Manufacturing method of three-dimensional crepe fabric

A production method and technology for fabric, which are applied in chemical instruments and methods, lamination auxiliary operations, lamination devices, etc., can solve the problems of uneven wrinkling, unrealistic, inconspicuous concave-convex patterns, etc., and achieve strong three-dimensional effects. Strong three-dimensional, three-dimensional and long-lasting effect

Inactive Publication Date: 2020-08-07
WUJIAN RUNFENG SILK FINISHING CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing three-dimensional fabrics on the market adopt the jacquard double-layer manufacturing process. The imported large circular knitting machine is expensive and inconvenient to maintain. Moreover, the three-dimensional structure formed by weaving is not strong in three-dimensionality, the concave-convex pattern is not obvious, not realistic, and the output is low. The cost is high; there is another method on the market that is to glue the face cloth and compound it with a shrink film, and then process it to achieve a concave-convex three-dimensional effect, but this process does not wrinkle uniformly, and the wrinkle effect takes a while Time will gradually reduce or disappear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for making a three-dimensional crepe cloth, comprising the following steps:

[0017] 1. Prepare a face cloth with a weight of 50 grams per square meter. The base cloth is made of 40D polyester warp-knitted fabric, and the face cloth is dyed and shaped.

[0018] 2. Cut the face cloth and the base cloth so that the width of the base cloth is slightly larger than the face cloth.

[0019] 3. Put the face cloth on the roller printing machine to perform the operations of printing glue, pasting, pre-drying, and winding in sequence. Glue and special glue curing agent are added to the slurry feeding device on the roller printing machine. mixture.

[0020] 4. Put the rolled fabric in step 3 into the drying room at a temperature of 90°C and keep the temperature constant for 10 hours to fully cure the glue, and the base fabric and the surface fabric are completely bonded at the glued place.

[0021] 5. Unwind the fabric in step 4, pass it through a heating oven, and dry ...

Embodiment 2

[0025] Embodiment 2: a kind of preparation method of three-dimensional crepe cloth, comprises the following steps:

[0026] 1. Prepare a face cloth with a weight of 150 grams per square meter. The base cloth is made of 75D polyester yarn warp-knitted fabric, and the face cloth and base cloth are dyed and shaped.

[0027] 2. Cut the face cloth and the base cloth so that the width of the base cloth is slightly larger than the face cloth.

[0028] 3. Put the face cloth on the roller printing machine to perform the operations of printing glue, pasting, pre-drying, and winding in sequence. The slurry feeding device on the roller printing machine is added with a special glue curing agent.

[0029] 4. Put the rolled fabric in step 3 into the drying room at a temperature of 90°C and keep the temperature constant for 10 hours to fully cure the glue, and the base fabric and the surface fabric are completely bonded at the glued place.

[0030] 5. Unwind the fabric in step 4, pass it thr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a three-dimensional crepe fabric. The manufacturing method comprises the following steps: dyeing and shaping a surface fabric; cutting the surface fabric and a bottom fabric and enabling the breadth of the bottom fabric to be slightly larger than the breadth of the surface fabric; putting the surface fabric on a roller printing machine for glue pattern printing in sequence, pre-drying the surface fabric, then laminating the surface fabric with the bottom fabric, and finally carrying out rolling, wherein a mixture of glue and a special glue curing agent is added into a slurry feeding device on the roller printing machine; putting the rolled fabric into a drying room, and keeping the fabric at a constant temperature of 60 DEG C to 90 DEG C for 10-14 hours to completely cure the glue, wherein the bottom fabric and the surface fabric are completely bonded at positions with the glue; and unreeling the fabrics, allowing the fabrics to pass through a heating oven, and drying the fabrics for 9-15 seconds at a temperature of 150-230 DEG C, wherein the bottom fabric contracts with heat, and the surface fabric moves upwards to form a protruding effect at non-bonded positions. The crepe fabric produced through the method has obvious concave-convex effect and is high and durable in stereoscopic impression.

Description

technical field [0001] The invention relates to a method for making three-dimensional crepe cloth. Background technique [0002] Most of the existing three-dimensional fabrics on the market adopt the jacquard double-layer manufacturing process. The imported large circular knitting machine is expensive and inconvenient to maintain. Moreover, the three-dimensional structure formed by weaving is not strong, the concave-convex pattern is not obvious, not realistic, and the output is low. The cost is high; there is another method on the market, which is to glue the face cloth and compound it with a shrink film, and then process it to achieve a concave-convex three-dimensional effect, but this process does not wrinkle uniformly, and the wrinkle effect takes a while Time will gradually reduce or disappear. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the invention provides a method for making three-dimensional creped cloth. [0004] The techni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/06B32B37/12B32B37/14B32B38/14B32B38/16B32B38/00
CPCB32B37/06B32B37/12B32B37/144B32B38/0036B32B38/145B32B38/164B32B2037/1253
Inventor 郭伟翔
Owner WUJIAN RUNFENG SILK FINISHING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com