A kind of spring steel with good heat resistance and impact resistance and production method thereof

A production method and impact-resistant technology, applied in the field of spring steel production, can solve the problems of poor spring steel performance, difficult to meet, poor tensile strength, impact resistance and resistance to hydrogen embrittlement fracture, etc., to ensure strong toughness and resistance. The effect of hydrogen embrittlement fracture performance, improving hardenability and good heat resistance

Active Publication Date: 2021-12-14
MAANSHAN IRON & STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the relatively poor performance of existing spring steel not only at room temperature, but also at high temperature and high pressure conditions, its tensile strength, impact resistance and hydrogen embrittlement resistance are poor, so it is difficult to meet its requirements. Insufficient for use under special high temperature and high pressure conditions, providing a spring steel with good heat resistance and shock resistance and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of spring steel with good heat resistance and impact resistance and production method thereof
  • A kind of spring steel with good heat resistance and impact resistance and production method thereof
  • A kind of spring steel with good heat resistance and impact resistance and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063]The chemical composition of the spring steel of this embodiment is: C: 0.50%, Si: 1.60%, Mn: 0.80%, Cr: 0.80%, Mo: 0.4%, W: 0.70%, V: 0.20%, Nb: 0.02 %, Ti: 0.015%, Ni: 0.20%, Cu: 0.20%, P: 0.015%, S: 0.010%, O: 0.0012%, N: 0.006%, and the rest are Fe and other unavoidable impurities. Wherein, P value = 1.75, Meq value = 0.312.

[0064] Its processing step adopts the technical process of the present invention, and the control parameters of its wire rod rolling related technical process are as follows: figure 1 Shown, and then its normal temperature mechanical properties, high temperature mechanical properties, hydrogen embrittlement resistance were tested, the results are shown in figure 2 , image 3 and Figure 4 .

Embodiment 2

[0066] The chemical composition of the spring steel of this embodiment is: C: 0.60%, Si: 2.00%, Mn: 1.00%, Cr: 1.30%, Mo: 0.50%, W: 1.30%, V: 0.40%, Nb: 0.04 %, Ti: 0.030%, Ni: 0.15%, Cu: 0.15%, P: 0.015%, S: 0.010%, O: 0.0012%, N: 0.006%, and the rest are Fe and other unavoidable impurities. Wherein, P value = 2.6, Meq value = 0.282.

[0067] Its processing step adopts the technical process of the present invention, and the control parameters of its wire rod rolling related technical process are as follows: figure 1 Shown, and then its normal temperature mechanical properties, high temperature mechanical properties, hydrogen embrittlement resistance were tested, the results are shown in figure 2 , image 3 and Figure 4 .

Embodiment 3

[0069] The chemical composition of the spring steel of this embodiment is: C: 0.56%, Si: 2.20%, Mn: 0.90%, Cr: 1.00%, Mo: 0.20%, W: 0.80%, V: 0.30%, Nb: 0.02 %, Ti: 0.020%, Ni: 0.30%, Cu: 0.30%, P: 0.015%, S: 0.009%, O: 0.0011%, N: 0.003%, and the rest are Fe and other unavoidable impurities. Wherein, P value = 4.0, Meq value = 0.343.

[0070] Its processing step adopts the technical process of the present invention, and the control parameters of its wire rod rolling related technical process are as follows: figure 1 Shown, and then its normal temperature mechanical properties, high temperature mechanical properties, hydrogen embrittlement resistance were tested, the results are shown in figure 2 , image 3 and Figure 4 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
fatigue strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a spring steel with good heat resistance and impact resistance and a production method thereof, belonging to the technical field of spring steel production. The weight percent of chemical composition of the spring steel is: C: 0.50%-0.60%, Si: 1.60%-2.20%, Mn: 0.80%-1.00%, Cr: 0.80%-1.30%, Mo: 0.20%-0.50%, W : 0.70%~1.30%, V: 0.20%~0.40%, Nb: 0.02%~0.04%, Ti: 0.015%~0.030%, Ni: 0.15%~0.30%, Cu: 0.15%~0.30%, P: trace Fe content ~ 0.015%, S: trace ~ 0.010%, O ≤ 0.0012%, N ≤ 0.006%, and the rest are Fe and other unavoidable impurities. Its production methods are: electric arc furnace smelting, LF furnace refining, RH or VD vacuum degassing, round billet continuous casting, billet rolling, flaw detection, peeling, high-speed wire rod controlled rolling, Stelmore cooling line controlled cold treatment and heat treatment . The spring steel obtained by adopting the technical solution of the present invention has good performances of heat resistance, impact resistance and hydrogen embrittlement fracture resistance, thereby being able to effectively meet the use requirements of the spring steel under high temperature and high pressure.

Description

technical field [0001] The invention belongs to the technical field of spring steel production, and more specifically relates to a spring steel with good heat and shock resistance and a production method thereof. Background technique [0002] Spring steel has excellent comprehensive mechanical properties and elastic resistance, so it is widely used in key fields of the national economy such as automobiles, aviation and military. In recent years, all walks of life are facing tremendous pressure to save energy and reduce costs. From the perspective of energy saving and economy, the demand for spring weight reduction is increasing. It is imperative to develop new ultra-high-strength spring steel, especially in the face of train speed increase, The development of lightweight aircraft requires springs to increase strength, reduce weight, and increase life. [0003] However, the traditional method is to increase the strength by changing the heat treatment temperature, but the duc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C21D8/06C22C33/04
CPCC22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C22C33/04C21D8/065
Inventor 汪开忠张晓瑞于同仁姜婷尹德福龚梦强余良其丁雷郭湛孙凯吴建曦牟祖茂郝震宇
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com