A kind of grinding wheel for photovoltaic glass processing and preparation method thereof

A photovoltaic glass and grinding wheel technology, applied in the field of grinding wheels, can solve the problems of unstable use quality of grinding wheels, limited processing speed, poor chip removal, etc., and achieve the effects of good sharpness and deformation resistance, long service life and stable quality.

Active Publication Date: 2021-02-23
苏州赛尔科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For edging wheels for photovoltaic glass, conventional grinding wheels mostly use copper-tin-iron-nickel as the matrix formula. This formula is modified by adding iron and nickel on the basis of the copper-tin formula, with copper-iron-nickel as the skeleton and low-melting tin powder as the Binder, iron and diamond have good wettability, the contact angle is 50°, which is far better than copper, while nickel has good wear resistance and toughness, and is infinitely soluble with copper, and can reduce copper and iron The sintering loss of the low melting point metal tin in the base formula, but the carcass formula has a fatal weakness, the sharpness is poor, the quality of the grinding wheel is unstable, and edge chipping caused by poor chip removal often occurs, and because it is not sharp enough, the processing speed is limited , causing certain troubles to manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of grinding wheel for photovoltaic glass processing and preparation method thereof
  • A kind of grinding wheel for photovoltaic glass processing and preparation method thereof
  • A kind of grinding wheel for photovoltaic glass processing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the grinding wheel for photovoltaic glass processing disclosed by the invention is as follows:

[0025] (1) Mix metal powder and ball mill to obtain a metal matrix; the metal powder is composed of copper powder, tin powder, cobalt powder and chromium powder;

[0026] (2) Mix the metal matrix and diamond to obtain the material;

[0027] (3) Cold pressing the material to obtain the green body;

[0028] (4) The green body is sintered and hot forged to obtain a grinding wheel for photovoltaic glass processing.

Embodiment

[0030] Mixing: Add the metal powder into the ball mill according to the formula requirements in terms of mass percentage, add alcohol with a total weight of 25% of the metal powder, and then put in zirconium balls, the ratio of ball to material is 2:1 (wt%), and the speed is 500 rpm. Mix and carry out ball milling for 100 minutes, take out the material and dry it, then put it into a V-type mixer, add acetone with 10% of the total mass of metal powder, add diamond after mixing for 120 minutes (the volume ratio of metal matrix to diamond is 75: 25), after mixing for 60 minutes, pass through a 120# sieve (120 microns) after drying to obtain a uniformly mixed material;

[0031] Pressing: the above materials are added to the existing mold and placed on a hydraulic press, and a pressure of 4 tons / cm is applied 2 , keep the pressure for 10 seconds; then reverse the mold up and down and apply a pressure of 4 tons / cm 2 , hold the pressure for 10 seconds, thereby making a cold-pressed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a grinding wheel for photovoltaic glass processing and a preparation method thereof. Copper powder, tin powder, cobalt powder and chromium powder are mixed and then ball-milled to obtain a metal carcass, and the metal carcass is mixed with diamond to obtain a material; cold pressing The material is obtained into a green body, and the green body is sintered and hot forged to obtain a grinding wheel for photovoltaic glass processing. The grinding wheel for photovoltaic glass processing prepared by the formula provided by the present invention has the characteristics of strong holding force, good sharpness and long service life, and can meet the requirements of photovoltaic glass processing. When cutting 3.5mm photovoltaic glass, the edge chipping is less than 20 μm, and the cutting life of the blade is long. Up to 50000m.

Description

technical field [0001] The invention belongs to the technical field of grinding wheels, and in particular relates to a grinding wheel for photovoltaic glass processing and a preparation method thereof. Background technique [0002] Crystalline silicon solar cells are developing rapidly, but monocrystalline silicon has poor mechanical properties, is easily damaged, and is easily corroded. Therefore, photovoltaic glass is usually used for packaging to protect the battery and prolong its service life. The processing of photovoltaic glass has therefore attracted great attention, and diamond grinding wheels have emerged as the times require. For edging wheels for photovoltaic glass, conventional grinding wheels mostly use copper-tin-iron-nickel as the matrix formula. This formula is modified by adding iron and nickel on the basis of the copper-tin formula, with copper-iron-nickel as the skeleton and low-melting tin powder as the Binder, iron and diamond have good wettability, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D18/00B24D3/34
CPCB24D3/346B24D18/0009
Inventor 张莹莹王思宇李威夏磊冉隆光
Owner 苏州赛尔科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com