Impact-resistant high-strength bulletproof glass and preparation method thereof

Abstract

The invention discloses a preparation method of impact-resistant high-strength bulletproof glass. The preparation method comprises the following steps: S1, cleaning and air-drying a semi-tempered glass substrate; S2, performing lamination according to the superposing sequence of the semi-tempered glass substrate and the PVB film; S3, placing the superposed glass combination on a roller press for pre-pressing; S4, feeding the pre-pressed glass combination into an autoclave for autoclaving to obtain a semi-finished product glass substrate interlayer combination; S5, overlapping according to an overlapping sequence of the semi-finished product glass substrate interlayer combination, the PU film and the PC board to obtain a combined material; S6, the laminated combined material is put into a vacuum bag to be subjected to edge sealing treatment; and S7, autoclaving the combined material for 4-6 h under the conditions that the temperature is 110-120 DEG C and the pressure is 1.1-1.25 Mpa, thus producing the bullet-proof glass. The invention also discloses the bullet-proof glass prepared by the method. According to the bulletproof glass prepared by the invention, the overall dead weight can be reduced by about 20%-30%, and meanwhile, the impact resistance and bulletproof performance are kept unchanged.

Description

technical field [0001] The invention relates to the technical field of bulletproof glass, in particular to an impact-resistant high-strength bulletproof glass and a preparation method thereof. Background technique [0002] In recent years, terrorist attacks on a global scale have occurred from time to time, and the damage caused by bomb explosions is relatively large, which not only poses a serious threat to the lives of people outdoors, but also causes great harm and harm to people indoors nearby. loss. According to the analysis of security experts and related data, 75% of the injuries caused by bomb explosions are directly related to the scattering of building glass and the splashing of fragments. the main reason. [0003] At present, the existing bullet-proof glass preparation process usually adopts two pre-pressing and autoclaving processes, wherein the second pre-pressing and autoclaving are carried out step by step, and the pre-pressing adopts the roller pressing met...

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a method for preparing impact-resistant high-strength bullet-proof glass, which simplifies the preparation process of existing bullet-proof glass and can solve the problem that curved surface bullet-proof glass cannot be produced by rolling method; and by the The bulletproof glass prepared by the method can effectively reduce the weight and thickness of the bulletproof glass while improving the impact resistance and penetration resistance of the glass, and reduce the cost, and the overall dead weight can be reduced by about 20%-30%.

Images