A dy(iii)-cu(ii) eutectic single-molecule magnet and its preparation method

A single-molecule magnet and a technology for molecular magnets are applied in the field of Dy-Cu eutectic single-molecule magnets and their preparation, achieving the effects of simple process, high yield and broad application prospects.

Active Publication Date: 2022-05-20
ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the true eutectic of metal coordination compounds, that is, the eutectic molecules are only composed of metal complexes as reactants has not been reported in the literature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A dy(iii)-cu(ii) eutectic single-molecule magnet and its preparation method
  • A dy(iii)-cu(ii) eutectic single-molecule magnet and its preparation method
  • A dy(iii)-cu(ii) eutectic single-molecule magnet and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation method of the Dy(III)-Cu(II) eutectic single-molecule magnet in this embodiment, the steps are as follows:

[0025] (1) Add 0.1 mmol of Dy(hfac) 3 (H 2 O) 2 Dissolve in 10 mL of methanol and stir for 25 minutes;

[0026] (2) Add 0.1 mmol of Cu(acac) 2 Dissolve in 15 mL of dichloromethane and stir for 10 minutes;

[0027] (3) Dy(hfac) will be dissolved 3 (H 2 O) 2 The methanol solution was added to the dissolved Cu(acac) 2 In dichloromethane solution, continue to stir at room temperature for 15 minutes, then filter, the resulting clear solution volatilizes naturally, after 3 days, dark green crystals are obtained, filter, wash with a small amount of methanol, and dry at room temperature to obtain Dy(III)-Cu(II) Eutectic molecular material with a calculated yield of 92% (calculated as Dy).

[0028] Perkin-Elmer 2400 elemental analyzer was used to analyze the content of C and H in the Dy(III)-Cu(II) eutectic molecular material, according to the mol...

Embodiment 2

[0034] The Dy(III)-Cu(II) eutectic single-molecule magnet [Dy(hfac) 3 (H 2 O) 2 ]-[Cu(acac) 2 ] The preparation method, the steps are as follows:

[0035] (1) Dy(hfac) 3 (H 2 O) 2 Dissolve in methanol and stir for 20 minutes to obtain Dy(hfac) with a concentration of 0.007 mol / L 3 (H 2 O) 2 methanol solution;

[0036] (2) Add Cu(acac) 2 Dissolved in dichloromethane, stirred for 15 minutes to obtain Cu(acac) with a concentration of 0.005 mol / L 2的 Dichloromethane solution;

[0037] (3) According to the volume ratio = 15:18, Dy(hfac) will be dissolved 3 (H 2 O) 2 The methanol solution was added to the dissolved Cu(acac) 2 In dichloromethane solution, continue to stir at room temperature for 20 minutes, filter, the resulting clear solution volatilizes naturally, after 3 days, dark green crystals are obtained, filter, wash with a small amount of methanol, and dry at room temperature to obtain Dy(III)-Cu(II) Eutectic molecular magnets.

Embodiment 3

[0039] The Dy(III)-Cu(II) eutectic single-molecule magnet [Dy(hfac) 3 (H 2 O) 2 ]-[Cu(acac) 2 ] The preparation method, the steps are as follows:

[0040] (1) Dy(hfac) 3 (H 2 O) 2 Dissolve in methanol and stir for 30 minutes to obtain Dy(hfac) with a concentration of 0.008 mol / L 3 (H 2 O) 2 methanol solution;

[0041] (2) Add Cu(acac) 2 Dissolve in dichloromethane and stir for 12 minutes to obtain Cu(acac) with a concentration of 0.006 mol / L 2的 Dichloromethane solution;

[0042] (3) According to the volume ratio = 15:20, Dy(hfac) will be dissolved 3 (H 2 O) 2 The methanol solution was added to the dissolved Cu(acac) 2 In dichloromethane solution, continue to stir at room temperature for 18 minutes, filter, the resulting clear solution volatilizes naturally, and obtain dark green crystals after 3 days, filter, wash with a small amount of methanol, and dry at room temperature to obtain Dy(III)-Cu(II) Eutectic molecular magnets.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Dy(III)-Cu(II) eutectic single-molecule magnet and a preparation method thereof. The chemical formula is: [Dy(hfac) 3 (H 2 O) 2 ]‑[Cu(acac) 2 ], wherein hfac is hexafluoroacetylacetonate anion, acac is acetylacetonate anion, and the preparation method is as follows: dissolve Dy(hfac) 3 (H 2 O) 2 The methanol solution was added to the dissolved Cu(acac) 2 Dichloromethane solution, stirred at room temperature for 15-20 minutes, filtered, the resulting clear solution volatilized naturally, and dark green crystals were obtained after 3 days, filtered, washed, and dried to obtain the Dy(III)-Cu(II) eutectic molecular magnet , the Dy(III)-Cu(II) eutectic molecular material has the performance of a single-molecule magnet, and has broad application prospects as a molecular-based magnetic material in high-density information storage devices, quantum chemical calculations, and spintronics.

Description

technical field [0001] The invention belongs to the technical field of preparation and application of molecular-based magnetic materials, and in particular relates to a Dy(III)-Cu(II) eutectic single-molecule magnet and a preparation method thereof. Background technique [0002] Single-molecule magnets are composed of independent single molecules that have almost no interaction in the magnetic sense. Each molecule can be regarded as a magnetic unit. At the blocking temperature T B The following exhibit superparamagnetic behavior. Single-molecule magnets have the characteristics of magnetic bistability, and can exhibit the hysteresis and slow magnetic relaxation behavior of traditional macroscopic magnets, so they have potential applications in ultra-high-density information storage, quantum computing, and molecular spintronics. ; On the other hand, single-molecule magnets usually exhibit the quantum tunneling effect (QTM effect) of microscopic particles at low temperature,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C49/92C07C45/77C07C45/81H01F1/42
CPCC07C49/92H01F1/42C07B2200/13
Inventor 李郤里周立明王爱玲崔明会
Owner ZHENGZHOU UNIVERSITY OF LIGHT INDUSTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap