A kind of glass suitable for uv curing process and preparation method thereof

A curing process and glass technology, applied in glass manufacturing equipment, glass furnace equipment, glass production, etc., can solve the problems of glass yellowing and transmittance, reduce the number of irradiation times, strong anti-irradiation ability, and color difference small effect

Active Publication Date: 2022-07-29
深圳南玻科技有限公司 +3
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a glass suitable for UV curing process and its preparation method, aiming to solve the problems of yellowing and lower transmittance of existing glass after UV curing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass suitable for uv curing process and preparation method thereof
  • A kind of glass suitable for uv curing process and preparation method thereof
  • A kind of glass suitable for uv curing process and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0059] In Table 1, Table 2 and Table 3, commonly used glass raw materials such as oxides and carbonates, etc. were appropriately selected to have the compositions shown in the tables, and were weighed to obtain 150 g of the batch mixture; The batch mixture was placed in a platinum crucible, and the platinum crucible was placed in a silicon-molybdenum furnace, heated to 1650 °C, melted for 3 hours, homogenized and cast into a mold, kept at 620 °C for 1 hour annealing, and then followed by annealing. Furnace cooling to obtain block glass; the block glass is processed to obtain several pieces of thin glass with a size of 50mm×50mm×0.7mm, and the upper and lower surfaces are polished.

[0060] like figure 2 and image 3 As shown, the above-mentioned glass sample 20 is irradiated twice by a metal halide lamp, and the irradiation time is 5s each time, and the filter 10 is used to cover half of the glass sample 20 during irradiation, and the energy in the direct irradiation area fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass suitable for UV curing process and a preparation method thereof. Calculated by mass percentage, the glass includes the following components: 58% to 66% SiO 2 , 15% to 20% Al 2 O 3 , 3% to 8% Li 2 O, 7% to 12% Na 2 O, 0% to 2% K 2 O, 0% to 3% MgO, 0% to 3% B 2 O 3 , 1%~5% ZrO 2 , 0.01~0.05% CeO 2 and 0.01%~2% SnO 2 . The glass provided by the present invention has strong anti-irradiation ability. In the UV curing process of the glass, even if the single irradiation energy is increased, discoloration is not easy to occur, and the transmittance is basically not reduced, so that the number of irradiation can be reduced, and the Production efficiency; and adding a filter device to the glass in the UV curing process has less effect on the color difference of the glass after multiple irradiations.

Description

technical field [0001] The invention relates to the technical field of glass manufacturing, in particular to a glass suitable for a UV curing process and a preparation method thereof. Background technique [0002] At present, most of the glass cover plates on the market are fully laminating process. Compared with the traditional frame attaching process, the fully laminating process has the advantages of better display effect, thinner body and simpler assembly process. Therefore, the fully laminating process has become a screen sticker. The mainstream of lamination, and a very important process in the full lamination process is UV curing, which needs to go through 3000-5000mj / cm 2 The energy is used to irradiate the glass cover; however, the general glass cover will turn yellow after UV curing, and the transmittance will also decrease, which will seriously affect the appearance and display effect. The more serious the yellowing of the glass is. [0003] In order to solve th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C3/095C03C4/00C03B5/16C03B25/00
CPCC03C3/095C03C4/00C03B5/16C03B25/00Y02P40/57
Inventor 戴斌陈志鸿何进刘建党肖子凡刘攀邓臻禄刘红刚王明忠
Owner 深圳南玻科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap