Sterilization sealant for ceramic tile gap filling and preparation method thereof

A gap filling and beautifying agent technology, applied in the field of beautifying agents, can solve the problems of high price, wear, easy to scratch, etc., achieve the effect of natural and delicate color, excellent comprehensive performance, and avoid excessive hardness

Inactive Publication Date: 2020-05-08
安徽瑞波源数据科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the beautifying agent paint film in the prior art shrinks severely after drying, and secondary caulking is required. The cured film is relatively soft. If it is scrubbed for a long time, it is prone to scratches and abrasions, which will affect the appearance of the later stage. , it is more or less expensive, and the materials used are toxic and not environmentally friendly. After a long time, there will be cracks and dents in the brick joints, which not only affect the aesthetics of the ground and walls, but also affect the The service life of ceramic tiles is seriously detrimental to the construction quality of decoration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sterilization sealant for ceramic tile gap filling and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A bactericidal beautifying agent for ceramic tile gap filling, comprising A component and B component with a weight ratio of 10:1, and the A component includes the following components in parts by weight:

[0035] 88 parts of epoxy resin modified styrene-acrylic emulsion, 45 parts of silane-terminated polyether, 22 parts of phthalic anhydride polyester polyol, 10 parts of polytetrahydrofuran, 8 parts of epoxy-containing organosiloxane, 1,2-dicarboxylic acid di 1.5 parts of isononyl ester, 5 parts of acetyl tri-n-butyl citrate, 50 parts of talc powder, 5 parts of carbon black, 35 parts of bentonite, 20 parts of nano attapulgite, 12 parts of hollow glass microspheres, 15 parts of volcanic ash, 2 parts of fungicide HY-606-1, 3 parts of isothiazolinone derivative preservative, 30 parts of reinforcing fiber mixed with glass fiber and aramid fiber at a weight ratio of 1:1, 8 parts of pigment, dilauric acid 3 parts of dibutyltin;

[0036] The B component is epoxy resin amine ...

Embodiment 2

[0040] A bactericidal beautifying agent for ceramic tile gap filling, comprising A component and B component with a weight ratio of 12:1, and the A component includes the following components in parts by weight:

[0041] 100 parts of epoxy resin modified styrene-acrylic emulsion, 47 parts of silane-terminated polyether, 26 parts of phthalic anhydride polyester polyol, 6 parts of polytetrahydrofuran, 10 parts of epoxy-containing organosiloxane, 1,2-dicarboxylic acid di 1 part of isononyl ester, 5 parts of acetyl tri-n-butyl citrate, 45 parts of talc, 7 parts of carbon black, 35 parts of bentonite, 20 parts of nano attapulgite, 12 parts of hollow glass microspheres, 10 parts of volcanic ash, 1.4 parts of fungicide HY-606D, 5 parts of isothiazolinone derivative preservative, 25 parts of reinforcing fiber mixed with glass fiber and aramid fiber at a weight ratio of 5:1, 5 parts of pigment, dibutyltin dilaurate 5 copies;

[0042] The B component is the epoxy resin amine curing age...

Embodiment 3

[0046] A bactericidal beautifying agent for ceramic tile gap filling, comprising A component and B component with a weight ratio of 10:1, and the A component includes the following components in parts by weight:

[0047] 85 parts of epoxy resin modified styrene-acrylic emulsion, 40 parts of silane-terminated polyether, 22 parts of phthalic anhydride polyester polyol, 10 parts of polytetrahydrofuran, 8 parts of epoxy-containing organosiloxane, 1,2-dicarboxylic acid di 1 part of isononyl ester, 4 parts of acetyl tri-n-butyl citrate, 50 parts of talc, 5 parts of carbon black, 36 parts of bentonite, 20 parts of nano attapulgite, 8 parts of hollow glass microspheres, 10 parts of volcanic ash, 2 parts of fungicide HY-606D-2, 4 parts of isothiazolinone derivative preservative, 40 parts of reinforcing fiber mixed with glass fiber and aramid fiber at a weight ratio of 2:1, 5 parts of pigment, dilauric acid 3 parts of dibutyltin;

[0048] The B component is the epoxy resin amine curing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a sterilization sealant for ceramic tile gap filling and a preparation method of the sterilization sealant, and relates to the field of sealants, the sterilization sealant comprises a component A and a component B, wherein the component A comprises the following components in parts by weight: 80-100 parts of epoxy resin modified styrene-acrylic emulsion, 40-50 parts of silane-terminated polyether, 22-27 parts of phthalic anhydride polyester polyol, 5-11 parts of polytetrahydrofuran, 7-10 parts of epoxy-group-containing organosiloxane, 1-2 parts of 1, 2-diisononyl diformate, 3 to 8 parts of acetyl tri-n-butyl citrate, 40-50 parts of talcum powder, 5-10 parts of carbon black, 32-38 parts of bentonite, 10-20 parts of nano attapulgite, 8-15 parts of hollow glass beads, 10-20 parts of volcanic ash, 1-2 parts of a bactericide, 3-5 parts of a preservative, 20-40 parts of reinforced fibers, 5-10 parts of a pigment and 1-5 parts of dibutyltin dilaurate. The component B isan epoxy resin amine curing agent. The prepared sterilization sealant is excellent in comprehensive performance, capable of meeting the requirement for building ceramic tile seam filling, attractive,elegant, rich in color, natural and fine.

Description

technical field [0001] The invention relates to the field of beautifying agents, in particular to a bactericidal beautifying agent for filling gaps in ceramic tiles and a preparation method thereof. Background technique [0002] With the progress of society and the rapid development of the decoration industry, people have higher and higher requirements for the beauty of home decoration, especially in the beautification and modification of the gaps between decoration materials, which are increasingly paid attention to. For example, during the construction of ceramic tiles, one of the most commonly used materials in the field of architectural decoration, considering the factors of thermal expansion and contraction, certain gaps need to be reserved between the tiles. Fill and decorate it with caulking agent. The performance of the caulking agent directly affects the effect of home decoration. [0003] At present, the sealants usually used to fill the gaps of tiles are ordinar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J125/14C09J163/00C09J171/02C09J167/00C09J11/04C09J11/06C09J11/08
CPCC08K2201/014C08L2201/02C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J125/14C08L63/00C08L71/02C08L67/00C08L77/10C08K13/06C08K9/00C08K7/26C08K7/28C08K3/04C08K3/34C08K7/14C08K5/47C08K5/5435C08K5/11
Inventor 尹娜
Owner 安徽瑞波源数据科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products