Instant sodium alginate hydrogel fire extinguishing agent and preparation method thereof

A technology of sodium alginate and hydrogel, which is applied in the direction of fire prevention equipment, etc.

Active Publication Date: 2020-06-16
SUZHOU XIQUAN SOFTWARE TECH CO LTD
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of ready-to-mix sodium alginate hydrogel fire extinguishing agent and preparation method thereof, to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Instant sodium alginate hydrogel fire extinguishing agent and preparation method thereof
  • Instant sodium alginate hydrogel fire extinguishing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] S1: Prepare materials:

[0046] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0047] Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0048] S2: Prepare filler:

[0049] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 10 minutes, and then add them to a supersonic jet mill for pulverization. The pulverization time is 10 minutes to obtain superfine material A; take white carbon black, add it to a supersonic jet mill, and pulverize it. The crushing time is 10min to obtain superfine material B;

[0050] Take ultra-fine material A and ultra-fine ma...

Embodiment 2

[0058] S1: Prepare materials:

[0059] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0060] Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0061] S2: Prepare filler:

[0062] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 13 minutes, and then add them to a supersonic airflow mill for pulverization. The pulverization time is 15 minutes to obtain superfine material A; The pulverization time is 15min, and the superfine material B is obtained;

[0063] Take ultra-fine material A and ultra-fine material B, stir and heat up to 42°C, then add fluorocarbo...

Embodiment 3

[0071] S1: Prepare materials:

[0072] Weigh 2-acrylamide-2-methylpropanesulfonic acid, dispersant, cyclohexane, chitosan, ammonium dihydrogen phosphate, ammonium sulfate, additives, white carbon black and fluorocarbon surfactant in proportion, and set aside ;

[0073]Weigh sodium alginate, acrylic acid, N-isopropylacrylamide, N,N-methylenebisacrylamide, sodium acrylate, attapulgite, ammonium persulfate, tetramethylethylenediamine, and the second additive in proportion , Calcium chloride, Calcium nitrate and Calcium carbonate, spare.

[0074] S2: Prepare filler:

[0075] Take ammonium dihydrogen phosphate, ammonium sulfate and additives, stir for 15 minutes, and then add them to a supersonic jet mill for pulverization. The pulverization time is 20 minutes to obtain superfine material A; take white carbon black, add it to a supersonic jet mill, and pulverize it. The crushing time is 25min to obtain superfine material B;

[0076] Take ultra-fine material A and ultra-fine mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Water absorption rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses an instant sodium alginate hydrogel fire extinguishing agent and a preparation method thereof. The instant sodium alginate hydrogel fire extinguishing agent comprises modifiedsodium alginate hydrogel, a filler and water-absorbent resin; the filler comprises a first additive, a second additive and a third additive; the first additive is a conventional dry powder extinguishing agent and comprises ammonium dihydrogen phosphate, ammonium sulfate, auxiliary agents and other materials. The preparation method comprises the steps: preparing a first additive, firstly crushing ammonium dihydrogen phosphate, ammonium sulfate and other main materials by using a supersonic jet mill to obtain ultrafine mixed powder which has the advantages of fine particle size, narrow particlesize distribution, high overall surface activity and convenience for subsequent modification. The invention discloses the instant sodium alginate hydrogel fire extinguishing agent and the preparationmethod thereof, wherein the instant sodium alginate hydrogel fire extinguishing agent is reasonable in component design and simple in process operation, preparation of the sodium alginate hydrogel fire extinguishing agent can be realized, and the fire extinguishing agent is excellent in fire extinguishing performance and relatively high in practicability.

Description

technical field [0001] The invention relates to the technical field of fire extinguishing agents, in particular to a ready-to-mix sodium alginate hydrogel fire extinguishing agent and a preparation method thereof. Background technique [0002] Among various disasters, fire is one of the main disasters that most often and commonly threatens public safety and social development, and when a fire occurs, fire extinguishers are our common fire fighting and rescue equipment. [0003] Among the existing fire extinguishing agents on the market, the most common fire extinguishing agents are water fire extinguishing agent, dry powder fire extinguishing agent, foam fire extinguishing agent, carbon dioxide fire extinguishing agent, haloalkane fire extinguishing agent, with the progress and development of science and technology, hydrogel fire extinguishing agent gradually entered Our sight, but the existing hydrogel fire extinguishing agent has poor mechanical strength, and it is easy to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A62D1/00C08F251/00C08F220/60C08F220/06
CPCA62D1/0064C08F251/00C08F220/06C08F220/54C08F222/385C08F220/585
Inventor 祁海强
Owner SUZHOU XIQUAN SOFTWARE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com