned charge and its preparation field, can solve the problems of material waste, inability to recycle, increase the difficulty of alloy smelting, etc., so as to reduce costs and reduce Production cost, effect of high strength performance

Active Publication Date: 2020-02-04
BAOJI TITANIUM IND +1
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the TC18 titanium alloy contains many types of elements, including Al with a low melting point and Mo with a high melting point, as well as Cr and Fe, which are easy to segregate, it not only increases the difficulty of smelting the alloy, but also increases the recovery of the alloy. Disposal is also an issue, recycling is not yet possible
At present, there are a large number of TA1, TA2, TA3, TA4, TA11, TA18, TB2, TB6, TC4, TC6 and TC18 titanium alloy residues in relevant domestic titanium enterprises, which cannot be recycled, resulting in huge waste of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-cost and high-strength titanium alloy plate prepared by 100% of returned burdens and preparation method thereof
  • Low-cost and high-strength titanium alloy plate prepared by 100% of returned burdens and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The following will clearly and completely describe the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0028] In order to solve the above technical problems, the present invention provides a low-cost high-strength titanium alloy plate prepared by returning 100% of the charge to the furnace, and its components are calculated by mass percentage: Al: 3.0-6.0wt.%; Mo: 3.0-5.5wt. %; V: 3.0~5.5wt.%; Cr: 0.1~2.0wt.%; Fe: 0.1~2.0wt.%; O: ≤0.20wt.%; N: ≤0.10wt.%; C: ≤0.10wt .%; the balance is Ti and unavoidable impurities. The raw materials of all the above-mentioned components of the low-cost high-strength titanium alloy are...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a low-cost and high-strength titanium alloy plate prepared by 100% of returned burdens. The low-cost and high-strength titanium alloy plate comprises the following components inpercentage by mass: 3.0-6.0% of Al, 3.0-5.5% of Mo, 3.0-5.5% of V, 0.1-2.0% of Cr, 0.1-2.0% of Fe, O not more than 0.20%, N not more than 0.10%, C not more than 0.10%, and the balance of Ti and inevitable impurities; raw materials of all the components of the low-cost and high-strength titanium alloy plate prepared by 100% of the returned burdens are pure titanium residues and titanium alloy residues; the pure titanium residues are one or more of TA1, TA2, TA3 and TA4; and the titanium alloy residues are one or several of TA11, TA18, TB2, TB6, TC4, TC6 and TC18. The invention further providesa preparation method of the low-cost and high-strength titanium alloy plate prepared by 100% of the returned burdens. Compared with the prior art, the low-cost and high-strength titanium alloy plateprepared by 100% of the returned burdens by the preparation method reaches the stretch strength of higher than 1150 MPa.

Description

technical field [0001] The invention relates to the field of preparation and processing of titanium alloys, in particular to a low-cost high-strength titanium alloy plate prepared by 100% returned charge and a preparation method thereof. Background technique [0002] Because titanium alloy has a series of advantages such as low density, high specific strength and excellent corrosion resistance, it has become more and more widely researched and applied in the fields of aerospace, shipbuilding and chemical industry. Due to the high cost of titanium and titanium alloys, the large-scale application of titanium and titanium alloys is limited. Therefore, the research and application of low-cost titanium alloys have attracted the attention of countries all over the world, and a lot of financial and manpower have been invested in the development of low-cost titanium alloy materials and the development of short-process preparation and processing technologies. [0003] The high cost ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C14/00C22C1/02C22F1/18C22B9/20C22B7/00B21C37/02
CPCB21C37/02C22B7/003C22B9/20C22C1/02C22C14/00C22F1/183Y02P10/20
Inventor 王新王俭乔璐李蒙刘继雄张平辉王小翔刘钊强刚刚
Owner BAOJI TITANIUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products