A process for increasing the bonding strength of aluminum honeycomb panels

A technology of bonding strength and aluminum honeycomb, which is applied in the field of composite panels, can solve the problems of small glue contact area, low bonding strength, and failure to connect aluminum honeycomb core and aluminum plate.

Active Publication Date: 2021-09-14
广东华粘新材料研究有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the production process of existing aluminum honeycomb panels, glue is usually used to coat the side of the aluminum panel in contact with the aluminum honeycomb core, so that the two aluminum panels are laminated and bonded to the upper and lower ends of the aluminum honeycomb core respectively. However, this method The contact area between the cells at the root of the aluminum honeycomb core and the glue on the aluminum plate is relatively small, and the bonding strength between the two is not high. The role of aluminum plate connection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A process for increasing the bonding strength of aluminum honeycomb panels
  • A process for increasing the bonding strength of aluminum honeycomb panels

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The idea, specific structure and technical effects of the present invention will be clearly and completely described below in conjunction with the embodiments and accompanying drawings, so as to fully understand the purpose, features and effects of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, rather than all of them. Based on the embodiments of the present invention, other embodiments obtained by those skilled in the art without creative efforts belong to The protection scope of the present invention.

[0013] refer to figure 1 and figure 2 , the application of a continuous production process of aluminum honeycomb panels of the present invention mainly includes the steps of mixing, gluing, billet formation, scraping, static pressure cooling and solidification, wherein the process of the mixing step is as follows: the reactive hot melt adhesive Component A and component B of the reactive hot me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for increasing the bonding strength of an aluminum honeycomb panel. The aluminum honeycomb panel includes an upper panel, an aluminum honeycomb core and a lower panel sequentially laminated from top to bottom. The upper panel and the lower panel are connected with the aluminum honeycomb panel One side of the laminated core is coated with glue, including the following steps: (1) fixing the upper plate and the lower plate of the aluminum honeycomb panel after forming the billet; (2) moving the distance a of the aluminum honeycomb core to make the glue gather on the aluminum honeycomb core on the outer edge of the hole. This process makes the glue gather on the outer edge of the cells of the aluminum honeycomb core, thereby greatly increasing the contact area between the cells of the aluminum honeycomb core and the glue, thereby increasing the bonding strength between the aluminum honeycomb core and the upper and lower plates, and improving the aluminum honeycomb core. The bonding strength of the honeycomb panel can reduce the amount of glue on the premise of meeting the bonding strength requirements, thereby saving costs.

Description

technical field [0001] The invention relates to the technical field of composite panels, in particular to a process for increasing the bonding strength of aluminum honeycomb panels. Background technique [0002] Aluminum honeycomb panel refers to a composite panel with a three-layer structure of "aluminum panel / aluminum honeycomb core / aluminum panel". The aluminum panel and aluminum honeycomb core are bonded with an adhesive. This composite panel has high strength, light weight and no formaldehyde. It is widely used in the interior and exterior decoration of large buildings, as well as the compartment partitions of aircraft or ships, and is now further expanded to the fields of furniture panels and other fields. In the production process of existing aluminum honeycomb panels, glue is usually used to coat the side of the aluminum panel in contact with the aluminum honeycomb core, so that the two aluminum panels are laminated and bonded to the upper and lower ends of the alumi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B3/12B32B15/01B32B7/12B32B37/12B32B37/06B32B37/10
CPCB32B3/12B32B7/12B32B15/016B32B37/06B32B37/10B32B37/1284B32B2038/0076B32B2250/03B32B2250/40B32B2305/024B32B2309/022B32B2309/025B32B2309/125
Inventor 龙万堂
Owner 广东华粘新材料研究有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products